ASTM B140 B140M-2007 Standard Specification for Copper-Zinc-Lead (Red Brass or Hardware Bronze) Rod Bar and Shapes《铜锌铅杆材(铅红黄铜或硬青铜)、棒材和型材标准规范》.pdf

《ASTM B140 B140M-2007 Standard Specification for Copper-Zinc-Lead (Red Brass or Hardware Bronze) Rod Bar and Shapes《铜锌铅杆材(铅红黄铜或硬青铜)、棒材和型材标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM B140 B140M-2007 Standard Specification for Copper-Zinc-Lead (Red Brass or Hardware Bronze) Rod Bar and Shapes《铜锌铅杆材(铅红黄铜或硬青铜)、棒材和型材标准规范》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B 140/B 140M 07Standard Specification forCopper-Zinc-Lead (Red Brass or Hardware Bronze) Rod,Bar, and Shapes1This standard is issued under the fixed designation B 140/B 140M; the number immediately following the designation indicates the yearof original adoption or, in the case of revis

2、ion, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 This specification

3、 establishes the requirements forcopper-zinc-lead (leaded red brass or hardware bronze) rod,bar, and shapes of UNS Alloy Nos. C31400, C31600, andC32000 available for screw machine applications.1.2 UnitsThe values stated in inch-pound units or SI unitsare to be regarded separately as standard. Within

4、 the text, SIunits are shown in brackets. The values in each system are notexact equivalents; therefore, each system shall be used inde-pendently of the other. Combining values from the two systemsmay result in nonconformance with the specification.2. Referenced Documents2.1 ASTM Standards:2B 249/B

5、249M Specification for General Requirements forWrought Copper and Copper-Alloy Rod, Bar, Shapes andForgingsB 601 Classification for Temper Designations for Copperand Copper AlloysWrought and CastB 846 Terminology for Copper and Copper AlloysE8 Test Methods for Tension Testing of Metallic MaterialsE8

6、M Test Methods for Tension Testing of Metallic Mate-rials MetricE62 Test Methods for Chemical Analysis of Copper andCopper Alloys (Photometric Methods)E 478 Test Methods for Chemical Analysis of CopperAlloys3. General Requirements3.1 The following sections of Specification B 249/B 249Mconstitute a p

7、art of this specification:3.1.1 Terminology (B 846),3.1.2 Materials and Manufacture,3.1.3 Workmanship, finish, and appearance,3.1.4 Sampling,3.1.5 Number of Tests and Retests,3.1.6 Specimen Preparation,3.1.7 Test Methods,3.1.8 Significance of Numerical Limits,3.1.9 Inspection,3.1.10 Rejection and Re

8、hearing,3.1.11 Certification,3.1.12 Test Reports (Mill),3.1.13 Packaging and Package Marking, and3.1.14 Supplemental Requirements.3.2 In addition, when a section with a title identical to oneof those referenced in 3.1 appears in this specification, itcontains additional requirements that supplement

9、those whichappear in Specification B 249/B 249M.4. Ordering Information4.1 Include the following information when placing ordersfor products under this specification:4.1.1 ASTM designation and year of issue,4.1.2 Copper Alloy UNS No. designation (Scope),4.1.3 Temper designation (Temper Section),4.1.

10、4 Quantity; total weight or length, or number of piecesof each temper, form, and alloy.4.1.5 Dimensionsdiameter, distance between parallel sur-faces,4.1.6 How furnished; specific lengths with or without ends,and4.1.7 If product is purchased for agencies of the U.S.government. (B 249/B 249M).1This sp

11、ecification is under the jurisdiction ofASTM Committee B05 on Copperand Copper Alloys and is the direct responsibility of Subcommittee B05.02 on Rod,Bar, Wire, Shapes and Forgings.Current edition approved April 1, 2007. Published April 2007. Originallyapproved in 1941. Last previous edition approved

12、 in 2001 as B 140/B 140M 01.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1*A Summary of Changes section ap

13、pears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.4.2 The following options are available to this specificationand should be specified in the contract or purchase order whenrequired:4.2.1 Heat identific

14、ation or traceability details,4.2.2 Certification (Specification B 249/B 249M), and4.2.3 Mill Test Reports (Specification B 249/B 249M).5. Material and Manufacture5.1 Material:5.1.1 The material of manufacture shall be a form (castbillets, logs, or rods) of Copper Alloy UNS Nos. C31400,C31600, or C3

15、2000 of such purity and soundness as to besuitable for processing into the products prescribed herein.5.2 Manufacture:5.2.1 The product shall be manufactured by such hot work-ing, cold working, straightening, and annealing processes as toproduce a uniform wrought structure in the finished product.6.

16、 Chemical Composition6.1 The material shall conform to the chemical compositionrequirements in Table 1 for the Copper Alloy UNS No.designation specified in the ordering information.6.1.1 These composition limits do not preclude the presenceof other elements. By agreement between the manufacturer and

17、the purchaser, limits may be established and analysis requiredfor unnamed elements.6.2 For alloys in which zinc is listed as the “remainder,”either copper or zinc may be taken as the difference betweenthe sum of results of all other elements determined and 100 %.When copper is so determined, that di

18、fference value shallconform to the requirements given in Table 1.6.3 When all elements in Table 1 are determined, the sum ofthe results shall be 99.6 % minimum.7. Temper7.1 Tempers, as defined in Classification B 601, available tothis specification are O60 (soft anneal), H02 (half-hard), andH04 (har

19、d).8. Mechanical Property Requirements8.1 Tensile Requirements:8.1.1 Product furnished under this specification shall con-form to the tensile requirements specified in Table 2 (inch-pound units) or Table 3 (SI units) when tested in accordancewith Test Methods E8or E8M.9. Dimensions, Mass and Permiss

20、ible Variations9.1 The dimensions and tolerances for product described bythis specification shall be as specified in Specification B 249/B 249M with particular reference to the following tables andrelated paragraphs:9.2 Diameter or Distance Between Parallel Surfaces:9.2.1 RodRefer to Table 1 for rou

21、nd, hexagonal andoctagonal rod.9.2.2 BarRefer to Table 8 for thickness and Table 10 forwidth.9.3 LengthsRefer to Tables 13 and 14.9.4 StraightnessRefer to Table 16.9.5 ShapesThe dimensional tolerances for shapes shall beagreed upon between the manufacturer or supplier and thepurchaser and shall be s

22、pecified in the order or purchasecontract.10. Test Methods10.1 Chemical Analysis:10.1.1 The material composition shall, in case of dispute, bedetermined as follows:Element ASTM Test MethodCopper E 478Lead E 478, atomic absorptionIron E 478Nickel E 478, photometricPhosphorus E62Zinc E 478, Titrimetri

23、cTABLE 1 Chemical RequirementsElementComposition, %Copper Alloy UNS No.C31400 C31600 C32000Copper 87.5 to 90.5 87.5 to 90.5 83.5 to 86.5Lead 1.3 to 2.5 1.3 to 2.5 1.5 to 2.2Iron, max 0.10 0.10 0.10Nickel 0.7 max 0.7 to 1.2 0.25 maxZinc remainder remainder remainderPhosphorus . 0.04 to 0.10 .B 140/B

24、140M 07211. Keywords11.1 C31400; C31600; C32000; hardware bronze; hardwarebronze rod; hardware bronze shapes; leaded brass shapes;leaded red brass bar; leaded red brass rodSUMMARY OF CHANGESCommittee B05 has identified the principle changes to this specification that have been incorporated since the

25、2001 issue as follows:(1) Changes made to conform to the ASTM and B05 Form andStyle guidelines.TABLE 2 Tensile Requirements (Inch-Pound Units)Copper AlloyUNS No.Temper DesignationDiameter or Distance BetweenParallel Surfaces, in.Width, in.TensileStrength,min, ksiYield Strengthat 0.5 %ExtensionUnder

26、Load,min, ksiElongation in4 3 Diameteror Thickness ofSpecimenmin, %ACode NameC31400, C31600,C32000O60 soft anneal all forms all sizes . 35 10 25C31400, C31600,C32000HO2 half hard rod:12 and under . 50 30 7over12 to 1 . 45 27 10over 1 . 40 25 12bar: 1 and under 2 and under 40 25 12over 1 over 2 40B25

27、B12BC31400 H04 hard rod 2 and under . 53 40 6C31600, C32000 H04 hard rod 2 and under . 60 50 6bar 1 and under 2 and under 60 50 6AIn any case, a minimum gage length of 1 in. shall be used.BIn the case of bars either over 1 in. in thickness or over 2 in. in width, or both, these values shall apply.TA

28、BLE 3 Tensile Requirements (SI Units)Copper AlloyUNS No.Temper DesignationDiameter or Distance BetweenParallel Surfaces, mmWidth, mmTensileStrength,min MPaYield Strengthat 0.5 %ExtensionUnder Load,min, MPaElongationAmin, %Code NameC31400, C 31600,C32000O60 Soft anneal all forms all sizes . 240 70 25

29、C31400, C31600,C32000HO2 half hard rod: 12 and under . 345 205 7over 12 to 25 . 310 185 10over 25 . 275 170 12bar: 25 and under 50 and under 275 170 12over 25 over 50 275B170B12BC31400 H04 hard rod 50 and under . 365 275 6C31600, C32000 H04 hard rod 50 and under . 415 345 6bar 25 and under 50 and un

30、der 415 345 6AElongation values are based on a gage length of 5.65 times the square root of the area for dimensions greater than 2.5 mm.BIn the case of bars either over 25 mm in thickness or over 50 mm in width, or both, these values shall apply.B 140/B 140M 073ASTM International takes no position r

31、especting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.Thi

32、s standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM Inte

33、rnational Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown

34、below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).B 140/B 140M 074