ASTM D267-1982(2003) Standard Specification for Gold Bronze Powder《黄青铜粉规格的标准规范》.pdf

《ASTM D267-1982(2003) Standard Specification for Gold Bronze Powder《黄青铜粉规格的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM D267-1982(2003) Standard Specification for Gold Bronze Powder《黄青铜粉规格的标准规范》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D 267 82 (Reapproved 2003)Standard Specification forGold Bronze Powder1This standard is issued under the fixed designation D 267; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in p

2、arentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers the materials commerciallyknown as gold bronze, pale gold bronze, and rich gold bronzepowders.2. Referenced Documents2.

3、1 ASTM Standards:D13 Specification for Spirits of Turpentine2D 185 Test Methods for Coarse Particles in Pigments,Pastes, and Paints2D 480 Test Methods for Sampling and Testing of FlakedAluminum Powders and Pastes22.2 U.S. Federal Specification:A-A-1800 Water-Resisting Spar Varnish33. Composition and

4、 Properties3.1 The bronze powder shall be made from new ingotmetals. It shall consist of fine polished flakes containing notless than 3 % of fatty or oily matter (polishing lubricant) togive good “leafing” properties.3.2 The residue retained on a No. 100 (150-m) sieve, usingalcohol as the wash liqui

5、d, shall not exceed 0.2 % (in accor-dance with Test Methods D 185).3.3 The powder shall have good “leafing” properties. (By“leafing” is understood the property of forming an apparentlycontinuous brilliant film over the entire free surface of amixture of the powder in a suitable liquid (Note 1), with

6、in 1min after cessation of stirring the mixture.) In testing forleafing properties the powder shall be mixed in the proportionof 3 to 4 lb (370 to 475 g/L) to a gallon (3.8 L) of the liquid.As thus mixed it shall also give a free flowing, smooth,continuous coating in accordance with Test Methods D 4

7、80.NOTE 1A suitable liquid is made by mixing spar varnish conformingto the U. S. Federal Specification for Water-Resisting Spar Varnish (No.A-A-1800) with turpentine conforming to Specification D13 in suchproportions that the mixture will have a viscosity of 0.65 to 0.85 poises (Bto C on the Gardner

8、-Holdt scale).3.4 The gold bronze powder shall be suitable for makinggold bronze paint. It shall match in shade and fineness areference sample mutually agreed upon by the purchaser andthe seller.4. Sampling4.1 Two samples shall be taken at random from differentpackages from each lot, batch, days pac

9、k, or other unit ofproduction in a shipment. When no markings distinguishingbetween units of production appear, samples shall be takenfrom different packages in the ratio of two samples for each 5tons (inch-pound or SI), except that for shipments of less than10 000 lb two samples shall be taken. At

10、the option of thepurchaser, the samples may be tested separately or afterblending in equal quantities the samples from the sameproduction unit to form a composite sample.5. Test Methods5.1 Test shall be conducted in accordance with the appro-priate methods of ASTM International, where applicable. Te

11、stprocedures not covered by ASTM methods shall be mutuallyagreed upon between the purchaser and the seller.6. Keywords6.1 bronze powders; leafing; spar varnish1This specification is under the jurisdiction of ASTM Committee D01 on Paintand Related Coatings, Materials, and Applications and is the dire

12、ct responsibility ofSubcommittee D01.31 on Pigment Specifications.Current edition approved Oct. 1, 2003. Published October 2003. Originallyapproved in 1927. Last previous edition approved in 1982 as D 267 82 (1999).2Annual Book of ASTM Standards, Vol 06.03.3Available from Standardization Documents O

13、rder Desk, DODSSP, Bldg. 4,Section D, 700 Robbins Ave., Philadelphia, PA 19111-50981Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.ASTM International takes no position respecting the validity of any patent rights asserted in connecti

14、on with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible

15、 technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consi

16、deration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Ba

17、rr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).D 267 82 (2003)2