1、Designation: B 134/B 134M 05Standard Specification forBrass Wire1This standard is issued under the fixed designation B 134/B 134M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, the year of last revision. A number in parentheses i

2、ndicates the year of last reapproval.A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 This specification establishes requirements for round,hexagonal, octagonal,

3、 rectangular and square brass wire ofUNS Alloy Nos. C21000, C22000, C22600, C23000, C23400,C24000, C26000, C27000, and C27400.1.2 UnitsThe values stated in either inch-pound or SIunits are to be regarded separately as standard. Within the textand tables, the SI units are shown in brackets. The value

4、s statedin each system may not be exact equivalents: therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may result in nonconformancewith the standard.2. Referenced Documents2.1 ASTM Standards:2B 250/B 250M Specification for General Requirements forWr

5、ought Copper Alloy WireB 601 Classification for Temper Designations for Copperand Copper AlloysWrought and CastB 846 Terminology for Copper and Copper AlloysE8 Test Methods for Tension Testing of Metallic MaterialsE8M Test Methods for Tension Testing of Metallic Mate-rials (Metric)E112 Test Methods

6、for Determining the Average GrainSizeE 478 Test Methods for Chemical Analysis of CopperAlloys3. General Requirements3.1 The following sections of Specification B 250/B 250Mconstitute a part of this specification.3.1.1 Terminology,3.1.2 Materials and Manufacture,3.1.3 Workmanship, Finish and Appearan

7、ce,3.1.4 Sampling,3.1.5 Number of Tests and Retests,3.1.6 Specimen Preparation,3.1.7 Test Methods,3.1.8 Significance of Numerical limits,3.1.9 Inspection,3.1.10 Rejection and Rehearing,3.1.11 Certification,3.1.12 Mill Test Reports,3.1.13 Product Marking,3.1.14 Packaging and Package Marking,3.1.15 Su

8、pplementary Requirements.3.2 In addition, when a section with a title identical to thatreferenced in 3.1 appears in this specification, it containsadditional requirements that supplement those that appear inSpecification B 250/B 250M.4. Ordering Information4.1 Include the following information in or

9、ders for product:4.1.1 ASTM Designation and year of issue,4.1.2 Copper Alloy UNS No. designation,4.1.3 Temper,4.1.4 Cross section: round, hexagonal, octagonal, rectangu-lar, or square,4.1.5 Quantity: total weight, footage, or number of pieces ofeach temper, cross section, or alloy,4.1.6 Dimensions:

10、diameter or distance between parallelsurfaces, width and thickness, length,4.1.7 Type of edge: square corners, rounded edge, full-rounded edge,4.1.8 How furnished: coil, spool, or reel, specific lengthswith or without ends, and4.1.9 When material is purchased for agencies of the U.S.government (Spec

11、ification B 250/B 250M).4.2 The following options are available to this specificationand should be specified in the contract or purchase order whenrequired:4.2.1 Certification (Specification B 250/B 250M, and1This specification is under the jurisdiction ofASTM Committee B05 on Copperand Copper Alloy

12、s and is the direct responsibility of Subcommittee B05.02 on Rod,Bar, Wire, Shapes, and Forgings.Current edition approved Oct. 1, 2005. Published November 2005. Originallyapproved in 1940. Last previous edition approved in 2001 as B 134/B 134M 01.2For referenced ASTM standards, visit the ASTM websit

13、e, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor D

14、rive, PO Box C700, West Conshohocken, PA 19428-2959, United States.4.2.2 Mill test report (Specification B 250/B 250M.5. Materials and Manufacture5.1 MaterialThe material shall be made from cast billets,logs, or rods of Copper Alloy UNS Nos. C21000, C22000,C22600, C23000, C23400, C24000, C26000, C27

15、000, orC27400, of such purity, soundness, and structure to be suitablefor processing into the desired product.5.2 ManufactureThe products shall be manufactured bysuch hot working, cold working, and annealing processing as toproduce a uniform wrought structure in the finished product.6. Chemical Comp

16、osition6.1 The material shall conform to the chemical composi-tional requirements specified in Table 1 for the copper alloyspecified in the ordering information.6.1.1 When all elements specified for a given alloy in Table1 are determined, their sum of results shall be as follows:Alloy UNS Nos.Sum of

17、 Re-sults,Percent,MinimumC21000, C22000, C22600, C23000,C23400, C2400099.8C26000, C27000, C27400 99.76.2 These composition limits do not preclude the presenceof other elements. Limits may be established and analysisrequired for unnamed elements by agreement between themanufacturer or supplier and th

18、e purchaser.6.3 Zinc, listed as the “remainder,” is the difference betweenthe sum of results for all elements determined and 100 %.7. Temper7.1 The product in drawn or rolled wire of UNS Alloy Nos.C21000, C22000, C22600, C23000, C23400, C24000,C26000, C27000, and C27400 shall be available in H00, H0

19、1,H02, H03, H04, H06, H08, and H10 tempers as defined inClassification B 601.7.1.1 Product made in H04 temper is not generally availablein sizes over12 in. 13 mm in diameter.7.1.2 Product made in H06 temper is not generally availablein sizes over38 in. 10 mm in diameter.7.1.3 Product made in H08 tem

20、per is not generally availablein sizes over14 in. 6 mm in diameter.7.1.4 Square product is not generally available in H06 orH08 tempers.7.1.5 The tension test shall be the standard temper test forall H temper wire.7.1.6 The product in annealed form of UNS Alloys Nos.C21000 and C22000 shall be availa

21、ble in OS050, OS035,OS025, and OS015 tempers as defined in Classification B 601.7.1.7 The product in annealed form of UNS Alloy Nos.C22600, C23000, C23400, and C24000 shall be available inOS070, OS050, OS035, OS025, OS015, and OS010 tempers asdefined in Classification B 601.7.1.8 The product in anne

22、aled form of UNS Alloy Nos.C26000, C27000, and C27400 shall be available in OS120,OS070, OS050, OS035, OS025, and OS015 tempers as definedin Classification B 601.8. Grain Size for Annealed Wire8.1 Grain size shall be the standard requirement for allproduct in the annealed tempers.8.2 Acceptance or r

23、ejection based on grain size shall dependonly on the average grain size of test specimens taken fromeach of two sample portions and each specimen shall be withinthe limits prescribed in Table 2 when determined in accordancewith Test Methods E112.9. Mechanical Property Requirements9.1 Tensile Strengt

24、h Requirements:9.1.1 Drawn or rolled product shall conform to the require-ments specified in Tables 3-6, by alloy and temper, for wire0.020 in. 0.5 mm and over in diameter or distance betweenparallel surfaces.9.1.1.1 The temper of wire under 0.020 in. 0.5 mm indiameter or distance between parallel s

25、urfaces shall be subjectto agreement between the manufacturer, or supplier, and thepurchaser.9.1.2 Rectangular product, furnished in the “H” tempersshall conform to the requirements in Tables 5 and 6 for thetemper and CopperAlloy UNS No. designation specified in theordering information when tested i

26、n accordance with TestMethods E8or E8M.9.1.3 Acceptance or rejection based upon mechanical prop-erty shall depend on the tensile strength values obtained whentested in accordance with Test Methods E8or E8M.TABLE 1 Chemical RequirementsCopper AlloyUNS No.Composition, %Copper Lead, max Iron, max ZincC

27、21000 94.096.0 0.05 0.05 remainderC22000 89.091.0 0.05 0.05 remainderC22600 86.089.0 0.05 0.05 remainderC23000 84.086.0 0.05 0.05 remainderC23400 81.084.0 0.05 0.05 remainderC24000 78.581.5 0.05 0.05 remainderC26000 68.571.5 0.07 0.05 remainderC27000 63.068.5 0.10 0.07 remainderC27400 61.064.0 0.10

28、0.05 remainderB 134/B 134M 0529.2 Rockwell Hardness:9.2.1 The approximate Rockwell hardness values for rect-angular other than square wire given in Table 2, Table 5, andTable 6 are for general information and assistance in testingand shall not be used as a basis for product rejection.TABLE 2 Grain S

29、ize Requirements and Approximate Rockwell Hardness Values for Annealed WireTemperDesignationGrain Size, mmApproximate Rockwell Hardness for Rectangular WireAF Scale 30-T ScaleStandard(B 601)Nominal Min Max Min Max Min MaxCopper Alloy UNS No. C21000OS050 0.050 0.035 0.090 40B52B. 4OS035 0.035C0.025 0

30、.050 47B54B. 7OS025 0.025 0.015 0.035 50B61B11OS015 0.015CD0.025 54B65B723Copper Alloy UNS No. C22000OS050 0.050 0.035 0.090 50 60 1 16OS035 0.035C0.025 0.050 54 64 7 21OS025 0.025 0.015 0.035 58 70 13 31OS015 0.015CD0.025 62 75 19 39Copper Alloy UNS Nos. C22600, C23000, and C23400OS070 0.070 0.050

31、0.100 53 60 6 16OS050 0.050C0.035 0.070 56 63 10 20OS035 0.035C0.025 0.050 58 66 13 24OS025 0.025C0.015 0.035 60 72 16 34OS015 0.015CD0.025 62 79 19 48OS010 0.010 0.015 66 83 25 50Copper Alloy UNS No. C24000OS070 0.070 0.050 0.120 53 64 2 21OS050 0.050C0.035 0.070 57 67 8 27OS035 0.035C0.025 0.050 6

32、1 72 16 35OS025 0.025C0.015 0.035 63 77 20 42OS015 0.015CD0.025 66 83 25 50Copper Alloy UNS Nos. C26000, C27000, and C27400OS120 0.120 0.070 . 50 62 . 21OS070 0.070 0.050 0.120 52 67 3 27OS050 0.050 0.035 0.070 61 73 20 35OS035 0.035 0.025 0.050 65 76 25 38OS025 0.025 0.015 0.035 67 79 27 42OS015 0.

33、015D0.025 72 85 33 50ARockwell hardness values apply as follows: The F scale applies to metal 0.020 in. 0.5 mm in thickness and over; the 30-T scale applies to metal 0.015 in. 0.4 mmin thickness and over.BCopper Alloy UNS No. C21000 in these several OS (annealed) tempers is too soft for Rockwell F h

34、ardness tests below 0.030 in. 0.75 mm in thickness.CThe nominal grain sizes are those in which wire other than rectangular are normally available. Rectangular wire is normally available in any of the nominal grain sizeslisted.DAlthough no minimum grain size is required, the material must be fully re

35、crystallized.TABLE 3 Tensile Strength Requirements for Round, Hexagonal, Octagonal, and Square Wire 0.020 in. and Over in Diameter or DistanceBetween Parallel SurfacesTemper Designation Tensile Strength, ksiACode NameCopper Alloy UNSNo.C21000Copper Alloy UNSNo.C22000Copper Alloy UNSNos. C22600and C2

36、3000Copper Alloy UNSNos. C23400and C24000Copper Alloy UNS Nos.C26000, C27000,and C27400Min Max Min Max Min Max Min Max Min MaxH00 eighth-hard 35 45 38 50 43 57 50 65 50 65H01 quarter-hard 41 51 45 57 53 65 62 75 62 77H02 half-hard 49 58 56 67 66 77 78 90 79 94H03 three-quarter hard 57 64 64 74 76 86

37、 90 101 92 107H04Bhard 61 68 70 79 83 92 100 110 102 117H06C,Dextra-hard 66 73 78 86 94 102 112 121 115 129H08E,Dspring 72 . 84 . 100 . 116 . 120 .Aksi = 1000 psi.BH04 (hard) temper wire is not generally available in sizes over12 in. in diameter.CH06 (extra-hard) temper is not generally available in

38、 sizes over38 in. in diameter.DSquare wire is not generally available in extra hard or spring tempers.EH08 (spring) temper is not generally available in sizes over14 in. in diameter.B 134/B 134M 053NOTE 1The Rockwell hardness test offers a quick and convenientmethod of checking for general complianc

39、e with properties for tempercondition.10. Dimensions, Mass, and Permissible Variations10.1 The dimensions and tolerances for product describedby this specification shall be as specified in SpecificationsB 250/B 250M with particular reference to the following tablesand related paragraphs in those spe

40、cifications:10.1.1 Diameter or Distance Between Parallel SurfacesTable 1 in B 250/B 250M.10.1.2 ThicknessTable 3 in Specifications B 250/B 250M.10.1.3 WidthTable 5 in Specification B 250/B 250M.10.1.4 LengthTables 7 and 8 in Specification B 250/B 250M.10.1.5 StraightnessTable 9 in Specification B 25

41、0/B 250M.10.1.5.1 This requirement is applicable to rectangular andsquare product only when ordered in lengths.10.1.6 Edge ContourRefer to the section on edge contour.11. Test Methods11.1 Chemical Analysis11.1.1 Composition shall be determined, in case of disagree-ment, as follows:Element Test Metho

42、dCopper E 478Lead E 478 (AA)Iron E 478Zinc E 478 (Titrametric)11.1.2 Test methods to be followed for the determination ofelements resulting from contractual or purchase order agree-ment shall be as agreed upon between the manufacturer orsupplier and the purchaser.12. Keywords12.1 brass wire; copper-

43、alloy wire; copper-zinc alloy wire;general purpose wire; hexagonal wire; high strength wire;nonelectrical wire; octagonal wire; ornamental wire; rectangu-lar wire; round wire; spring wire; square wire; UNS No.C21000; UNS No. C22000; UNS No. C22600; UNS No.C23000; UNS No. C23400; UNS No. C24000; UNS

44、No.C26000; UNS No.C27000; UNS No. C27400; wireTABLE 4 Tensile Strength Requirements for Round, Hexagonal, Octagonal, and Square Wire 0.5 mm and Over in Diameter or DistanceBetween Parallel SurfacesTemper Designation Tensile Strength, MPaACode NameCopper Alloy UNSNo.C21000Copper Alloy UNSNo.C22000Cop

45、per Alloy UNSNos. C22600and C23000Copper Alloy UNSNos. C23400and C24000Copper Alloy UNS Nos.C26000, C27000,and C27400Min Max Min Max Min Max Min Max Min MaxH00 Eighth-hard 240 310 260 345 295 395 345 450 345 450H01 Quarter-hard 285 350 310 395 365 450 425 515 425 530H02 Half-hard 340 400 385 460 455

46、 530 540 620 545 650H03 Three-quarter hard 395 440 440 510 525 595 620 695 635 740H04BHard 420 470 485 545 570 635 690 760 705 805H06C,DExtra-hard 455 505 540 595 650 700 770 835 795 890H08E,DSpring 495 . . . 580 . . . 690 . . . 800 . . . 830 . . .ASee Appendix X1.BH04 (hard) temper wire is not gene

47、rally available in sizes over 13 mm in diameter.CH06 (extra-hard) temper is not generally available in sizes over 10 mm in diameter.DSquare wire is not generally available in extra hard or spring tempers.EH08 (spring) temper is not generally available in sizes over 6 mm in diameter.B 134/B 134M 054T

48、ABLE 5 Tensile Strength Requirements and Approximate Rockwell Hardness Values for Rectangular WireTemper DesignationTensile Strength,ksiApproximate Rockwell HardnessAB Scale Superficial 30-TStandard(B 601)Former Min Max0.020 to0.036 in.inclOver 0.036in.0.012to0.028 in.inclOver 0.028in.Copper Alloy U

49、NS No. C21000H01 quarter-hard 37 47 20-48 24-52 34-51 37-54H02 half-hard 42 52 40-56 44-60 46-57 48-59H03 three-quarter-hard 46 56 50-61 53-64 52-60 54-62H04 hard 50 59 57-64 60-67 57-62 59-64H06 extra hard 56 64 64-70 66-72 62-66 63-67H08 spring 60 68 68-73 70-75 64-68 65-69H10 extra spring 61 69 69-74 71-76 65-69 66-70Copper Alloy UNS No. C22000H01 quarter-hard 40 50 27-52 31-56 38-53 41-56H02 half-hard 47 57 50-63 53-66 52-61 54-63H03 three-quarter-hard 52 62 59-68 62-71 58-64 60-66H04 hard 57 66 65-72 68-75 62-66 64-68H06 extra hard 6