SAE AMS 4860F-2009 Manganese Bronze Sand and Centrifugal Castings 58Cu C 39Zn C 1 2Fe C 1 0Al C 0 80Mn As Cast (UNS C86500)《58Cu-39Zn-1 2Fe-1 0Al-0 80Mn铸造的锰青铜 砂和离心铸件》.pdf

《SAE AMS 4860F-2009 Manganese Bronze Sand and Centrifugal Castings 58Cu C 39Zn C 1 2Fe C 1 0Al C 0 80Mn As Cast (UNS C86500)《58Cu-39Zn-1 2Fe-1 0Al-0 80Mn铸造的锰青铜 砂和离心铸件》.pdf》由会员分享，可在线阅读，更多相关《SAE AMS 4860F-2009 Manganese Bronze Sand and Centrifugal Castings 58Cu C 39Zn C 1 2Fe C 1 0Al C 0 80Mn As Cast (UNS C86500)《58Cu-39Zn-1 2Fe-1 0Al-0 80Mn铸造的锰青铜 砂和离心铸件》.pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and suggestions. Copyright 2015 SAE International All rights reserved. No part of this p

3、ublication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-497

4、0 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS4860F AEROSPACE MATERIAL SPECIFICATION AMS4860 REV. F Issued 1939-12 Revised 2

5、009-07 Reaffirmed 2015-09 Superseding AMS4860E Manganese Bronze, Sand and Centrifugal Castings 58Cu 39Zn 1.2Fe 1.0Al 0.80Mn As Cast (Composition similar to UNS C86500) RATIONALE AMS4860F has been reaffirmed to comply with the SAE five-year review policy. 1. SCOPE 1.1 Form This specification covers a

6、 manganese bronze alloy in the form of sand and centrifugal castings. 1.2 Application These castings have been used typically for parts requiring strength, toughness, and corrosion resistance, but usage is not limited to such applications. 2. APPLICABLE DOCUMENTS The issue of the following documents

7、 in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced document has been cancelled and no superseding document has

8、been specified, the last published issue of that document shall apply. 2.1 SAE Publications Available from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA), www.sae.org. AMS2694 In-Process Welding of Casting

9、s AMS2804 Identification, Castings 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org. ASTM B 208 Preparing Tension Test Specimens for Copper-Base Alloys for Sand, Permanent Mold, Centrifuga

10、l, and Continuous Castings ASTM E 8/E 8M Tension Testing of Metallic Materials ASTM E 478 Chemical Analysis of Copper Alloys ASTM E 1417 Liquid Penetrant Testing ASTM E 1742 Radiographic Examination 3. TECHNICAL REQUIREMENTS 3.1 Composition Shall conform to the percentages by weight shown in Table 1

11、, determined by wet chemical methods in accordance with ASTM E 478, by spectrochemical methods, or by other analytical methods acceptable to purchaser. TABLE 1 - COMPOSITION Element (3.1.1) min max Copper (3.1.4) 55.0 60.0 Zinc (3.1.2) 36.0 42.0 Iron 0.40 2.0 Aluminum 0.50 1.5 Manganese 0.10 1.5 Tin

12、 - 1.0 Nickel (plus Cobalt) - 1.0 Lead - 0.40 Sum of Named Elements (3.1.3) 99.0 - 3.1.1 These composition limits do not preclude the presence of other elements. Limits may be established and analysis required for unnamed elements by agreement between the manufacturer or supplier and purchaser. 3.1.

13、2 Zinc may be reported as “remainder”, or as the difference between the sum of results for all elements and 100%, or as the result of direct analysis. 3.1.3 When all the elements in Table 1 are analyzed, the sum shall be 99.0% minimum, but such determination is not required for routine acceptance of

14、 each lot. 3.1.4 In determining copper minimum, copper may be calculated as copper plus nickel. 3.2 Condition As cast. MO1(as sand cast) or MO2(as centrifugally cast) (See 8.2). 3.3 Casting Castings shall be produced in lots from metal conforming to 3.1. 3.3.1 A lot shall be all castings produced fr

15、om one furnace melt or crucible melt. When two or more furnace melts or crucible melts or combination thereof are used to charge a ladle for pouring, the castings therefrom shall constitute a lot. A lot shall be not more than 1000 pounds (454 kg) of castings. SAE INTERNATIONAL AMS4860F Page 2 of 6_

16、3.4 Test Specimens Chemical analysis specimens and tensile coupons shall be cast as follows: 3.4.1 Chemical Analysis Specimens Shall be cast from each melt and be of any convenient size, shape, and form. 3.4.2 Tensile Coupons Shall be cast with each lot of castings and in accordance with 3.4.2.1 and

17、 3.4.2.2. Metal for the coupons shall be part of the melt which is used for the castings. If the metal for castings is given any treatment, such as fluxing or cooling and reheating, the metal for the coupons shall be a portion of the metal so treated and, during such treatment, shall be heated to th

18、e same maximum temperature and held for approximately the same time as the molten metal for the castings. The temperature of the metal during pouring of the coupons shall be not lower than that during pouring of the castings. 3.4.2.1 Sand Cast Coupons from which specimens are machined shall be stand

19、ard keel blocks conforming to ASTM B 208 cast in molds made with the regular foundry mix of sand without using chills or baked sand core molds. Coupons shall be machined to standard tensile specimens conforming to ASTM E 8/E 8M with 0.500 inch (12.70 mm) diameter at the reduced parallel gage section

20、. 3.4.2.2 Centrifugally Cast Coupons from which specimens are machined shall be cylindrical bars of such size to allow machining of standard tensile specimens conforming to ASTM E 8/E 8M with 0.500 inch (12.70 mm) diameter at the reduced parallel gage section. 3.5 Properties Castings and representat

21、ive tensile specimens produced in accordance with 3.4.2 shall conform to the following requirements: 3.5.1 Tensile Properties Separately-cast specimens or specimens as in 4.3.4 cut from any area of a casting shall meet the requirements shown in Table 2, determined in accordance with ASTM E 8/E 8M. T

22、ABLE 2 - MINIMUM TENSILE PROPERTIES Property Value Tensile Strength Yield Strength at 0.2% Offset Elongation in 4D 65.0 ksi (448 MPa) 25.0 ksi (172 MPa) 20% 3.5.1.1 Tensile properties of separately-cast specimens shall be used for acceptance of castings except when purchaser specifies that tensile p

23、roperties of specimens cut from any area of a castings apply. 3.6 Quality 3.6.1 Castings, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from imperfections detrimental to usage of the castings. 3.6.1.1 Castings shall have smooth surfac

24、es and shall be cleaned sufficiently to permit nondestructive testing. SAE INTERNATIONAL AMS4860F Page 3 of 6_ 3.6.2 Castings shall be produced under radiographic control. This control shall consist of radiographic examination of castings in accordance with ASTM E 1742 until proper foundry technique

25、, which will produce castings free from harmful internal imperfections, is established for each part number and of production castings as necessary to ensure maintenance of satisfactory quality. 3.6.3 When specified, castings shall be subjected to fluorescent penetrant testing in accordance with AST

26、M E 1417. 3.6.4 Radiographic, fluorescent penetrant, and other quality acceptance standards may be agreed upon by purchaser and vendor. 3.6.5 Castings shall not be repaired by peening, plugging, welding, or other methods without written permission from purchaser. 3.6.5.1 When permitted in writing by

27、 purchaser, defects in castings may be removed and the castings reworked by welding in accordance with AMS2694. 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for Inspection The vendor of castings shall supply all samples for vendors tests and shall be responsible for the performance of all requ

28、ired tests. Purchaser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the castings conform to the specified requirements. 4.2 Classification of Tests 4.2.1 Acceptance Tests Except as specified in 4.2.1.1, composition (3.1), tensile properties (3.5

29、.1), and quality (3.6) are acceptance tests and shall be performed to represent each melt or lot as applicable. 4.2.1.1 Tensile properties of specimens cut from castings shall be determined only when specified by purchaser or when separately-cast coupons are not available. Tensile properties of sepa

30、rately-cast coupons need not be determined when tensile properties of specimens cut from castings are determined. 4.2.2 Preproduction Tests All technical requirements are preproduction tests and shall be performed prior to or on the first-article shipment of a casting to a purchaser, when a change i

31、n material and/ or processing requires reapproval as in 4.4.2, and when purchaser deems confirmatory testing to be required. 4.3 Sampling and Testing Shall be in accordance with the following: 4.3.1 One chemical analysis specimen in accordance with 3.4.1 from each melt or a casting from each lot. 4.

32、3.2 Two separately-cast tensile specimens in accordance with 3.4.2 from each lot except when properties of specimens cut from castings are required. 4.3.3 Sufficient castings of each part number in accordance with 4.4.1 as required to satisfy dimensional, mechanical property, and quality evaluation.

33、 SAE INTERNATIONAL AMS4860F Page 4 of 6_ 4.3.4 One or more castings from each lot when properties of specimens machined from castings are required. Specimens shall conform to ASTM E 8/E 8M and shall be either 0.500 inch (12.70 mm) in diameter at the reduced parallel gage section, subsize specimens p

34、roportional to the standard, or standard sheet-type specimens. For determining conformance to the requirements of 3.5.1, if specimen locations are not shown on the drawing, not less than two tensile specimens, one from the thickest section and one from the thinnest section, shall be cut from a casti

35、ng or castings from each lot. 4.4 Approval 4.4.1 Sample castings from new or reworked master patterns or molds and the casting procedure shall be approved by purchaser before castings for production use are supplied, unless such approval is waived by purchaser. 4.4.2 Vendor shall establish, for prod

36、uction of sample castings of each part number, parameters for the process control factors which will produce acceptable castings; these shall constitute the approved casting procedure and shall be used for producing production castings. If necessary to make any change in parameters for the process c

37、ontrol factors, vendor shall submit for reapproval a statement of the proposed changes in processing and, when requested, test specimens, sample castings, or both. Production castings incorporating the revised operations shall not be shipped prior to receipt of reapproval. 4.4.2.1 Control factors fo

38、r producing castings include, but are not limited to, the following: Type of furnace Furnace atmosphere Fluxing or deoxidation procedure Gating and risering practices Metal pouring temperature; variation of 50 F (28 C) is permissible Mold set-up, parting agent, and rotational speed for centrifugal c

39、astings Solidification and cooling procedures Cleaning operations Methods of inspection. 4.4.2.1.1 Any of the above process control factors for which parameters are considered proprietary by the vendor may be assigned a code designation. Each variation in such parameters shall be assigned a modified

40、 code designation. 4.5 Reports 4.5.1 The vendor of castings shall furnish with each shipment a report showing the results of tests for chemical composition of at least one casting or of separately-cast specimens from each melt and the results of tests for tensile properties of separately-cast coupon

41、s representing each lot or of specimens cut from castings from each lot and stating that the castings conform to the other technical requirements. This report shall include the purchase order number, lot number, AMS4860F, part number, and quantity. 4.6 Resampling and Retesting If any specimen used i

42、n the above tests fails to meet the specified requirements, disposition of the castings may be based on the results of testing two additional specimens. Failure of any retest specimen to meet the specified requirements shall be cause for rejection of the castings represented. Results of all tests sh

43、all be reported. 5. PREPARATION FOR DELIVERY 5.1 Identification Shall be in accordance with AMS2804. SAE INTERNATIONAL AMS4860F Page 5 of 6_ 5.2 Packaging Castings shall be prepared for shipment in accordance with commercial practice and in compliance with applicable rules and regulations pertaining

44、 to the handling, packaging, and transportation of the castings to ensure carrier acceptance and safe delivery. 6. ACKNOWLEDGMENT A vendor shall mention this specification number and its revision letter in all quotations and when acknowledging purchase orders. 7. REJECTIONS Castings not conforming t

45、o this specification, or to modifications authorized by purchaser, will be subject to rejection. 8. NOTES 8.1 A change bar (l) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the previous issue of thi

46、s document. An (R) symbol to the left of the document title indicates a complete revision of the document, including technical revisions. Change bars and (R) are not used in original publications, nor in documents that contain editorial changes only. 8.2 Copper temper designations are defined in AST

47、M B 601. 8.2.1 Terms used in AMS are clarified in ARP1917. 8.3 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary: dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equivalents of the primary units and are presented

48、 only for information. 8.4 Purchase documents should specify not less than the following: AMS4860F Type and part number or pattern number of castings desired Quantity of castings desired Type, location, and number of specimens for tensile testing when properties of specimens cut from castings are required (See 4.3.4) Nondestruct