《ARMY A-A-59745-2002 ZINC-RICH COATINGS [Superseded ARMY DOD-PRF-24648 CANC NOTICE 1 NAVY DOD-PRF-24648 (1) NAVY DOD-PRF-24648]《富锌涂料》.pdf》由会员分享，可在线阅读，更多相关《ARMY A-A-59745-2002 ZINC-RICH COATINGS [Superseded ARMY DOD-PRF-24648 CANC NOTICE 1 NAVY DOD-PRF-24648 (1) NAVY DOD-PRF-24648]《富锌涂料》.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、METRIC A-A-59745 October 9, 2002 COMMERCIAL ITEM DESCRIPTION ZINC-RICH COATINGS The General Services Administration has authorized the use of this commercial item description, for all federal agencies. 1. SCOPE. This commercial item description (CID) covers coatings used in the corrosion protection

2、of steel structures. These coatings use zinc-rich particles that make up part of the pigment content to provide sacrificial cathodic protection to steel substrates. 2. SALIENT CHARACTERISTICS. 2.1 Materials. Unless specified herein, materials shall be in accordance with the manufacturers material sp

3、ecifications. The use of recovered material made in compliance with regulatory requirements is acceptable providing that all requirements of this CID are met (see 4.1). 2.1.1 Zinc particles. The minimum (min) percentage (%) of zinc particles by dry film thickness (DFT) weight shall be 90%. 2.2. Conf

4、iguration. The coating composition, where zinc particles make up part of the pigment content of the zinc-rich paints, shall be capable of being applied by spraying or brushing and be compatible with CARC primers and topcoats per Army Drawing 12369000 (see 6.1.4 and 6.2). 2.3. Performance. The zinc-r

5、ich paints shall meet the following tests requirements and sample preconditioning requirements of table I: a. Accelerated corrosion (cyclic) b. Adhesion pull-off c. Adhesion cross-cut d. Mandrel bend Beneficial comments, recommendations, additions, deletions, clarifications, etc. and any data that m

6、ay improve this document should be sent by letter to: U.S. Army Tank-automotive and Armaments Command, ATTN: AMSTA-TR-E/ESA, 6501 E 11 Mile Road, Warren, MI 48397-5000 AMSC N/A FSC 8010 DISTRIBUTION STATEMENT A. Approved for public release; distribution is unlimited. Provided by IHSNot for ResaleNo

7、reproduction or networking permitted without license from IHS-,-,-A-A-59745 2 2.3.1 Accelerated corrosion test. The General Motors GM9540P “Accelerated Corrosion Test” (see 6.1.6) demonstrates the procedures to be used in cyclic corrosion testing for establishing acceptable levels of rust, blisterin

8、g and cutback. NOTE: For statistical analysis, a min of three (3) samples per performance test requirements shall be evaluated (min of 15 samples total). 2.3.1.1 Sample preparation. Sample preparation shall be performed in accordance with (IAW) the manufacturers recommendations and/or the system req

9、uirements by an operator experienced in the application of zinc-rich paints and CARC coatings. The following application and recommended curing samples will be preconditioned prior to testing. Table I shows the precondition methods for each performance requirement listed under section 2.3. TABLE I.

10、Sample preconditioning requirements. Performance requirements Precondition method 1 Precondition method 2 Accelerated corrosion test Scribe (IAW ASTM D1645) Chipped (IAW SAE J400) Adhesion pull-off N/A Adhesion cross-cut N/A Mandrel bend N/A Note: Only one precondition method is to be performed per

11、sample. 2.3.1.2 Rust. The zinc-rich paint test sample shall show no more than a maximum (max) presence of corrosion (red rust) over less than 5% of the surface area (stage 2) after 120 cycles of corrosion testing. The inspection rust rating shall be 2 as measured in accordance with the TACOM “Corros

12、ion Rating System” (see 6.1.5). No sample shall exhibit any stage 3 or 4 corrosion during or after 120 cycles of testing. 2.3.1.3 Blistering. The zinc-rich paint test sample shall have no more than a max composite blister rating of 5.3 after 120 cycles as tested when evaluated in accordance with AST

13、M D714 and converted using table II. Table II defines the size and density of the blisters. TABLE II. Composite blister index. Density Size Few (F) Medium (M) Medium Dense (MD)Dense (D) 10 10.0 10.0 10.0 10.0 9 9.22 8.75 8.00 4.80 8 8.44 7.50 6.00 3.50 7 7.67 6.25 4.60 1.60 6 6.89 5.00 3.70 1.10 5 6

14、.11 4.40 3.00 0.90 4 5.33 3.80 2.50 0.75 3 4.56 3.20 2.10 0.55 2 3.78 2.60 1.65 0.35 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-A-A-59745 3 TABLE II. Composite blister index - Continued. Density Size Few (F) Medium (M) Medium Dense (MD)Dense (D)

15、 1 3.00 2.00 1.00 0.00 0 0.00 0.00 0.00 0.00 NOTE: Number (NO.) 10 size represents no blistering and NO. 8 size represents the smallest size blister easily seen by the unaided eye. 2.3.1.4 Cutback test. The zinc-rich paint test sample shall have a max scribed cutback of no greater than 3.7 millimete

16、rs (mm) (0.15 inch (in.) and show no signs of underfilm corrosion initiating from the intentional scribe prior to the completion of the 120 cycles. 2.3.2 Adhesion pull-off test. The zinc-rich paint test sample shall have a min acceptable adhesion strength of 27.1 kilograms per square centimeter (kg/

17、cm2)(385 pounds per square inch (psi) with failure to the substrate allowed after 120 cycles of corrosion testing and as measured in accordance with ASTM D4541. 2.3.3 Adhesion cross-cut test. The zinc-rich paint test sample shall have a min acceptable cross-cut adhesion strength rating of 1.65 after

18、 the completion of 120 cycles of corrosion testing and as measured in accordance with ASTM D3359. Use method A (X-cut) for systems having a total system thickness greater than 0.127 mm (0.005 in.) or method B (cross-hatch) for systems having a total system thickness less than 0.127 mm. 2.3.4 Mandrel

19、 bend test. The zinc-rich paint test sample shall have a max acceptable crack length of 140 mm (5.5 in.) after the 120 cycles of accelerated corrosion testing and as measured in accordance with ASTM D522, testing over a conical mandrel. 2.4 Identification and markings. Identification and markings sh

20、all be permanent, legible and shall include, as a minimum, the Commercial and Government Entity (CAGE) code, contract number and part number. 3. REGULATORY REQUIREMENTS. The offeror/contractor is encouraged to use recovered materials to the maximum extent practicable, in accordance with paragraph 23

21、.403 of the Federal Acquisition Regulation (FAR) (see 6.1.1). 4. PRODUCT CONFORMANCE. The products provided shall meet the salient characteristics of this CID, conform to the producers own drawings, specifications, standards, and quality assurance practices, and be the same product offered for sale

22、in the commercial marketplace. The Government reserves the right to require proof of such conformance (see 6.2). Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-A-A-59745 4 4.1 Responsibility for inspection. The contractor is responsible for the perf

23、ormance of all inspections (examinations and tests). 5. PACKAGING. Preservation, packing, and marking shall be as specified in the contract or order (see 6.2). 6. NOTES. 6.1 Source of documents. 6.1.1 The Code of Federal Regulations (CFR) may be obtained from the Superintendent of Documents, U.S. Go

24、vernment Printing Office, Washington, DC 20402. 6.1.2 ASTM International ASTM D522, “Standard Test Methods for Mandrel Bend Test of Attached Organic Coatings”; ASTM D714, “Standard Test Method for Evaluating Degree of Blistering of Paints”; ASTM D3359, “Standard Test Methods for Measuring Adhesion b

25、y Tape Test” and ASTM D4541, “Standard Test Method for Pull-Off Strength of Coatings Using Portable Adhesion Testers” are available from ASTM International, PO Box C700, 100 Barr Harbor Drive, West Conshohocken, PA 19428-2959 or website: www.astm.org 6.1.3 SAE J400, “Test for Chip Resistance Of Surf

26、ace Coat” is available from the Society of Automotive Engineers, Inc., 400 Commonwealth Drive, Warrendale, PA 15096-0001 or website: www.sae.org 6.1.4 Army Drawing 12369000, “Paint Systems Index” is available from the Contracting Officer, U.S. Army Tank-automotive and Armaments Command, 6501 E. 11 M

27、ile Road, Warren, MI 48397-5000. 6.1.5 “TACOM Corrosion Rating System” is available from the Contracting Officer, U.S. Army Tank-automotive and Armaments Command, 6501 E. 11 Mile Road, Warren, MI 48397-5000. 6.1.6 GM9540P,“Accelerated Corrosion Test” is available from General Motors Corporation, c/o

28、 Global Engineering Documents, 15 Inverness Way East, Inglewood, CO 80112. 6.2 Ordering data. The contract or order should specify the following: a. CID document number and revision. b. Color of paint if required (see 2.2). c. Product conformance provisions (see 4). d. Packaging requirements (see 5)

29、. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-A-A-59745 5 6.3 Key words. Corrosion protection Corrosion resistance Paints Pigments MILITARY INTERESTS: CIVIL AGENCY COORDINATING ACTIVITY: GSA-FSS Custodians: Army - AT Preparing Activity: Navy - SH Army - AT Review Activities: (Project 8010-0178) Army - MI, MR Navy - AS, CG Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-