AECMA PREN 2545-1-1991 Aerospace Series Titanium and Titanium Alloy Remelting Stock and Castings - Technical Specification - Part 1 - General Requirements Edition 1《航空航天系列 钛和钛合金制预制.pdf

《AECMA PREN 2545-1-1991 Aerospace Series Titanium and Titanium Alloy Remelting Stock and Castings - Technical Specification - Part 1 - General Requirements Edition 1《航空航天系列 钛和钛合金制预制.pdf》由会员分享，可在线阅读，更多相关《AECMA PREN 2545-1-1991 Aerospace Series Titanium and Titanium Alloy Remelting Stock and Castings - Technical Specification - Part 1 - General Requirements Edition 1《航空航天系列 钛和钛合金制预制.pdf（10页珍藏版）》请在麦多课文档分享上搜索。

1、CEN PREN*:2545 (PT*l)*ED*L 71 m 340q587 0035765 O Approved by COMITE DE NORMALISATION of A.E.C.M.A. 1991-06-25 A. E .C. M .A. STAN DARD NORME A.E.C.M.A. A.E.C.M.A. NORM The cqiiivalenl versioiis iii French and Gcrnian languages can be supplied by 8.N.A.E . Tachiiopolis 54 199. rue Jean-Jacques Rouss

2、eau 92138 ISSY LES MOULINEAUX CEDEX - FRANCE prEN 2545 Part 7 Edition 1 June 1991 EDITE PAR LASSOCIATION EUROPEENNE DES CONSTRUCTEURS DE MATERIEL AEROSPATIAL 88, boulevard Malesherbes, 75008 PARIS - TeL. 45-63-82-85 UDC : Key words : ENGLISH VERSION Aerospace series Titanium and titanium alloy remel

3、ting stock and castings - Technical specification - Part 1 - General requirements Srie arospatiale Luft- und Raumfahrt Produits pour refusion et pices moules en titane et alfiages de titane - Spcification technique - Partie 1 - Exigences gnrales Vormaterial und Gupstclce aus Titan und Titanlegierung

4、en - Technische Lieferbedingungeii - Teil I - Allgemeine Anforderungen This (Aerospace series standardhas been dra.wn up under the responsibility ofAECMA (Association Europenne des Constructeurs de Matriel Arospatial). it is published on yellow paper in three equivalent versions (English, French, Ge

5、rman). It will be submitted as a draft European Standard to CEN (European Committee for Standardization) for final vote. Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without lic

6、ense from IHS-,-,-CEN PREN*2545 (PT*L)*ED*L 91 3404589 00L59bb 2 prEN 2545-1 Page 2 Contents 1 2 3 4 5 6 7 13 9 10 11 12 13 Scope and field of application References Defi ni tions Qual i ty assurance Manufacture Traceabi 1 i ty Freedom from defects Testing Marking Ac cep tance Inspection and test re

7、port Packing Wording of orders Annex A Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-CEN PREN*Z545 (PT*L)*ED*L 91 3404589 0035967 4 - - - - prEN 2545

8、-1 Page 3 1 This standard defines the general requirements for the manufacture, inspection and testing of remelting stock intended to be used for the production of castings and of castings in titanium and titanium alloys unless otherwise stated on the drawing, order or inspection schedule. Particula

9、r requirements are defined in EN 2545-2 and EN 2545-3. Scope and field of application This standard shall be applied in conjunction with EN material standards unless otherwise specified on the drawing, order or inspection schedule. By agreement between the manufacturer and the purchaser it may also

10、be applied to other materials or delivery conditions not covered by EN standards, The agreements shall be formalized by reference to this standard on the drawing, order or inspection schedule. 2 References EN 2000 Aerospace series - Quality assurance - EN aerospace products - Approval of he quality

11、system of manufacturers 1) EN 2078 Manufacturing schedule, inspection schedule and inspection report - General definitions - Aerospace series 1) EN 2545-2 Aerospace series ,. Titanium and titanium alloy remelting stock and castings - Technical specification - Part 2 - Remelting stock 2) EN 2545-3 Ae

12、rospace series - Titanium and titanium alloy remelting stock and castings - Technical specification - Part 3 - Pre-production and production castings 2) 3 Definitions The chart given in annex A completes the following definitions. 3.1 Charge Different materials that make up a furnace charge to be me

13、lted in order to obtain a parent cast or castings. 1) Published as AECMA Standard at the date of publication of the present 2) In preparation at the date of publication of the present standard. standard. Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under

14、license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-CEN PREN*Z545 (PT*L)*ED*L 91 W 3404589 OB159b8 b W prEN 2545-1 Page 4 3.2 Melt A mass of homogeneous liquid metal from a single charge. 3.3 Remelt Solid metal resulting from a single melt. 3.4 Parent

15、 cast A cast of remelting stock to be used for the production of castings. 3.5 Remelting stock Metal supplied in cast or wrought form, the composition of which has established by chemical analysis. 3.6 Casting A part manufactured by vacuum arc remelting (VAR) or electron beam me (EBM) . 3.7 Pre-prod

16、uction castings been ti ng Castings produced to a particular design which qualify the method of manufacture and mould configuration and demonstrate that the requirements of the purchaser can be met. 3.8. Batches 3.8.1 Batch of re-melting stock It shall consist of re-melting stock of the same form, t

17、he same nominal dimensions and from the same parent-cast, 3.8.2 Batch of castings It shall consist of castings of the same part number, coming from the same melting operation for EBM process or from the same electrode without alteration of the melting conditions for VAR process. They have been submi

18、tted together to hot isostatic pressing and, if applicable, to heat treatment. 3.8.3 Batch of scrap It shall consist of materials of the same type (see 4.21, of the same chemical composition and, if appropriate, submitted to the same conditioning operations. 3.9 Inspection schedule See EN 2078. Copy

19、right Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-o 3.10 Manufacturing schedule See EN 2078. 3.11 Inspection and testing report See EN 2078. 4 Quality assura

20、nce 4.1 General See EN 2000. 4.2 Scrap approval Scrap shall be : - prepared according to a procedure approved by the purchaser. The procedure shall include verification of chemical composition, freedom from contamination and the absence of foreign material. - approved by : . the scrap purchaser, . .

21、 the purchaser of remelting stock electrodes (VAR process), or the purchaser of the castings (EBM process). Additional requirements are given in EN 2545-2 and in EN 2545-3. 5 Manufacture 5.1 The method of melting shall be in accordance with EN 2545-2 or EN 2545-3, 5.2 The details of manufacture shal

22、l be recorded in the manufacturing schedule. o 5.3 When a manufacturing schedule has been agreed, no change shall be made without the written approval of the purchaser, 5.4 Unless otherwise agreed . and stated on the drawing, order and/or manufacturing schedule, the product shall be delivered in the

23、 heat treatment condition specified in the material standard. h Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,- CEN PREN82545 (PT*L)*ED*L 93 3404589 0

24、035970 4 fi- 550 prEN 2545-1 Page 6 - 3.5 5.5 If a specific temperature (value and tolerance) is stated, that temperature shall be mandatory. If a temperature range is stated, a temperature within that range, reduced by the furnace tolerances, shall be selected to give the required properties. Unles

25、s otherwise specified, the furnace charge shall be maintained at the temperature subject to the following tolerances in table 1, for the period stated. Table 1 550 5 8 1250 Selected temperature Tolerances (“Cl - 3. 10 6 Traceabi 1 i ty 6.1 6.2 Each casting shall be traceable to its charge and batch

26、at all stages of manufacture and del ivery. Remelting stock shall be traceable to its charge. 7 Freedom from defects All remelting stock and castings shall be free from harmful defects. Not withstanding previous acceptance complying with this standard any remelting stock or casting found, at a later

27、 stage., to contain such defects may be rejected. 8 Testing The tests required by the material standard, order, inspection schedule or drawing, shall be made in accordance with the requirements of the appropriate test standard, If a test standard does not exist, the method to be.used shall be agreed

28、 between the manufacturer and the purchaser. Unless otherwise stated on the drawing or inspection schedule, the frequency of testing shall be as specified in EN 2545-2 or EN 2545-3. The location of test samples shall be as indicated on the drawing or inspection schedule. The test samples and associa

29、ted test pieces shall be marked in such a manner as to ensure that their identity and location with respect to the product and the batch is maintained. Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or n

30、etworking permitted without license from IHS-,-,-CEN PREN*2545 (PTUL )*ED*1 91 W 3404589 OL5rb=, prEN 2545-1 Page 7 8.1 Chemical composition It shall conform with the material standard and be determined on each melt or parent cast by means of representative samples. The method of analysis shall be s

31、elected by the manufacturer but in case of dispute, the method set out in the relevant IS0 standard shall be used. If no IS0 standard exists, a fundamental method of chemical analysis shall be used. Elements not specified in the material standard shall not be added without the agreement of the purch

32、aser. 8.2 Mechanical testing Preparation of test samples and test pieces : 8.2.1 Where appropriate, test samples shall be heat treated in accordance with the material standard requirements of use for the heat treatment. 8.2.2 The mechanical test specimens shall be machined in the heat treatment cond

33、ition of use in accordance with the requirements of the applicable EN standard. Their surface shall be absolutely free from contamination. 8.2.3 The strain rate up to the proof stress shall be within the range of 0,3 %/min to 0,7 %/min. In case of dispute a strain rate of 0,5 %/min shall be used. Af

34、ter proof stress the speed may be increased up to 5 %/min or such that failure occurs within approximately 1 min. 8.3 Special tests Special tests and inspections may be required by the purchaser (e.g. micro and macro structure examination). In such cases, after agreement between the purchaser and th

35、e manufacturer, nature of test, methods, frequency, acceptance criteria and the re-test procedure shall be specified on the order, drawing or inspection schedul e, 8.4 Re-tests If any requirement is not met, re-tests shall be carried out under the following conditions : If the test procedure or test

36、 piece preparation is faulty, testing shall be re-appled at the original frequency after identification of the failure cause. When failure cannot be attributed to faulty test procedure or test piece preparation, further test samples shall be selected at twice the original frequency. At least one of

37、the samples shall be taken from the product or products on which the non-conforming results were obtained (unless al ready withdrawn by the manufacturer after suitable identification of the cause of failure). Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS u

38、nder license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-CEN PREN*Z545 (PT*L)*ED*L 91 E 3404589 0015972 8 prEN 2545-1 Page 8 If all results are satisfactory, the batch shall be accepted. If one or more results are unsatisfactory, the batch shall be :

39、- rejected, or - re-heat treated and tested as a new batch, except for chemical compos and radiographic examination, 8.5 Re-heat treatment ti on With the exception of stress relieving no product or test sample shall be re-heat treated more than two times without the agreement of the purchaser. 9 Mar

40、king See : - - EN 2545-3 for castings. The frequency of examination adopted by the manufacturer shall be sufficient to permit him to certify compliance with the requirements. EN 2545-2 for remelting stock, 10 Acceptance If required the manufacturer shall inform the purchaser or his chosen agent of t

41、he planned dates for the extraction of samples and acceptance testing in order that these operations may be witn,essed. 11 Inspection and test report The manufacturer shall furnish with each delivery, an inspection and test report conforming to the requirements of EN 2078, and stating the following

42、: manufacturers name and address, order number, material standard number, drawing or part or product number, quantity, melt, parent cast and/or batch number( s) , nie1 ti ng process, casting process, condition of the material as delivered, batch and/or test samples heat treatment data if appropriate

43、, results of all tests, retests and chemical analysis, inspectors stamp. Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-CEN PREN82545 (PT*L)*ED*L 93 I

44、 3404589 0035973 T Ii - - - _ prEN 2545-1 Page 9 12 Packing O All necessary precautions shall be taken to prevent damage and corrosion during transport. The exterior of the packing shall bear the following information : - name of purchaser, - mass, - order number and sufficient information to enable

45、 package contents ta be related to the relevant documentation. 13 Wording of orders Orders shall clearly indicate : O quantities to be supplied, date (s) of delivery, material standard number, delivery condition of the material, dimensions of re-melting stock or casting number or its drawing number

46、with the re1 want i ssue number, i f appl icabl e, number of the inspection schedule and/or, where appropriate, manufacturing schedule , method of melting, if required, delivery address, nature and type of packing, where appropriate. Copyright Association Europeene des Constructeurs de Materiel Aero

47、spatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 2545-1 Page 10 CEN PREN*Z545 (PT*L)*ED*L 9L M 3404589 0015974 L I Not def Annex A Sketch to illustrate definitions I be used as requirements for the manufacturing p

48、rocess (given in the chapters ning manufacture in EN 2545-1, EN 2545-2 and EN 2545-3) blelter Melt 1 Reme 1 t II forging rolling Batch of remelting stock remelting stock electrodes L Founder Founder Vacuum Arc Remelting (VAR) electrodes 1 Castings Electron Beam Melting (BBM) Remelting Scrap Alloying stock I elements I Charge I I Melt/ i Castings Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-