SAE AMS 4219F-2010 Aluminum Alloy Castings 7 0Si - 0 55Mg - 0 12Ti - 0 06Be (A357 0 T6) Solution and Precipitation Heat Treated (UNS A13570)《7 0Si 0 55Mg 0 12Ti 0 06Be (A357 0 T6)溶.pdf

《SAE AMS 4219F-2010 Aluminum Alloy Castings 7 0Si - 0 55Mg - 0 12Ti - 0 06Be (A357 0 T6) Solution and Precipitation Heat Treated (UNS A13570)《7 0Si 0 55Mg 0 12Ti 0 06Be (A357 0 T6)溶.pdf》由会员分享，可在线阅读，更多相关《SAE AMS 4219F-2010 Aluminum Alloy Castings 7 0Si - 0 55Mg - 0 12Ti - 0 06Be (A357 0 T6) Solution and Precipitation Heat Treated (UNS A13570)《7 0Si 0 55Mg 0 12Ti 0 06Be (A357 0 T6)溶.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and suggestions. Copyright 2015 SAE International All rights reserved. No part of this p

3、ublication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-497

4、0 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS4219F AEROSPACE MATERIAL SPECIFICATION AMS4219 REV. F Issued 1966-03 Revised 2

5、010-01 Reaffirmed 2015-10 Superseding AMS4219E Aluminum Alloy Castings 7.0Si - 0.55Mg - 0.12Ti - 0.06Be (A357.0 T6) Solution and Precipitation Heat Treated (Composition similar to UNS A13570) RATIONALE AMS4219F has been reaffirmed to comply with the SAE five-year review policy. 1. SCOPE 1.1 Form Thi

6、s specification covers an aluminum alloy in the form of castings. 1.2 Application These castings have been used typically for structural components requiring high strength, but usage is not limited to such applications. 1.3 Safety - Hazardous Materials While the materials, methods, applications, and

7、 processes described or referenced in this specification may involve the use of hazardous materials, this specification does not address the hazards which may be involved in such use. It is the sole responsibility of the user to ensure familiarity with the safe and proper use of any hazardous materi

8、als and to take necessary precautionary measures to ensure the health and safety of all personnel involved (See 8.2). 2. APPLICABLE DOCUMENTS The issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The suppli

9、er may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced document has been cancelled and no superseding document has been specified, the last published issue of that document shall apply. 2.1 SAE Publications Available from SAE Internation

10、al, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA), www.sae.org. AMS2360 Room Temperature Tensile Properties of Castings AMS2694 In-Process Welding of Castings AMS2771 Heat Treatment of Aluminum Alloy Castings AMS2804 Identi

11、fication, Castings AMS2175 Casting, Classification and Inspection of 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org. ASTM B 557 Tension Testing Wrought and Cast Aluminum- and Magnesium-

12、Alloy Products ASTM B 557M Tension Testing Wrought and Cast Aluminum- and Magnesium- Alloy Products (Metric) ASTM E 29 Using Significant Digits in Test Data to Determine Conformance with Specifications ASTM E 34 Chemical Analysis of Aluminum and Aluminum Alloys ASTM E 155 Reference Radiographs for I

13、nspection of Aluminum and Magnesium Castings ASTM E 607 Atomic Emission Spectrometric Analysis of Aluminum and Aluminum Alloys by the Point-to-Plane Technique, Nitrogen Atmosphere ASTM E 716 Sampling Aluminum and Aluminum Alloys for Spectrochemical Analysis ASTM E 1251 Analysis of Aluminum and Alumi

14、num Alloys by Atomic Emission Spectrometry ASTM E 1417 Liquid Penetrant Testing ASTM E 1742 Radiographic Examination 3. TECHNICAL REQUIREMENTS 3.1 Composition Shall conform to the percentages by weight shown in Table 1, determined by wet chemical methods in accordance with ASTM E 34, by spectrochemi

15、cal methods in accordance with ASTM E 607, ASTM E 1251, or by other analytical methods acceptable to purchaser (See 3.4.1). TABLE 1 - COMPOSITION Element min max Silicon 6.5 7.5 Iron - 0.20 Copper - 0.20 Manganese - 0.10 Magnesium 0.40 0.7 Zinc - 0.10 Titanium 0.04 0.20 Beryllium 0.04 0.07 Other Ele

16、ments, each - 0.05 Other Elements, total - 0.15 Aluminum remainder 3.1.1 Test results may be rounded by the “rounding off” method of ASTM E 29. 3.2 Condition Solution and precipitation heat treated. SAE INTERNATIONAL AMS4219 F Page 2 of 8_ 3.3 Castings Castings shall be produced from metal conformin

17、g to 3.1, determined by analysis of a specimen (3.4.1) cast after the last melt addition. 3.4 Cast Test Specimens Chemical analysis specimens and tensile specimens shall be cast as follows: 3.4.1 Chemical Analysis Specimens Shall be cast from each melt after the last melt addition and shall be teste

18、d to qualify the melt as in 3.1. Spectrochemical sample shall be prepared in accordance with ASTM E 716. 3.4.2 Tensile Specimens Shall be produced as follows: 3.4.2.1 Specimens Cut from a Casting and Specimens from Integrally Cast Coupons Shall be removed after heat treatment, shall conform to ASTM

19、B 557 or ASTM B 557M and shall be either 0.500 inch (12.70 mm) diameter at the reduced parallel gage section, standard sheet type specimens, or subsize specimens proportional to the standard as required by 3.6.1. 3.4.2.2 Separately Cast Specimens Shall conform to ASTM B 557 or ASTM B 557M and shall

20、be cast from each melt after the last melt additions. Specimens shall be cast in molds representing the mold used for castings. Chills are not permitted on test specimen cavity, except on the end face of the specimen when approved in accordance with 4.4.2. 3.5 Heat Treatment Heat treat to the T6 tem

21、per in accordance with AMS2771. 3.6 Properties Castings and representative tensile specimens produced in accordance with 3.4.2 shall conform to the following requirements: 3.6.1 Tensile Properties Shall be as follows, determined in accordance with ASTM B 557 or ASTM B 557M; conformance to the requir

22、ements of 3.6.1.1 shall be used as basis for acceptance of castings except when purchaser specifies that the requirements of 3.6.1.2 or 3.6.1.3 apply. SAE INTERNATIONAL AMS4219 F Page 3 of 8_ 3.6.1.1 Specimens Cut From Castings Specimens as in 4.3.3 shall have the properties shown in Table 2. TABLE

23、2 - MINIMUM TENSILE PROPERTIES Property Value Tensile Strength 38.0 ksi (262 MPa) Yield Strength at 0.2% Offset 30.0 ksi (207 MPa) Elongation in 4D 2% 3.6.1.1.1 When properties other than those of Table 2 are required, tensile specimens as in 4.3.3 machined from locations indicated on the drawing, f

24、rom a casting or castings chosen at random to represent the lot, shall have the properties indicated on the drawing for such specimens. Property requirements may be designated in accordance with AMS2360. 3.6.1.2 Integrally Cast Specimens Specimens as in 4.3.3.1 shall have the properties shown in Tab

25、le 3. TABLE 3 - MINIMUM TENSILE PROPERTIES Property Value Tensile Strength 41.0 ksi (283 MPa) Yield Strength at 0.2% Offset 32.0 ksi (221 MPa) Elongation in 4D 3.0% 3.6.1.3 Separately Cast Specimens Specimens as in 4.3.3.2 shall have the properties shown in Table 3. 3.7 Quality Castings, as received

26、 by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from imperfections detrimental to usage of the castings. 3.7.1 When acceptance standards are not specified, Grade C of AMS2175 shall apply. 3.7.2 Methods of inspection and frequency of inspection sha

27、ll be as agreed upon by purchaser and vendor. A “Casting Class” of AMS2175 may be selected to specify the method and frequency of inspection. 3.7.3 Castings shall be produced under radiographic control. This control shall consist of 100% radiographic inspection of castings until process control fact

28、ors (4.4.2) have been established to ensure production of acceptable castings. Unless otherwise specified by purchaser, continued radiographic inspection of production castings shall be performed at a frequency determined by the vendor to ensure continued maintenance of internal quality. 3.7.3.1 Rad

29、iographic inspection shall be conducted in accordance with ASTM E 1742, unless otherwise specified by purchaser. 3.7.4 When specified by purchaser, castings shall be fluorescent penetrant inspected using a method specified by purchaser, or, if not specified, a method in accordance with ASTM E 1417.

30、3.7.5 Castings shall not be peened, plugged, impregnated, or welded unless authorized by purchaser. 3.7.5.1 When authorized by purchaser, welding in accordance with AMS2694 or other welding program approved by purchaser may be used. SAE INTERNATIONAL AMS4219 F Page 4 of 8_ 4. QUALITY ASSURANCE PROVI

31、SIONS 4.1 Responsibility for Inspection The vendor of castings shall supply all samples for vendors tests and shall be responsible for the performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the castings co

32、nform to specified requirements. 4.2 Classification of Tests 4.2.1 Acceptance Tests Except as specified in 4.2.1.1, composition (3.1), tensile properties of specimens cut from castings (3.6.1.1) or, when specified, from integrally cast coupons (3.6.1.2) or separately cast specimens (3.6.1.3), and qu

33、ality (3.7) are acceptance tests and shall be performed to represent each melt or heat treat lot as applicable. 4.2.1.1 Tensile properties of separately cast specimens or integrally cast coupons shall be determined when specified by purchaser or when specimens cut from castings cannot be obtained. T

34、ensile properties of separately cast specimens or from integrally cast coupons need not be determined when tensile properties of specimens cut from castings are determined. 4.2.2 Periodic Tests Radiographic inspection (3.7.3) following the establishment of process control (4.4.2) is a periodic test

35、and shall be performed at a frequency selected by the vendor unless frequency of testing is specified by purchaser. 4.2.3 Preproduction Tests All technical requirements are preproduction tests and shall be performed on the first-article shipment of a casting to a purchaser, when a change in material

36、 and/or processing requires reapproval as in 4.4.2, and when purchaser deems confirmatory testing to be required. 4.3 Sampling and Testing Shall be in accordance with the following: 4.3.1 One chemical analysis specimen in accordance with 3.4.1 from each melt for conformance to 3.1. 4.3.2 One or more

37、 preproduction castings in accordance with 4.4.1 of each part number. 4.3.3 Not less than two tensile specimens machined from a casting or castings from each heat treat lot except when purchaser specifies use of separately cast specimens as in 4.3.3 or integrally cast coupons as in 4.3.3.1. If the n

38、umber and locations of specimens are not shown on the drawing, not less than two specimens, one from the thickest section and one from the thinnest section, shall be cut from a casting or castings from each heat treat lot. 4.3.3.1 When permitted by purchaser, test bars integrally cast with the casti

39、ngs may be tested in lieu of testing specimens cut from castings. Size, number, and location of integrally cast coupons shall be as specified on the casting drawing or as agreed upon by purchaser and vendor. 4.3.3.2 One separately cast tensile specimen in accordance with 3.4.2 representing each heat

40、 treat lot, except when properties of specimens machined from castings or from integrally cast coupons are required. SAE INTERNATIONAL AMS4219 F Page 5 of 8_ 4.4 Approval 4.4.1 Sample castings from new or reworked patterns or molds and the casting procedure shall be approved by purchaser before cast

41、ings for production use are supplied, unless such approval be waived by purchaser. 4.4.2 Vendor shall establish, for production of sample castings of each part number, parameters for the process control factors which will produce acceptable castings; these shall constitute the approved casting proce

42、dure and shall be used for producing production castings. Vendor shall also establish control factors for producing separately cast tensile specimens, but these control factors need not be identical to those used for production of castings. If necessary to make any change in parameters for the proce

43、ss control factors, vendor shall submit for reapproval a statement of the proposed changes in processing and, when requested, sample castings, test specimens, or both. Production castings incorporating the revised operations shall not be shipped prior to receipt of reapproval. 4.4.2.1 Control factor

44、s for producing castings and separately cast tensile specimens include, but are not limited to the following. Suppliers procedures shall identify tolerances, ranges and/or control limits as applicable. Type of furnace Furnace atmosphere Alloy additions, fluxing, deoxidation, and gas removal procedur

45、es Gating and risering practice Mold composition and molding practice Core composition and fabrication method, when applicable Metal pouring temperature Solidification and cooling procedures Solution heat treat and precipitation hardening cycles Straightening procedure, when applicable Cleaning oper

46、ations Methods of inspection Radiographic inspection sampling plan, if used. 4.4.2.1.1 Any of the above process control factors for which parameters are considered proprietary by the vendor may be assigned a code designation. Each variation in such parameters shall be assigned a modified code design

47、ation. 4.5 Reports The vendor of castings shall furnish with each shipment a report showing the results of tests for composition of each melt and the results of tests for tensile properties of specimens cut from castings or, when specified or permitted, from integrally-cast coupons from each heat tr

48、eat lot, or from separately-cast test specimens representing each heat treat lot, and stating that the castings conform to the other technical requirements. This report shall include the purchase order, melt and heat treat lot numbers, AMS4219F, part number, and quantity. 4.6 Resampling and Retesting If any specimen used in the above tests fails to