BS PD CEN TS 16969-2016 Paints and varnishes Coating materials and coating systems for exterior wood Assessment of end grain sealing performance《涂料和清漆 外部木材的涂层材料和涂层系统 端面纹理密.pdf

《BS PD CEN TS 16969-2016 Paints and varnishes Coating materials and coating systems for exterior wood Assessment of end grain sealing performance《涂料和清漆 外部木材的涂层材料和涂层系统 端面纹理密.pdf》由会员分享，可在线阅读，更多相关《BS PD CEN TS 16969-2016 Paints and varnishes Coating materials and coating systems for exterior wood Assessment of end grain sealing performance《涂料和清漆 外部木材的涂层材料和涂层系统 端面纹理密.pdf（14页珍藏版）》请在麦多课文档分享上搜索。

1、PD CEN/TS 16969:2016 Paints and varnishes Coating materials and coating systems for exterior wood Assessment of end grain sealing performance BSI Standards Publication WB11885_BSI_StandardCovs_2013_AW.indd 1 15/05/2013 15:06PD CEN/TS 16969:2016 PUBLISHED DOCUMENT National foreword This Published Doc

2、ument is the UK implementation of CEN/TS 16969:2016. The UK participation in its preparation was entrusted to Technical Committee STI/28, Paint systems for non-metallic substrates. A list of organizations represented on this committee can be obtained on request to its secretary. This publication doe

3、s not purport to include all the necessary provisions of a contract. Users are responsible for its correct application. The British Standards Institution 2016. Published by BSI Standards Limited 2016 ISBN 978 0 580 92697 6 ICS 87.040 Compliance with a British Standard cannot confer immunity from leg

4、al obligations. This Published Document was published under the authority of the Standards Policy and Strategy Committee on 31 August 2016. Amendments issued since publication Date Text affectedPD CEN/TS 16969:2016TECHNICAL SPECIFICATION SPCIFICATION TECHNIQUE TECHNISCHE SPEZIFIKATION CEN/TS 16969 J

5、uly 2016 ICS 87.040 English Version Paints and varnishes - Coating materials and coating systems for exterior wood - Assessment of end grain sealing performance Peintures et vernis - Produits de peinture et systmes de peinture pour bois en extrieur - valuation des performances du colmatage des bois

6、de bout Beschichtungsstoffe - Beschichtungsstoffe und Beschichtungssysteme fr Holz im Auenbereich - Beurteilung des Leistungsverhaltens von Hirnholzversielgelungen This Technical Specification (CEN/TS) was approved by CEN on 12 June 2016 for provisional application. The period of validity of this CE

7、N/TS is limited initially to three years. After two years the members of CEN will be requested to submit their comments, particularly on the question whether the CEN/TS can be converted into a European Standard. CEN members are required to announce the existence of this CEN/TS in the same way as for

8、 an EN and to make the CEN/TS available promptly at national level in an appropriate form. It is permissible to keep conflicting national standards in force (in parallel to the CEN/TS) until the final decision about the possible conversion of the CEN/TS into an EN is reached. CEN members are the nat

9、ional standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Sl

10、ovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2016 CEN All rights of exploitation in any form and by any me

11、ans reserved worldwide for CEN national Members. Ref. No. CEN/TS 16969:2016 EPD CEN/TS 16969:2016 CEN/TS 16969:2016 (E) 2 Contents Page European foreword . 3 1 Scope 4 2 Normative references 4 3 Terms and definitions . 4 4 Principle . 4 5 Sample preparation 5 5.1 Wood 5 5.2 Preparation of coated and

12、 uncoated samples 6 5.2.1 Wood conditioning . 6 5.2.2 Sample selection 6 5.2.3 Coating application . 6 5.2.4 Sealing and conditioning 6 6 Apparatus . 7 7 Procedure. 7 7.1 Pre-Conditioning . 7 7.2 Absorption cycle 7 7.3 Optional testing of weathered samples . 8 8 Calculation and expression of results

13、 8 9 Test report . 8 Bibliography 9 PD CEN/TS 16969:2016 CEN/TS 16969:2016 (E) 3 European foreword This document (CEN/TS 16969:2016) has been prepared by Technical Committee CEN/TC 139 “Paints and varnishes”, the secretariat of which is held by DIN. Attention is drawn to the possibility that some of

14、 the elements of this document may be the subject of patent rights. CEN shall not be held responsible for identifying any or all such patent rights. According to the CEN/CENELEC Internal Regulations, the national standards organisations of the following countries are bound to announce this Technical

15、 Specification: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Sl

16、ovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. PD CEN/TS 16969:2016 CEN/TS 16969:2016 (E) 4 1 Scope This Technical Specification specifies a test method to evaluate the ability of coating materials to seal the end grain of wood against ingress of water. This procedure is relevant

17、 for joinery or wood based cladding materials whose service life can depend on the control of water penetration through the coated end-grain. 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. Fo

18、r dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 927-5:2006, Paints and varnishes - Coating materials and coating systems for exterior wood - Part 5: Assessment of the liquid water permeab

19、ility EN ISO 4618, Paints and varnishes - Terms and definitions (ISO 4618) 3 Terms and definitions For the purposes of this document, the terms and definitions given in EN ISO 4618 and the following apply. 3.1 water absorption ability of a coated or uncoated wood sample to absorb water from liquid o

20、r vapour SOURCE: EN 927-5:2006, 3.1 3.2 water permeability ability of a coating system to allow the transmission of water as liquid or vapour SOURCE: EN 927-1:2013, 3.13 3.3 stable mass mass achieved when the difference between two subsequent weighings within 24 h does not exceed 0,2 % SOURCE: EN 92

21、7-5:2006, 3.3 3.4 end grain sealer system applied on the end grain 4 Principle Water permeability is assessed by measuring the water uptake over a 72 h period of coated test pieces exposed to liquid water. The coating under test is applied to the end grain surface of a defined test piece where the r

22、emaining sides are carefully sealed using a sealer of a defined mandatory low water PD CEN/TS 16969:2016 CEN/TS 16969:2016 (E) 5 permeability. Results are expressed as water absorption of coated wood samples in grams per square meter test surface per 72 h. 5 Sample preparation 5.1 Wood The wood shal

23、l be spruce (Picea abies) that has been selected to be free from knots and cracks, to be straight-grained and of normal growth rate (i.e. between 3 and 8 annual rings per 10 mm). The wood shall be free from blue stain and evidence of surface or bulk infection. Abnormal porosity (caused by bacterial

24、attack) shall be avoided. Abnormally porous wood can be detected qualitatively by the rapid absorption of a drop of propan-2-ol (isopropanol) applied to the surface; the drop should not be absorbed in less than 30 s by normal wood. The test should be carried out at not less than six places, widely s

25、eparated on the rear face of the test sample. The density of the wood shall be between 0,4 g/cm 3and 0,5 g/cm 3when measured at an equilibrium moisture content of approximately 12 %. The measured density shall be recorded. Condition the wood prior to conversion into test samples at (20 2) C and a re

26、lative humidity of (65 5) %. Convert the conditioned wood into samples (45 2) mm (45 2) mm (150 2) mm in size. The samples shall be planed all round to a smooth and uniform finish. The end grain shall be cut with a sharp circular saw to obtain a smooth surface without visible defects from cutting. A

27、ny samples showing surface splitting shall be rejected. The longitudinal edges shall be rounded with 3 mm radius. For illustration, see Figure 1. Key a = (150 2) mm b = (45 2) mm c = (45 2) mm Figure 1 Size of test samples PD CEN/TS 16969:2016 CEN/TS 16969:2016 (E) 6 5.2 Preparation of coated sample

28、s and sealed controls 5.2.1 Wood conditioning Prior to coating, condition the samples to constant mass at (20 2) C and a relative humidity of (65 5) %. Samples shall be weighed at intervals of not less than one day until they have reached a stable mass (see 3.3). 5.2.2 Sample selection Select five s

29、amples for each of the coatings to be tested. Select also five samples for testing the sealer product; this set of samples will serve as sealed controls. 5.2.3 Coating application Coating systems shall be applied according to the manufacturers specifications. Apply each test coating system to one en

30、d grain surface only. Record applied quantity of each coating layer by weighing the samples before and after coating application. 5.2.4 Sealing and conditioning Samples shall be sealed in the same way whether they are applied for test coatings or control of sealer. Seal all sides and the uncoated en

31、d-grain of the samples against water entry using at least two coats of a flexible moisture-impermeable coating, for example a solvent-free epoxy or polyurethane paint. The liquid water permeability of the sealer tested according to EN 927-5 shall not exceed 30 g/m 2in 72 h. The sealer shall cover th

32、e edges completely and overlap the test face by 2 mm (see Figure 2). Apply the sealer to the uncoated end grain so many times that a closed and uniform film is obtained. Key 1 coating application on one end grain 2 sealing of all sides and the opposite end grain d overlap of sealer on test face, d =

33、 2 mm Figure 2 Coating and sealing of the test samples PD CEN/TS 16969:2016 CEN/TS 16969:2016 (E) 7 6 Apparatus 6.1 Conditioning room, of appropriate size, controlled at a temperature of (20 2) C and a relative humidity of (65 5) %. 6.2 Container, for deionized water, of size sufficient to hold the

34、all the samples under test. 6.3 Balance, capable of weighing to the nearest 0,01 g. 7 Procedure 7.1 Pre-Conditioning After coating application, sealing and drying of coating materials the samples shall be stored in controlled environment (see 6.1) at (20 2) C and a relative humidity of (65 5) %, unt

35、il a stable mass is achieved. NOTE Usually 28 days is used as a suitable time period for drying and curing. 7.2 Absorption cycle Weigh the test samples to the nearest 0,01 g and record the initial mass (m 0). Fill the container (6.2) with deionized water and place it in the conditioning room (6.1).

36、The water shall have reached stable temperature in the conditioned room, i.e. (20 2) C. Immerse the test samples with the coated end grain surface under test down into the water ensuring that the whole of the test face is fully wetted. Use a sample holder and load the samples with weight to ensure t

37、hat the test surfaces are (10 3) mm under the water surface. After 72 h remove the test samples from the water, blot lightly to remove any water droplets and weigh. Record the elapsed time and mass (m 1). All handling of the samples shall be carried out in the conditioning room (6.1). An example for

38、 the test set up see Figure 3. Key 1 Samples with end grain sealer under test facing downwards 2 water 3 grid to ensure full wetting of test face Figure 3 Example for test set up PD CEN/TS 16969:2016 CEN/TS 16969:2016 (E) 8 7.3 Optional testing of weathered samples If required, end grain sealers may

39、 be subjected to a weathering test before or after measurement of liquid water permeability. 8 Calculation and expression of results At the end of the test, calculate the water uptake m 1 m 0, in grams for the five coated samples with the end grain sealer under test and the five sealed control sampl

40、es. Calculate the water absorption per square metre of test surface for the five coated samples with the end grain sealer under test and the five sealed control samples by dividing the water uptake by the nominal test area of each of the five test samples. From the five values for the water absorpti

41、on mean value and standard deviation shall be stated in the test report. 9 Test report The test report shall contain at least the following information: a) all details necessary to identify the product tested; b) a reference to this Technical Specification; c) the name and address of the testing lab

42、oratory; d) the identification number of the test report; e) the name and address of the organization or the person who ordered the test; f) the mean water absorption value and standard deviation for the coated and the sealed control samples, as indicated in Clause 8; g) the density of the wood used

43、 for the test samples; h) the applied amount of coating materials under test; i) any deviation from the test method specified; j) the authorization date of the test report. PD CEN/TS 16969:2016 CEN/TS 16969:2016 (E) 9 Bibliography EN 927-1:2013, Paints and varnishes - Coating materials and coating s

44、ystems for exterior wood - Part 1: Classification and selection This page deliberately left blankThis page deliberately left blankBSI is the national body responsible for preparing British Standards and other standards-related publications, information and services. BSI is incorporated by Royal Char

45、ter. British Standards and other standardization products are published by BSI Standards Limited. British Standards Institution (BSI) About us We bring together business, industry, government, consumers, innovators and others to shape their combined experience and expertise into standards -based sol

46、utions. The knowledge embodied in our standards has been carefully assembled in a dependable format and refined through our open consultation process. Organizations of all sizes and across all sectors choose standards to help them achieve their goals. Information on standards We can provide you with

47、 the knowledge that your organization needs to succeed. Find out more about British Standards by visiting our website at or contacting our Customer Services team or Knowledge Centre. Buying standards You can buy and download PDF versions of BSI publications, including British and adopted European a

48、nd international standards, through our website at where hard copies can also be purchased. If you need international and foreign standards from other Standards Development Organizations, hard copies can be ordered from our Customer Services team. Copyright in BSI publications All the content in BS

49、I publications, including British Standards, is the property of and copyrighted by BSI or some person or entity that owns copyright in the information used (such as the international standardization bodies) and has formally licensed such information to BSI for commercial publication and use. Save for the provisions below, you may not transfer, share or disseminate any portion of the standard to any other person. You may not adapt, distribute, commercially exploit, or publicly displ