BS S 163-1990 Specification for nickel-chromium-molybdenum-vanadium steel forging stock forgings bars and parts (1900 MPa limiting ruling section 100 mm)《锻坯 锻件 棒材和零件用镍-铬-钼-钒钢规范(1900MPa 限定控制剖面100mm.pdf
《BS S 163-1990 Specification for nickel-chromium-molybdenum-vanadium steel forging stock forgings bars and parts (1900 MPa limiting ruling section 100 mm)《锻坯 锻件 棒材和零件用镍-铬-钼-钒钢规范(1900MPa 限定控制剖面100mm.pdf》由会员分享,可在线阅读,更多相关《BS S 163-1990 Specification for nickel-chromium-molybdenum-vanadium steel forging stock forgings bars and parts (1900 MPa limiting ruling section 100 mm)《锻坯 锻件 棒材和零件用镍-铬-钼-钒钢规范(1900MPa 限定控制剖面100mm.pdf(8页珍藏版)》请在麦多课文档分享上搜索。
1、BRITISH STANDARD AEROSPACE SERIES BS S 163: 1990 Specification for Nickel-chromium- molybdenum-vanadium steel forging stock, forgings, bars and parts (1900 MPa: limiting ruling section 100 mm)BSS 163:1990 This British Standard, having been prepared under the directionof the Aerospace Standards Polic
2、y Committee, waspublished under the authorityof the Board ofBSIandcomes into effect on 31 October 1990 BSI 04-2000 The following BSI references relate to the work on this standard: Committee reference ACE/15 Draft for comment 89/73979 DC ISBN 0 580 18987 2 Committees responsible for this British Sta
3、ndard The preparation of this British Standard was entrusted by the Aerospace Standards Policy Committee (ACE/-) to Technical Committee ACE/15 upon which the following bodies were represented: British Forging Industry Association British Independent Steel Producers Association British Industrial Fas
4、teners Federation British Investment Casting Trade Association British Steel Industry British Steel Industry (Wire Section) Civil Aviation Authority (Airworthiness Division) Institute of British Foundrymen Ministry of Defence National Association of Steel Stockholders Rolls-Royce Limited Seamless St
5、eel Tube Association Society of British Aerospace Companies Limited Steel Casting Research and Trade Association Amendments issued since publication Amd. No. Date of issue CommentsBSS 163:1990 BSI 04-2000 i Contents Page Committees responsible Inside front cover Foreword ii 1 Scope 1 2 References 1
6、3 Technical requirements 1 Table 1 Technical requirements for Ni-Cr-Mo-V Steel 2BSS 163:1990 ii BSI 04-2000 Foreword This British Standard has been prepared under the direction of the Aerospace Standards Policy Committee and is a revision of MoD (PE) Specification DTD5192, which it supersedes. A Bri
7、tish Standard does not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a fro
8、nt cover, an inside front cover, pages i and ii, pages1 to 3 and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the inside front cover.BSS 163:1990 BSI 04-2000 1 1 Scope This British Standar
9、d specifies the chemical composition, mechanical properties and inspection and test requirements for a nickel-chromium-molybdenum-vanadium steel (iron base, Ni 1.75, Cr1.25, Mo 1, V 0.2) supplied in the following forms and as parts for general aerospace use. a) Forging stock, designation S 163A, col
10、umns2,3 and 4 of Table 1. b) Forgings, designation S 163C, columns5,6and7 of Table 1. c) Black bars for machining, designation S 163B, columns 8, 9 and 10 of Table 1. d) Bright bars for machining, designation S 163D, columns 11, 12 and 13 of Table 1. 2 References This standard makes reference to the
11、 following standards publications: BS S 100, Procedure for inspection and testing of wrought steels (other than sheet, strip and tubes). BS EN 2500, Guidelines for the preparation and use of standards for metallic materials 1) . 3 Technical requirements 3.1 The material in its delivery and use condi
12、tions shall comply with Table 1, the format and nomenclature of which comply with BS EN 2500. 3.2 This standard shall be used in conjunction with BS S 100, as given in Table 1, or as given in 3.3 to3.8. 3.3 One sample from the top and bottom of each ingot shall be taken for sulphur printing or deep
13、etching tests. 3.4 The material shall be overall dressed. 3.5 Before rehardening, the material shall be softened. 3.6 Material shall not be hardened and tempered more than two times. 3.7 Parts finally heat treated after machining shall comply with sections 1 and 7 of BS S 100. 3.8 Parts shall be sup
14、plied in the hardened and tempered condition. 1) In preparation.BSS 163:1990 2 BSI 04-2000 Table 1 Technical requirements for Ni-Cr-Mo-V Steel 1 Chemical composition % Element C Si Mn P S Cr Mo Ni V Fe min. 0.38 0.50 0.30 1.0 0.80 1.5 0.10 Base max. 0.46 0.80 0.80 0.010 0.010 1.50 1.20 2.0 0.30 2 1
15、2 3 4 5 6 7 3 Method of melting Vacuum arc remelted 4 Form Method of production Limit dimensions Forging stock D eu 100 mm Forgings D eu 100 mm 5 Acceptance standards Sections 1 and 5 of BS S 100 Sections 1 and 6 of BS S 100 6 Condition of supply and heattreatment prior to delivery Softened 960 C u
16、u 980 C/FC to 660 C and hold W 48 h/AC (1) (5) (7) 7 Condition of use and heattreatment prior to use As condition of supply Hardened and tampered 600 C u u 650 C/910 C u u 930 C/OQ(1) (2) (5) + u 70 C/W 2 h (3) + W 300 C 8 Test piece Heat treatment Sampling Condition ofsupply Machined or forged test
17、 sample See line 29 Condition ofsupply Reference heat treatment See line 29 9 Dimensions concerned D or a mm W 125 (6) W 125 (6) 10 Thickness of cladding oneach face % 11 Direction of sample L T L T 12 Tensile Temperature C Ambient temperature 13 Proof stress R p0.2 Mpa W 1540 W 1 540 14 Strength R
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
5000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制: