ASTM C603-2014 Standard Test Method for Extrusion Rate and Application Life of Elastomeric Sealants《弹性密封料的挤压率和使用寿命的标准试验方法》.pdf

《ASTM C603-2014 Standard Test Method for Extrusion Rate and Application Life of Elastomeric Sealants《弹性密封料的挤压率和使用寿命的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM C603-2014 Standard Test Method for Extrusion Rate and Application Life of Elastomeric Sealants《弹性密封料的挤压率和使用寿命的标准试验方法》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C603 14Standard Test Method forExtrusion Rate and Application Life of ElastomericSealants1This standard is issued under the fixed designation C603; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revis

2、ion. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope1.1 This test method covers two laboratory pro

3、cedures fordetermining the extrusion rate and application life (or “potlife”) of elastomeric chemically curing sealants for use inbuilding construction.NOTE 1These sealants are supplied with various rheological proper-ties ranging from pourable liquids to nonsagging pastes. Single-component sealants

4、 are supplied ready for use upon opening the container,and their rate of cure is determined by the climatic conditions to whichthey are exposed. Multicomponent sealants are supplied as a basecomponent and a curing agent separately packaged. After mixing the twoparts, the sealant is ready for applica

5、tion, and curing begins immediately.1.2 The values stated in SI units are to be regarded as thestandard. The values given in parentheses are provided forinformation only.1.3 There is no known ISO equivalent to this test method.1.4 This standard does not purport to address all of thesafety concerns,

6、if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2C717 Terminology of Building Seals and Sealan

7、ts3. Terminology3.1 Refer to Terminology C717 for definitions of the fol-lowing terms used in this standard: standard conditions.4. Significance and Use4.1 The results obtained by this test method are simply ameasure of the time required to extrude a known volume ofsealant through a known orifice un

8、der a predetermined pres-sure.4.2 This test method is not considered a measure of curerate.5. Apparatus5.1 Caulking Gun, 177-mL (6-fl oz) capacity, air-powered.5.2 Polyethylene Cartridge, 177-mL (6-fl oz), with the frontend having an inside diameter of 13.7 6 0.05 mm (0.540 60.002 in.).5.3 Air Suppl

9、y, providing 345 kPa (50-psi) pressure andhaving the necessary connection fittings for attachment to theair-powered caulking gun.5.4 Timing Device (clock or watch), calibrated in seconds.5.5 500-mL (1-pt) Container6. Procedure6.1 Extrusion Rate of Single-Component SealantFirstcondition the unopened

10、container for at least 16 h at standardconditions. Then place a sufficient amount of sealant into the177-mL (6-fl oz) cartridge to fill it completely with the plungerin place, fully retracted. Using no nozzle on the cartridge, gunthe sealant at 345 kPa (50-psi) pressure into the 500-mL (1-pt)contain

11、er, measuring the time in seconds required to empty thecartridge.NOTE 2When the printed instructions of the sealant manufacturer sorecommended, heat the sealant before extruding it into the container.6.2 Extrusion Rate or Application Life or both, of MixedMulticomponent SealantFirst condition the un

12、opened con-tainers of both sealant and curing agent for at least 16 h atstandard conditions. Then mix 400 g of the sealant with theproper amount of curing agent, stirring the mixture by hand for5 min. Place a sufficient amount of the mixed compound intothe 177-mL (6-fl oz) cartridge to fill it compl

13、etely with theplunger in place, fully retracted, and set the filled cartridgeaside, in a vertical position, at standard conditions, for 3 h1This test method is under the jurisdiction ofASTM Committee C24 on BuildingSeals and Sealants and is the direct responsibility of Subcommittee C24.20 onGeneral

14、Test Methods.Current edition approved June 1, 2014. Published July 2014. Originally approvedin 1969. Last previous edition approved in 2008 as C603 - 04(2008). DOI:10.1520/C0603-14.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.or

15、g. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1(Note 3). Then, using no nozzle on the cartridge, gun thesealant a

16、t 345 kPa (50-psi) pressure into the 500-mL (1-pt)container, measuring the time in seconds required to empty thecartridge.NOTE 3Curing times and conditions for multi-component mixedcompounds may vary. Therefore curing periods of longer or shorter than3 h, and under other than the specified standard

17、conditions, or either oneof these two may be specified in some cases.7. Report7.1 The report on the extrusion rate of the single-componentsealant shall state:7.1.1 The trade name (or other identification) of the sealant.7.1.2 The time, in seconds, required to empty the cartridge(the extrusion rate),

18、 and7.1.3 Any variation, specified or otherwise, from the abovedescribed test method, including heating of the sealant if sorequired.7.2 The report on the extrusion rate or application life, orboth, of the multicomponent sealant shall state:7.2.1 The trade name (or other identification) of the seala

19、nt,7.2.2 The time, in seconds, required to empty the cartridgeafter the 3-h (or other specified) curing period, and7.2.3 Any variations, specified or otherwise, from the abovedescribed test method, including the length of curing periodand the conditions of temperature and humidity during thisperiod.

20、8. Precision and Bias38.1 The precision and bias calculations for this test methodare based on the results of four laboratories testing fivematerials, each in triplicate. The results are given in Table 1.9. Keywords9.1 application life; extrusion rate; pot life; sealantASTM International takes no po

21、sition respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibi

22、lity.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to A

23、STM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the addres

24、s shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 61

25、0-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ data have been filed at ASTM International

26、Headquarters and maybe obtained by requesting Research Report RR:C24-1010.TABLE 1 Precision and Bias DataAMaterial AverageEstimatedStandardDeviationWithin aLaboratoryEstimatedStandardDeviationBetweenLaboratoriesRepeat-abilityInternalReproduci-bilityG1 3.6 0.32 1.24 0.91 3.40G2 2.4 0.52 1.54 1.48 4.36G3 5.3 0.30 2.37 0.86 6.70G4 6.3 2.32 6.46 6.56 18.28G5 2.1 0.22 0.89 0.62 2.51AAt 95 % confidence a variation of as much as 6.56 can be expected within alaboratory and 18.28 between laboratories.C603 142