SAE AMS 4117K-2015 Aluminum Alloy Rolled or Cold Finished Bars Rods and Wire and Flash Welded Rings 1 0Mg - 0 60Si - 0 28Cu - 0 20Cr (6061 -T6 -T651) (UNS A96061).pdf

《SAE AMS 4117K-2015 Aluminum Alloy Rolled or Cold Finished Bars Rods and Wire and Flash Welded Rings 1 0Mg - 0 60Si - 0 28Cu - 0 20Cr (6061 -T6 -T651) (UNS A96061).pdf》由会员分享，可在线阅读，更多相关《SAE AMS 4117K-2015 Aluminum Alloy Rolled or Cold Finished Bars Rods and Wire and Flash Welded Rings 1 0Mg - 0 60Si - 0 28Cu - 0 20Cr (6061 -T6 -T651) (UNS A96061).pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、AEROSPACEMATERIAL SPECIFICATIONAMS4117 REV. KIssued 1960-01Revised 2015-03Superseding AMS4117JAluminum Alloy, Rolled or Cold Finished Bars, Rods, and Wireand Flash Welded Rings1.0Mg - 0.60Si - 0.28Cu - 0.20Cr (6061; -T6, -T651)(Composition similar to UNS A96061)RATIONALEAMS4117K revises Properties (

2、3.3.1.1.2), Classification of Tests (4.2.1 and 4.2.2), Reports (4.4.1), and is a Five Year Review and update of this specification.1. SCOPE1.1 FormThis specification covers an aluminum alloy in the form of rolled or cold-finished bars, rods, and wire and of flash welded rings and stock for flash wel

3、ded rings.1.1.1 This specification covers rounds 8 inches (203 mm) and under in specified diameter, and square, rectangular, hexagonal, and octagonal bars 50 square inches (322 cm2) and under in cross-sectional area and 8 inches (203 mm) and under in least distance between parallel sides, and flash

4、welded rings 8 inches (203 mm) and under in radial thickness (See 8.4).1.2 ApplicationThese products have been used typically for parts requiring moderate strength where limited formability is acceptable, but usage is not limited to such applications.2. APPLICABLE DOCUMENTSThe issue of the following

5、 documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced document has been cancelled and no superseding doc

6、ument has been specified, the last published issue of that document shall apply._SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suit

7、ability for any particular use, including any patent infringement arising therefrom, is the sole responsibility of the user.”SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and sugges

8、tions.Copyright 2015 SAE InternationalAll rights reserved. No part of this publication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE.TO PLACE A DO

9、CUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada)Tel: +1 724-776-4970 (outside USA)Fax: 724-776-0790Email: CustomerServicesae.orgSAE WEB ADDRESS: http:/www.sae.orgSAE values your input. To provide feedbackon this Technical Report, please visithttp:/www.sae.org/technical/standards/AMS4117KSAE I

10、NTERNATIONAL AMS4117K Page 2 of 62.1 SAE PublicationsAvailable from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or +1 724-776-4970 (outside USA), www.sae.org.AMS2355 Quality Assurance Sampling and Testing of Aluminum Alloys and Magn

11、esium Alloys, Wrought Products, Except Forging Stock, and Rolled, Forged, or Flash Welded RingsAMS2772 Heat Treatment of Aluminum Alloy Raw MaterialsAMS7488 Rings, Flash Welded, Aluminum and Aluminum AlloysAS1990 Aluminum Alloy Tempers2.2 ASTM PublicationsAvailable from ASTM International, 100 Barr

12、Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org.ASTM B660 Packaging/Packing of Aluminum and Magnesium ProductsASTM B666/B666M Identification Marking of Aluminum and Magnesium Products2.3 ANSI PublicationsAvailable from American National Standards Instit

13、ute, 25 West 43rd Street, 4th Floor, New York, NY 10036, Tel: 212-642-4900, www.ansi.org.ANSI H35.2 Dimensional Tolerances for Aluminum Mill ProductsANSI H35.2M Dimensional Tolerances for Aluminum Mill Products (Metric)3. TECHNICAL REQUIREMENTS3.1 CompositionShall conform to the percentages by weigh

14、t shown in Table 1, determined in accordance with AMS2355.Table 1 - CompositionElement min maxSilicon 0.40 0.8Iron - 0.7Copper 0.15 0.40Manganese - 0.15Magnesium 0.8 1.2Chromium 0.04 0.35Zinc - 0.25Titanium - 0.15Other Elements, each - 0.05Other Elements, total - 0.15Aluminum remainder3.2 ConditionT

15、he product shall be supplied in the following condition:SAE INTERNATIONAL AMS4117K Page 3 of 63.2.1 Bars, Rods, and WireRolled or cold finished, as ordered.3.2.1.1 Bars, rods, and wire under 0.500 inch (12.70 mm) in nominal diameter or least distance between parallel sides shall be solution and prec

16、ipitation heat treated to the -T6 temper in accordance with AMS2772. Where -T6 temper is ordered, -T651 temper may be supplied.3.2.1.2 Bars and rods 0.500 to 8.000 inches (12.70 to 203.20 mm), inclusive, in nominal diameter or least distance between parallel sides shall be solution heat treated, str

17、ess-relieved by stretching to produce a nominal permanent set of 1-1/2% but not less than 1% nor more than 3%, and precipitation heat treated to -T651temper. Heat treatments shall be in accordance with AMS2772.3.2.1.2.1 Bars and rods stress-relieved by stretching shall receive no further straighteni

18、ng operations after stretching unless specifically authorized by purchaser.3.2.2 Flash Welded RingsShall be manufactured in accordance with AMS7488 and solution and precipitation heat treated to the -T6 temper in accordance with AMS2772.3.2.3 Stock for Flash Welded RingsAs ordered by the flash welde

19、d ring manufacturer.3.3 PropertiesProduct shall conform to the following requirements, determined in accordance with AMS2355 on the mill product.3.3.1 Bars, Rods, Wire, and Flash Welded Rings3.3.1.1 T6 and T651 Temper Tensile PropertiesShall be shown in Table 2 for rounds 8 inches (203 mm) and under

20、 in specified diameter, for square, rectangular, hexagonal, and octagonal bars 50 square inches (322 cm2) and under in cross-sectional area and 8 inches (203 mm) and under in least distance between parallel sides, and for flash welded rings 8 inches (203 mm) and under in radial thickness.Table 2 - T

21、6 and T651 temper minimum tensile propertiesProperty ValueTensile Strength 42.0 ksi (290 MPa)Yield Strength at 0.2% Offset 35.0 ksi (241 MPa)Elongation in 2 Inches (50.8 mm) or 4D 10%3.3.1.1.1 Yield strength and elongation requirements do not apply to product under 0.125 inch (3.18 mm) in nominal di

22、ameter or least distance between parallel sides.3.3.1.1.2 Mechanical property requirements for product outside of the range covered by 1.1.1 shall be as agreed upon between purchaser and producer.3.3.2 Stock for Flash Welded RingsSpecimens taken from the stock after solution and precipitation heat t

23、reatment in accordance with 3.2.2 shall conform to the requirements of 3.3.1.1.SAE INTERNATIONAL AMS4117K Page 4 of 63.3.3 Response to Heat Treatment3.3.3.1 Response to Heat Treatment (T6 or T651 to T42 Temper)When specified, product in the T6 or T651 temper (without the subsequent imposition of col

24、d working or forming operations), after solution heat treatment and natural aging to the T42 temper (see AS1990) in accordance with AMS2772 shall have the properties of Table 3. 3.3.3.1.1 Natural Aging before TestingSpecimens in the T42 tempers will not be required to be tested within 4 days after c

25、ompletion of the solution heat treatment. If, within this period, the manufacturer elects to test specimens, which thereupon fail to meet the requirements, they can discard these original test results and test additional specimens selected after four days of aging. These specimens shall be selected

26、from the same location in the production lot or sample as those tested previously in accordance with AMS2355.3.3.3.2 Response to Heat Treatment (T6 or T651 to T62 Temper)When specified, product in the T6 or T651 temper, after solution and precipitation heat treatment to the T62 temper (See AS1990) i

27、n accordance with AMS2772 shall have the properties shown in Table 3.3.3.3.3 T42 and T62 Temper Tensile PropertiesShall be shown in Table 3, except as specified in 3.3.3.3.1 and 3.3.3.3.2.Table 3 T42 and T62 temper minimum tensile propertiesTemperTensile Strength ksi (MPa)Yield Strength at 0.2% Offs

28、et ksi (MPa)Elongation in 2 inches or 4DT42 30.0 (207) 14.0 (97) 18T62 42.0 (290) 35.0 (241) 103.3.3.3.1 Tensile property requirements shown in Table 3 apply to rounds 8.000 inches (203.20 mm) and under in nominal diameter and to squares, rectangles, hexagons, and octagons having a cross-sectional a

29、rea of 50 square inches (322 cm2) and under in cross-sectional area and 8.000 inches (203.20 mm) and under in least distance between parallel sides, and for flash welded rings 8.000 inches (203.20 mm) and under in radial thickness.3.3.3.3.2 Yield strength and elongation requirements do not apply to

30、product under 0.125 inch (3.18 mm) in nominal diameter or least distance between parallel sides.3.4 QualityThe product, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from imperfections detrimental to usage of the product.3.5 Tolerance

31、sBars, rods, and wire shall conform to all applicable requirements of ANSI H35.2 or ANSI H35.2M.SAE INTERNATIONAL AMS4117K Page 5 of 64. QUALITY ASSURANCE PROVISIONS4.1 Responsibility for InspectionThe vendor of the product shall supply all samples for vendors tests and shall be responsible for the

32、performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the product conforms to specified requirements.4.2 Classification of Tests4.2.1 Acceptance TestsComposition (3.1), tensile properties (3.3.1.1), and toler

33、ances (3.5) are acceptance tests and, except for composition, shall be performed on each lot. Response to heat treatment, T6 or T651 to T42 temper (3.3.3.1) and T6 or T651 to T62 temper (3.3.3.2) are acceptance tests when specified by the purchaser.4.2.2 Periodic TestsThe ability of stock for flash

34、welded rings to develop required properties (3.3.2) are periodic tests and shall be performed ata frequency selected by the vendor unless frequency of testing is specified by purchaser.4.3 Sampling and TestingShall be in accordance with AMS2355.4.4 ReportsThe vendor of bars, rods, wire, and stock fo

35、r flash welded rings, shall furnish with each shipment a report stating that the product conforms to the composition and tolerances, and showing the numerical results of tests on each inspection lot to determine conformance to the other acceptance test requirements. This report shall include the pur

36、chase order number, inspection lot number(s), AMS4117K, size, and quantity. The report shall also identify the producer, the product form, and the size of the mill product.4.4.1 When the product size is outside the range covered by 1.1.1, the report shall contain a statement to that effect.4.5 Resam

37、pling and RetestingShall be in accordance with AMS2355.5. PREPARATION FOR DELIVERY5.1 Identification5.1.1 Bars, Rod, and WireIn accordance with ASTM B666/B666M.5.1.2 Flash Welded Rings and Stock for Flash Welded RingsAs agreed upon by purchaser and vendor.5.2 PackagingThe product shall be prepared f

38、or shipment in accordance with ASTM B660 and in compliance with applicable rules and regulations pertaining to the handling, packaging, and transportation of the product to ensure carrier acceptance and safe delivery.SAE INTERNATIONAL AMS4117K Page 6 of 66. ACKNOWLEDGMENTA vendor shall mention this

39、specification number and its revision letter in all quotations and when acknowledging purchase orders.7. REJECTIONSProduct not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection.8. NOTES8.1 A change bar (l) located in the left margin is for th

40、e convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the previous issue of this document. An (R) symbol to the left of the document title indicates a complete revision of the document, including technical revisions. Change bars and (R) are n

41、ot used in original publications, nor in documents that contain editorial changes only.8.2 Terms used in AMS are clarified in ARP1917.8.3 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary; dimensions and properties in SI units and the Celsius temperatures are

42、shown as the approximate equivalents of the primary units and are presented only for information.8.4 Purchase documents should specify not less than the following:AMS4117KForm and size or part number of product desiredProperty and acceptance requirements from the cognizant engineering organization applicable to sizes outside the range listed in 1.1.1Quantity of product desiredResponse to heat treatment, T6 or T651 to T42 temper (if required) (See 3.3.3.1)Response to heat treatment, T6 or T651 to T62 temper (if required) (See 3.3.3.2).PREPARED BY AMS COMMITTEE “D”