ASTM A459-2008(2013) Standard Specification for Zinc-Coated Flat Steel Armoring Tape《镀锌平轧扁钢铠装带标准规格》.pdf

《ASTM A459-2008(2013) Standard Specification for Zinc-Coated Flat Steel Armoring Tape《镀锌平轧扁钢铠装带标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM A459-2008(2013) Standard Specification for Zinc-Coated Flat Steel Armoring Tape《镀锌平轧扁钢铠装带标准规格》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A459 08 (Reapproved 2013)Standard Specification forZinc-Coated Flat Steel Armoring Tape1This standard is issued under the fixed designation A459; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revisio

2、n. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers requirements for zinc-coatedflat steel tape in coils for use as interlocking armor and flatarmor for ele

3、ctrical cables. The zinc-coated tape is producedwith three classes of zinc coating weight.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered stan

4、dard.2. Referenced Documents2.1 ASTM Standards:2A90/A90M Test Method for Weight Mass of Coating onIron and Steel Articles with Zinc or Zinc-Alloy CoatingsA902 Terminology Relating to Metallic Coated Steel Prod-uctsB6 Specification for Zinc3. Terminology3.1 Definitions See Terminology A902 for defini

5、tions ofgeneral terminology relating to metallic-coated steel products.4. Ordering Information4.1 Orders for material under this specification shall includethe following information:4.1.1 Quantity of each size,4.1.2 Width and thickness (see 13),4.1.3 Class of coating (see 11), and4.1.4 Packaging req

6、uirements (see 17).5. Materials and Manufacture5.1 The base metal shall be steel made by the basic-oxygen,or electric-furnace process and of such quality that whenprocessed and coated with zinc, the finished tape shall have theproperties and characteristics prescribed in this specification.5.2 The u

7、ncoated tape shall have a mill finish and may haveeither a mill or slit edge. If the uncoated tape is manufacturedby slitting or shearing, slitting burrs shall be kept to a minimumconsistent with good commercial practice.5.3 The zinc shall be applied by either the hot-dip or theelectrogalvanizing pr

8、ocess by a final operation so that allsurfaces including edges are coated.5.4 The slab zinc when used shall conform to any grade ofzinc described in Specification B6.6. Joints6.1 The zinc-coated tape shall be furnished in coils of onecontinuous length, with not more than an average of oneweld/50 lb

9、(23 kg). Only welds made prior to the zinc coatingoperation shall be permitted and the area of such welds shallconform to the standard tolerance for thickness. The weldsshall be smooth and free of sharp projections.7. Sampling7.1 During the visual inspection specified in Section 16, theinspector sha

10、ll select at random, 1 sample coil from every 10coils in the first 100 coils of the lot and 1 sample coil for everyadditional 35 coils, but not less than 3 coils from the entire lot.7.2 From each coil of zinc-coated tape thus selected, asample of suitable length shall be taken for the weight ofcoati

11、ng and the mechanical tests as specified in Sections 8 to12.7.3 Any sample that indicates the presence of a weld shallbe discarded and another sample shall be taken from the coilfor testing.8. Tensile Strength8.1 The zinc-coated tape shall have a tensile strength of 70ksi (483 MPa), maximum. The ten

12、sile strength shall bedetermined on longitudinal specimens consisting of the fullwidth of the tape when practical, or a straight specimen cut orsheared from the center of the tape.9. Elongation9.1 The zinc-coated tape shall have an elongation of not lessthan 10 % in 10 in. (254 mm). The elongation s

13、hall be1This specification is under the jurisdiction of ASTM Committee A05 onMetallic-Coated Iron and Steel Products and is the direct responsibility ofSubcommittee A05.11 on Sheet Specifications.Current edition approved April 1, 2013. Published April 2013. Originallyapproved in 1961. Last previous

14、edition approved in 2008 as A459 08. DOI:10.1520/A0459-08R13.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.

15、Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1determined as the permanent increase in length, after failure ofa marked section of the tape specimen originally 10 in. inlength.10. Ductility10.1 The tape shall be capable of being bent

16、 flat on itself,either lengthwise or crosswise, without indication of failure.There shall be no base metal cracks along any bend visible tothe naked eye. Cracks at sheared edges and coarse grains on thebends of any specimens may be disregarded. Flaking orcracking of the galvanized finish shall not b

17、e interpreted as afailure of the material.11. Weight of Coating11.1 The weight of zinc coating shall not be less than thatprescribed for the class specified, as follows:Class Weight of Zinc Coating, oz/ft2(g/m2) (Total of Both Surfaces and Both Edges)Class I 0.35 (110)Class II 0.70 (210)Class III 1.

18、00 (300)11.2 The weight of zinc coating specified is the total amounton both surfaces and both edges of the tape in ounces persquare foot (grams per square metre). The weight of zinccoating shall be calculated in accordance with the section onzinc-coated articles other than sheet or wire of Test Met

19、hodA90/A90M, using the following equation:C 5 W12 W2!/A) 3 N11.3 The weight of coating shall be determined by theHydrochloric Acid-Antimony Chloride Method prescribed inTest Method A90/A90M.12. Adherence of Coating12.1 The zinc coating shall remain adherent without flakingor spalling when the tape i

20、s subjected to a 180 bend over amandrel of the following diameter:Class Diameter of Mandrel,in. (mm)Classes I and IIClass III1/8 (3.18)5/8 (15.88)12.2 The zinc coating shall be considered as meeting thisrequirement if, when the tape is bent around the specifiedmandrel, the coating does not flake and

21、 none of it can beremoved from the tape by rubbing with the fingers. Looseningor detachment during the adherence test of superficial smallparticles of zinc formed by mechanical polishing of the surfaceof the zinc-coated tape shall not constitute failure in this test.13. Permissible Variations in Dim

22、ensions13.1 Width and ThicknessThe width and thickness of thefinished tape shall be expressed in decimal fractions of an inch.The variations in the width and thickness of zinc-coatedarmoring tape shall be within the limits specified in Table 1.13.2 CamberThe permissible camber for zinc-coated tapesh

23、all not exceed the amounts specified in Table 2.14. Workmanship and Finish14.1 The surface of the tape shall be free of injurious scale,flaws, seams and splits, and other imperfections not consistentwith good commercial practice. The zinc coating shall besmooth and continuous.15. Inspection15.1 The

24、manufacturer shall afford the inspector represent-ing the purchaser all reasonable facilities, without charge, tosatisfy him that the material is being furnished in accordancewith this specification. All tests and inspections shall be madeat the place of manufacture prior to shipment, unless otherwi

25、seagreed upon at the time of the purchase, and shall be soconducted as not to interfere unnecessarily with the operationof the works.16. Rejection16.1 The inspector shall visually examine the entire ship-ment or lot of coils for surface imperfections. The purchasermay reject the entire lot if after

26、visual examination, more than3 % of the coils in the entire lot are found defective, or if morethan 3 % of the samples selected in accordance with Section 6fail to pass any of the tests specified in Sections 8 to 13.IfnotTABLE 1 Permissible Variations in Dimensions of Zinc-Coated TapeNominal Ordered

27、 Width, in. (mm) Width Tolerance,in. (mm)Nominal Ordered Thickness, in. (mm) Thickness Toler-ance, in. (mm)0 to 1.500 (0 to 38.100), incl 0.008 (0.20) 0.020 to 0.025 (0.51 to 0.635) +0.002 (+0.05)0.001 (0.03)0.0251 to 0.035 (0.64 to 0.889) +0.0025 (+0.06)0.0015 (0.04)0.0351 to 0.045 (0.892 to 1.143)

28、 +0.003 (+0.08)0.002 (0.05)0.0451 to 0.063 (1.15 to 1.600) +0.0035 (+0.09)0.0025 (0.06)1.5001 to 3.000 (38.103 to 76.20), incl 0.010 (0.25) 0.020 to 0.025 (0.51 to 0.635) +0.002 (+0.05)0.002 (0.05)0.0251 to 0.035 (0.64 to 0.889) +0.003 (+0.08)0.002 (0.02)0.0351 to 0.045 (0.892 to 1.143) +0.003 (+0.0

29、8)+0.004 (+0.01)0.0451 to 0.063 (1.15 to 1.600) 0.003 (0.08)A459 08 (2013)2more than 3 % of the samples fail, a second set of samples,consisting of two specimens from each of the coils from whichthe original nonconforming samples were taken, shall be cutand tested for the nonconforming properties. I

30、f any of thesesamples fail, the purchaser may reject the entire lot.17. Packaging17.1 The finished zinc-coated tape shall be furnished incompact coils reasonably symmetrical in shape. The weight,inside diameter, and method of banding of the coils shall beagreed upon between the manufacturer and the

31、purchaser.18. Marking18.1 A durable tag showing the nominal size of tape and thename or mark of the manufacturer shall be securely attached toone coil on each pallet. The starting end of each coil shall beindicated by a suitable tag.ASTM International takes no position respecting the validity of any

32、 patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revi

33、sion at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your

34、comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyri

35、ghted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org

36、(e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).TABLE 2 Permissible Camber of Zinc-Coated TapeNominal Ordered Width, in. (mm) Permissible Camber,in.in8ft0 to 1.500 (0 to 38.100), incl1.501 to 3.000 (38.103 to 76.20), incl0.500.25A459 08 (2013)3