SAE AMS 6387B-2013 Steel Carbon Laminated Sheet Surface Bonded《表面结合层压板碳素钢》.pdf

《SAE AMS 6387B-2013 Steel Carbon Laminated Sheet Surface Bonded《表面结合层压板碳素钢》.pdf》由会员分享，可在线阅读，更多相关《SAE AMS 6387B-2013 Steel Carbon Laminated Sheet Surface Bonded《表面结合层压板碳素钢》.pdf（7页珍藏版）》请在麦多课文档分享上搜索。

1、_SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising theref

2、rom, is the sole responsibility of the user.”SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions.Copyright 2012 SAE InternationalAll rights reserved. No part of this publication may b

3、e reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE.TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada)Tel: +1 724-776-4970 (outside USA)Fax

4、: 724-776-0790Email: CustomerServicesae.orgSAE WEB ADDRESS: http:/www.sae.orgSAE values your input. To provide feedbackon this Technical Report, please visithttp:/www.sae.org/technical/standards/AMS6387BAEROSPACEMATERIALSPECIFICATIONAMS6387 REV. BIssued 2003-04Revised 2013-02Superseding AMS6387AStee

5、l, Carbon, Laminated Sheet, Surface BondedRATIONALEAMS6387B results from a Five Year Review and update of this document.1. SCOPE1.1 FormThis specification covers steel in the form of laminated sheet.1.2 ApplicationThis material has been used typically for shims in which thickness is adjusted by remo

6、val of laminations as required, but usage is not limited to such applications.1.3 ClassificationMaterials are classified as follows:1.3.1 TypeType I - All laminationsType II - One half laminationsType III - Three quarters laminations1.3.2 ClassClass 1 - 0.002 inch (0.05 mm) thick laminationsClass 2

7、- 0.003 inch (0.075 mm) thick laminationsSAE AMS6387B Page 2 of 72. APPLICABLE DOCUMENTSThe issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unl

8、ess a specific document issue is specified. When the referenced document has been cancelled and no superseding document has been specified, the last published issue of that document shall apply.2.1 SAE PublicationsAvailable from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, T

9、el: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA), www.sae.org.AMS5040 Steel, Sheet and Strip, 0.15 Carbon, Maximum, Deep Forming GradeAMS5042 Steel, Sheet and Strip, 0.15 Carbon, Maximum GradeAMS5044 Steel, Sheet and Strip, 0.15 Carbon, Maximum, Half Hard TemperAMS5047 Steel, S

10、heet and Strip, 0.08 - 0.13C, Aluminum Killed (SAE 1010), Deep Forming Grade2.2 American Society for Quality PublicationsAvailable from American Society for Quality, 600 North Plankinton Avenue, Milwaukee, WI 53203, Tel: 800-248-1946(United States or Canada) or +1-414-272-8575 (International), www.a

11、sq.org.ANSI/ASQC Z1.4 Sampling Procedures and Tables for Inspection by Attributes3. TECHNICAL REQUIREMENTS3.1 Composition3.1.1 LaminationsShall conform to AMS5040, AMS5042, AMS5044 or AMS5047.3.1.2 AdhesiveShall be of a composition that will meet the fabrication and quality requirements of this spec

12、ification.3.2 FabricationThe laminated shim stock shall consist completely of laminations each 0.002 inch 0.0002 (0.05 mm 0.005) thick or 0.003 inch 0.0003 (0.08 mm 0.008) thick, or partly of such laminations combined with a single thicker lamination, as ordered, bonded together by an adhesive such

13、that individual laminations may be peeled for adjustment of shim thickness. The thickness of each layer of adhesive shall not exceed 0.0003 inch (0.008 mm).3.2.1 Sheet shall be of the thicknesses and combinations of laminations and solid base shown in Table 1.SAE AMS6387B Page 3 of 7TABLE 1 - THICKN

14、ESS COMBINATIONS OF SHIM STOCKInch mmType IClass 1AllLaminated,0.002 in.(0.05 mm)LaminationsType IClass 2AllLaminated,0.003 in.(0.08 mm)LaminationsType IIClass 1HalfSolid,HalfLaminated,0.002 in.(0.05 mm)LaminationsType IIClass 2HalfSolid,HalfLaminated,0.003 in.(0.08 mm)LaminationsType IIIClass 1Thre

15、eQuartersSolid,OneQuarterLaminated,0.002 in.(0.05 mm)LaminationsType IIIClass 1ThreeQuartersSolid,OneQuarterLaminated,0.003 in.(0.08 mm)Laminations0.006 0.15 X0.008 0.20 X0.010 0.25 X0.012 0.31 X0.015 0.38 X X0.016 0.41 X X0.020 0.51 X X0.021 0.53 X X0.032 0.81 X X0.033 0.84 X X0.047 1.19 X X0.048 1

16、.22 X X0.062 1.58 X X X X0.063 1.60 X X X X0.078 1.98 X X X X0.080 2.03 X X X X0.093 2.37 X X X X0.094 2.39 X X X X0.109 2.77 X X X X0.121 3.07 X X X X X X0.125 3.18 X X X X X X3.2.2 Legacy Part NumbersLegacy part numbers of the form M22499/4 plus dash number shall meet the following Type, Class and

17、 dimensions specified in Table 2. Tolerance of Length and Width shall be plus and minus 0.125 inch. In the event of any conflict between the requirements of Table 1 and Table 2, the requirements of Table 2 shall govern.SAE AMS6387B Page 4 of 7TABLE 2 - REQUIREMENTS FOR LEGACY PART NUMBERSDash NoAThi

18、cknessBWidthLengthFeet Type Class001 0.010 8.000 4.000 I 1003 0.016 6.000 3.000 I 1005 0.024 8.000 2.000 I 1007 0.032 6.000 3.000 I 1009 0.062 6.000 3.000 I 13.3 Construction3.3.1 General RequirementsLaminations and solid stock, when applicable, shall be bonded together throughout the whole surface

19、area in a manner that will permit peeling of the laminations without the aid of mechanical devices, for adjustment of shim thickness, without separation of the remaining laminations and solid part. Laminations shall be bonded together in such a manner that any shape can be cut from the material usin

20、g suitable tools, without separation. Laminations shall remain intact without separation during normal handling. Requirements shall be applicable to laminations not less than eight hours after completion of bonding.3.3.2 Surface RoughnessFlat surfaces of laminations, and solid stock when applicable,

21、 shall have a maximum roughness of 63 RA (microinches) on original surfaces and on metallic surfaces after peeling.3.3.3 Water ResistanceSheet shall withstand total immersion in water at 120 F 3 (49 C 2) for at least three hours without separation of laminations or any evidence of corrosion.3.3.4 Pe

22、el StrengthEach individual lamination shall have a peel strength no less than 1 pound per inch of width (180 gm/cm of width) and no more than 5 pounds per inch of width (900 gm/cm of width), except at the solid/laminate bond line that may be higher.3.3.5 The existence of the applicable type, class a

23、nd nominal thickness shown in Table 1 is not intended to imply that all products described are commercially available. Only the products described in Table 2 have specific identification part numbers assigned to them.3.4 QualitySheet, as received by purchaser, shall be uniform in quality and conditi

24、on, sound, and free from foreign materials and from dents, creases, and other imperfections detrimental to usage of the sheet.3.5 Thickness TolerancesShall be as specified in Table 3.SAE AMS6387B Page 5 of 7TABLE 3A - TOTAL THICKNESS TOLERANCES, INCH/POUND UNITSNominal ThicknessInchesTolerance, Inch

25、PlusTolerance, InchMinusUp to 0.008, incl 0.001 0.0005Over 0.008 to 0.010, incl 0.0015 0.0005Over 0.010 to 0.016, incl 0.0015 0.001Over 0.016 to 0.021, incl 0.002 0.001Over 0.021 to 0.033, incl 0.003 0.002Over 0.033 to 0.048, incl 0.005 0.002Over 0.048 to 0.063, incl 0.006 0.002Over 0.063 to 0.080,

26、incl 0.007 0.002Over 0.080 to 0.094, incl 0.009 0.003Over 0.094 to 0.109, incl 0.010 0.003Over 0.109 to 0.125, incl 0.012 0.003Over 0.125 to 0.156, incl 0.015 0.003Over 0.156 to 0.187, incl 0.018 0.003Over 0.187 to 0.190, incl 0.018 0.005TABLE 3B - TOTAL THICKNESS TOLERANCES, SI UNITSNominal Thickne

27、ssMillimetersTolerance, MillimeterPlusTolerance, MillimeterMinusUp to 0.20, incl 0.025 0.013Over 0.20 to 0.25, incl 0.038 0.013Over 0.25 to 0.41, incl 0.038 0.025Over 0.41 to 0.53, incl 0.05 0.025Over 0.53 to 0.84, incl 0.08 0.05Over 0.84 to 1.22, incl 0.13 0.05Over 1.22 to 1.60, incl 0.15 0.05Over

28、1.60 to 2.03, incl 0.18 0.05Over 2.03 to 2.39, incl 0.23 0.08Over 2.39 to 2.77, incl 0.25 0.08Over 2.77 to 3.18, incl 0.30 0.08Over 3.18 to 3.96, incl 0.38 0.08Over 3.96 to 4.75, incl 0.46 0.08Over 4.75 to 4.83, incl 0.46 0.133.6 QualityThe shim stock shall be uniform in quality, clean, and free of

29、defects detrimental to functional performance of the material.4. QUALITY ASSURANCE PROVISIONS4.1 Responsibility for InspectionThe vendor of sheet shall supply all samples for vendors tests and shall be responsible for the performance of all required tests. Purchaser reserves the right to sample and

30、to perform any confirmatory testing deemed necessary to ensure that the sheet conforms to specified requirements.4.2 Classification of TestsAll technical requirements are acceptance tests and shall be performed on each heat or lot as applicable.SAE AMS6387B Page 6 of 74.3 Sampling and TestingA lot s

31、hall consist of all of the shim stock of the same composition, type, class, nominal size and lateral dimensions, manufactured under essentially the same conditions, and submitted for acceptance at the same time. Sampling shall be in accordance with ANSI/ASQC Z1.4. Lot acceptance criteria shall be ba

32、sed on a single sampling plan with a zero acceptance number.4.4 ReportsThe vendor of sheet shall furnish with each shipment a report showing the results of tests for peel strength of each lot and stating that the sheet conforms to the other technical requirements. This report shall include the purch

33、ase order number, lot number, AMS6387A, type, class, dash number or length and width as applicable, and quantity.4.5 Resampling and RetestingShall be in accordance with ANSI/ASQC Z1.4.5. PREPARATION FOR DELIVERY5.1 IdentificationEach sheet shall be legibly marked on one face with nominal shim stock

34、thickness, thickness of each lamination, percentage of total thickness that is laminated, and AMS6387B.5.2 PackagingSheet shall be prepared for shipment in accordance with commercial practice and in compliance with applicable rules and regulations pertaining to the handling, packaging, and transport

35、ation of the sheet to ensure carrier acceptance and safe delivery.6. ACKNOWLEDGEMENTA vendor shall include this specification number and its revision letter in all quotations and when acknowledging purchase orders.7. REJECTIONSSheet not conforming to this specification, or to modifications authorize

36、d by purchaser, will be subject to rejection.8. NOTES8.1 A change bar (|) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the previous issue of this document. An (R) symbol to the left of the document

37、 title indicates a complete revision of the document, including technical revision. Change bars and (R) are not used in original publications, nor in documents that contain editorial changes only.8.2 Terms used in AMS are clarified in ARP1917.8.3 Dimensions and properties in inch/pound units and the

38、 Fahrenheit temperatures are primary; dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equivalents of the primary units and are presented only for information.SAE AMS6387B Page 7 of 78.4 Purchase documents should specify not less than the following:AMS6387BType, class, and dash number or dimensions as applicableQuantity of sheet desired.PREPARED BY AMS COMMITTEE “E“