ASTM B514-2005 Standard Specification for Welded Nickel-Iron-Chromium Alloy Pipe《焊接的镍铁铬合金管标准规范》.pdf
《ASTM B514-2005 Standard Specification for Welded Nickel-Iron-Chromium Alloy Pipe《焊接的镍铁铬合金管标准规范》.pdf》由会员分享,可在线阅读,更多相关《ASTM B514-2005 Standard Specification for Welded Nickel-Iron-Chromium Alloy Pipe《焊接的镍铁铬合金管标准规范》.pdf(3页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: B 514 05Standard Specification forWelded Nickel-Iron-Chromium Alloy Pipe1This standard is issued under the fixed designation B 514; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in
2、 parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification2covers nickel-iron-chromium alloysin the form of welded, cold-worked, and annealed pipe forgeneral corrosive service and he
3、at-resisting applications. Theseproducts are furnished in three alloys: UNS N08120, UNSN08800, and UNS N08810.* Alloy UNS N08800 is employednormally in service temperatures up to and including 1100F(593C). Alloys UNS N08120 and UNS N08810 are employednormally in service temperatures above 1100F wher
4、e resis-tance to creep and rupture is required, and are annealed todevelop controlled grain size for optimum properties in thistemperature range.1.2 This specification covers outside diameter and nominalwall pipe shown in ANSI B36.19. Pipe having other dimen-sions may be furnished provided such pipe
5、 complies with allother requirements of the specification.1.3 The values stated in inch-pound units are to be regardedas the standard.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to beco
6、me familiarwith all hazards including those identified in the appropriateMaterial Safety Data Sheet (MSDS) for this product/materialas provided by the manufacturer, to establish appropriatesafety and health practices, and determine the applicability ofregulatory limitations prior to use.2. Reference
7、d Documents2.1 ASTM Standards:3B 899 Terminology Relating to Non-ferrous Metals andAlloysB 775 Specification for General Requirements for Nickeland Nickel Alloy Seamless and Welded Pipe2.2 ANSI Standard:B36.19 Stainless Steel Pipe43. Terminology3.1 Terms defined in Terminology B 899 shall apply unle
8、ssdefined otherwise in this standard.4. General Requirement4.1 Material furnished in accordance with this specificationshall conform to the applicable requirements of the currentedition of Specification B 775 unless otherwise providedherein.5. Ordering Information5.1 Orders for material under this s
9、pecification shouldinclude the following information:5.1.1 Alloy name or UNS number.5.1.2 ASTM designation and year of issue.5.1.3 Condition (temper) (Table 1).5.1.4 Dimensions:5.1.4.1 Nominal pipe size or outside diameter and schedulenumber or nominal wall thickness.5.1.4.2 Length (specific or rand
10、om).5.1.5 Quantity (feet or metres, or number of pieces).5.1.6 CertificationState if certification or a report of testresults is required.5.1.7 Samples for Product (Check) AnalysisState whethersamples for product (check) analysis should be furnished.5.1.8 Purchaser InspectionIf the purchaser wishes
11、towitness tests or inspection of material at the place of manu-facture, the purchase order must so state indicating which testsor inspections are to be witnessed.1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of Sub
12、committeeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition approved Nov. 1, 2005. Published November 2005. Originallyapproved in 1970. Last previous edition approved in 2002 as B 514 95 (2002)e1.2For ASME Boiler and Pressure Code applications see related SpecificationSB-514 in Sec
13、tion II of that Code.* New designation established in accordance with ASTM E 527 and SAE J1086,Practice for Numbering Metals and Alloys (UNS).3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards vol
14、ume information, refer to the standards Document Summary page onthe ASTM website.4Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036.TABLE 1 Mechanical Property RequirementsAlloyCondition(Temper)Tensile Strength,min, psi (MPa)Yield Strength,0.2
15、% Offset,min, psi (MPa)Elongation in2 in. or 50mm, min, %UNS N08120 annealed 90 000 (621) 40 000 (276) 30UNS N08800 annealed 75 000 (520) 30 000 (207) 30UNS N08810 annealed 65 000 (450) 25 000 (170) 301*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 10
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMB5142005STANDARDSPECIFICATIONFORWELDEDNICKELIRONCHROMIUMALLOYPIPE 焊接 镍铁铬 合金管 标准规范 PDF
链接地址:http://www.mydoc123.com/p-461445.html