NAVY MIL-PRF-32170 A-2006 DECK TILES WEAR-RESISTANT《耐磨瓦》.pdf

《NAVY MIL-PRF-32170 A-2006 DECK TILES WEAR-RESISTANT《耐磨瓦》.pdf》由会员分享，可在线阅读，更多相关《NAVY MIL-PRF-32170 A-2006 DECK TILES WEAR-RESISTANT《耐磨瓦》.pdf（10页珍藏版）》请在麦多课文档分享上搜索。

1、 Comments, suggestions, or questions on this document should be addressed to Commander, Naval Sea Systems Command, ATTN: SEA 05Q, 1333 Isaac Hull Avenue, SE, Stop 5160, Washington Navy Yard DC 20376-5160 or emailed to commandstandardsnavsea.navy.mil, with the subject line “Document Comment“. Since c

2、ontact information can change, you may want to verify the currency of this address information using the ASSIST Online database at http:/assist.daps.dla.mil. AMSC N/A FSC 7220 INCH-POUND MIL-PRF-32170A 13 June 2006 SUPERSEDING MIL-PRF-32170 12 August 2004 PERFORMANCE SPECIFICATION DECK TILES, WEAR-R

3、ESISTANT This specification is approved for use by all Departments and Agencies of the Department of Defense. 1. SCOPE 1.1 Scope. This specification establishes the requirements for wear-resistant and fatigue reducing deck tile systems (including required adhesives and/or sealers) that are halogen f

4、ree and require no floor finish used in Naval shipboard interior applications. 1.2 Classification. Coatings covered by this specification are of the following types, as specified (see 6.2): 1.2.1 Type. The types of deck tile systems are as follows: Type I Deck tile system for general use. Type II De

5、ck tile system for use onboard submarines. 1.2.2 Class. The classes of deck tile systems are as follows: Class 1 Wear-resistant deck tile system for areas with moderate to heavy foot or vehicular traffic. Class 2 Fatigue reducing deck tile system for areas with light foot traffic only. 2. APPLICABLE

6、 DOCUMENTS 2.1 General. The documents listed in this section are specified in sections 3, 4, or 5 of this specification. This section does not include documents cited in other sections of this specification or recommended for additional information or as examples. While every effort has been made to

7、 ensure the completeness of this list, document users are cautioned that they must meet all specified requirements of documents cited in sections 3, 4, or 5 of this specification, whether or not they are listed. Provided by IHSNot for ResaleNo reproduction or networking permitted without license fro

8、m IHS-,-,-MIL-PRF-32170A 2 2.2 Government documents. 2.2.1 Specifications, standards and handbooks. The following specifications, standards, and handbooks form a part of this document to the extent specified herein. Unless otherwise specified, the issues of these documents are those cited in the sol

9、icitation or contract. FEDERAL STANDARDS FED-STD-141 - Paint, Varnish, Lacquer and Related materials: Methods of Inspection, Sampling and Testing DEPARTMENT OF DEFENSE STANDARDS MIL-STD-1623 - Fire Performance Requirements and Approved Specifications for Interior Finish Materials and Furnishings (Na

10、val Shipboard Use) (Copies of these documents are available online at http:/assist.daps.dla.mil/quicksearch or http:/assist.daps.dla.mil or from the Standardization Document Order Desk, 700 Robbins Avenue, Building 4D, Philadelphia, PA 19111-5094.) 2.2.2 Other Government documents, drawings, and pub

11、lications. The following other Government documents, drawings, and publications form a part of this document to the extent specified herein. Unless otherwise specified, the issues of these documents are those cited in the solicitation or contract. BUREAU OF MEDICINE AND SURGERY (BUMED) BUMED INST 62

12、70.8 - Procedures for Obtaining Health Hazard Assessments (HHAs) (Copies of this document are available online at https:/bumed.med.navy.mil/ or from Bureau of Medicine and Surgery, Department of the Navy, 2300 E Street, NW, Washington, DC 20372-5300.) NAVAL SEA SYSTEMS COMMAND (NAVSEA) S9510-AB-ATM-

13、010 - Nuclear Powered Submarine Atmosphere Control Manual, Chapter 7 (Copies of this document are available from Commander, Naval Sea Systems Command, SEA 05Z9, 1333 Isaac Hull Ave., SE, Stop 5122, Washington Navy Yard DC 20376-5122.) CODE OF FEDERAL REGULATIONS 40 CFR 60, Ch.1, Appendix A, Method 2

14、4 - Determination of Volatile Matter Content, Water Content, Density, Volume Solids, and Weight Solids of Surface Coatings 40 CFR 63 - National Emission Standards for Hazardous Air Pollutants for Source Categories 40 CFR 82 - Protection of Environment: Protection of Stratospheric Ozone 40 CFR 261 -

15、Protection of Environment: Identification and Listing of Hazardous Waste (Copies of these documents are available online at www.gpoaccess.gov/index.html. or from the Superintendent of Documents, U.S. Government Printing Office, North Capitol & “H” Streets, N.W., Washington, DC 20402-0002.) Provided

16、by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-PRF-32170A 3 2.3 Non-Government publications. The following documents form a part of this document to the extent specified herein. Unless otherwise specified, the issues of these documents are those cited in

17、 the solicitation or contract. ASTM INTERNATIONAL ASTM D 2047 - Standard Test Method for Static Coefficient of Friction of Polish-Coated Flooring Surfaces as Measured by the James Machine ASTM D 3389 - Standard Test Method for Coated Fabrics Abrasion Resistance (Rotary Platform, Double-Head Abrader)

18、 (DoD adopted) ASTM D 4060 - Standard Test Method for Abrasion Resistance of Organic Coatings by the Taber Abraser (DoD adopted) ASTM E 260 - Standard Practice for Packed Column Gas Chromatography ASTM E 1252 - Standard Practice for General Techniques for Obtaining Infrared Spectra for Qualitative A

19、nalysis ASTM F 137 - Standard Test Method for Flexibility of Resilient Flooring Materials with Cylindrical Mandrel Apparatus (DoD adopted) ASTM F 386 - Standard Test Method for Thickness of Resilient Flooring Materials Having Flat Surfaces (DoD adopted) ASTM F 1265 - Standard Test Method for Resista

20、nce to Impact for Resilient Floor Tile ASTM F 1514 - Standard Test Method for Measuring Heat Stability of Resilient Vinyl Flooring by Color Change ASTM F 1515 - Standard Test Method for Measuring Light Stability of Resilient Vinyl Flooring by Color Change ASTM F 1914 - Standard Test Method for Short

21、-Term Indentation and Residual Indentation of Resilient Floor Covering ASTM F 2055 - Standard Test Method for Size and Squareness of Resilient Floor Tile by Dial Gage Method ASTM F 2199 - Standard Test Method for Determining Dimensional Stability of Resilient Floor Tile after Exposure to Heat (Copie

22、s of these documents are available from www.astm.org or ASTM International, 100 Barr Harbor Drive, West Conshohocken, PA 19428-2959.) 2.4 Order of precedence. In the event of a conflict between the text of this document and the references cited herein, the text of this document takes precedence. Not

23、hing in this document, however, supersedes applicable laws and regulations unless a specific exemption has been obtained. 3. REQUIREMENTS 3.1 Qualification. Deck tiles furnished under this specification shall be products that are authorized by the qualifying activity for listing on the applicable qu

24、alified products list before contract award (see 4.2 and 6.3). 3.2 Recycled, recovered, or environmentally preferable materials. Recycled, recovered, or environmentally preferable materials should be used to the maximum extent possible, provided that the material meets or exceeds the operational and

25、 maintenance requirements, and promotes economically advantageous life cycle costs. 3.3 Dimensions and workmanship. 3.3.1 Size. The deck tiles size shall be as specified (see 6.2). The size of deck tiles shall not vary greater than 1/64-inch per foot (0.4 mm/305 mm). 3.3.2 Thickness. The deck tiles

26、size shall be as specified (see 6.2). The thickness of deck tiles shall not vary by 0.005 in (0.13 mm). Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-PRF-32170A 4 3.3.3 Squareness. The out-of-squareness of the tile shall not exceed 0.010 in. (0

27、.25 mm). 3.3.4 Weight. 3.3.4.1 Class 1 products. The deck tiles weight shall be as specified (see 6.2). The weight of deck tiles shall not vary by 2 percent from the specified values. In no case shall the tiles weigh greater than 0.7 pounds per square foot. 3.3.4.2 Class 2 products. The deck tiles w

28、eight shall be as specified (see 6.2). The weight of the deck tiles shall not vary by 2 percent from the specified values. In no case shall the tiles weigh greater than 2.7 pounds per square foot. 3.3.5 Workmanship. The deck tiles shall be uniform in quality and condition. They shall be clean, smoot

29、h, and free from all foreign materials and defects, including those listed in Table IV. 3.3.6 Dimensional stability. The dimensional stability of the deck tiles shall not vary by greater than 0.020 in/linear foot (0.51 mm/305 mm). 3.4 Fire performance. The fire performance of the deck tile system, i

30、ncluding any required adhesive and/or sealer, shall conform to the requirements in MIL-STD-1623. 3.5 Indentation (Class 1 only). The average initial indentation shall not exceed 10 percent, and the initial indentation of any single specimen shall not exceed 12 percent. The average residual indentati

31、on at the end of the 60-minute recovery period shall not exceed 8 percent, and the maximum residual indentation of any single specimen shall not exceed 10 percent. 3.6 Flexibility before and after heating. The deck tiles shall not crack, break, or show any indication of weakness when tested before a

32、nd after heating. 3.7 Wear resistance. The deck tiles shall not show wear characteristics exceeding 30 mg loss. 3.8 Resistance to heat and light. The exposed surface of the deck tile system shall show no appreciable change in color, delamination, or signs of checking, cracking or any other deteriora

33、tion. The measured change in color shall not exceed 5 E as defined in ASTM F 1514 and ASTM F 1515. 3.9 Slip resistance. The deck tiles shall have slip resistance equal to or greater than 0.50 static coefficient of friction. 3.10 Impact resistance. The deck tile system shall show no visible signs of

34、chipping, cracking, or detachment from the steel plate outside the prescribed zinc oxide circle. 3.11 Resistance to cleaning agents. The deck tile system shall show no blistering or wrinkling and no more than a slight whitening or softening upon removal of the fluid wetted sponges. After 2 hours of

35、air drying, the portion of the panel that was covered by fluid wetted sponges shall be indistinguishable with regard to hardness, color, and gloss from the unexposed areas of the tile system. 3.12 Serviceability. The deck tile system shall show no deficiencies that would limit its serviceability whe

36、n examined during and after the minimum service period specified in 4.4.10, and shall maintain an acceptable aesthetic appearance with no finish added and a maximum maintenance requirement of periodic wet mopping with water. 3.13 Off-gassing (Type II only). The deck tile system (including required a

37、dhesive and/or sealer) shall be tested for off-gassing in accordance with Chapter 7 of NAVSEA Technical Manual S9510-AB-ATM-010, and shall be certified for and assigned a usage category of either “Limited” or “Permitted” (see 4.4.11 and 6.5). Provided by IHSNot for ResaleNo reproduction or networkin

38、g permitted without license from IHS-,-,-MIL-PRF-32170A 5 3.14 Toxicity. The deck tile system shall have no adverse effect on the health of personnel when used for its intended purpose and shall not cause any environmental problems during waste disposal (see 4.4.12 and 6.6). 3.15 Disposal. The deck

39、tile system (including required adhesive and/or sealers) shall not contain any hazardous material or exhibit any hazardous characteristic as defined under 40 CFR 261. 3.16 Volatile organic content (VOC) solvent. The VOC of all adhesives and/or sealers specified for use with the deck tiles shall not

40、exceed 250 grams per liter (g/L). 3.17 Hazardous air pollutant (HAP) content. The HAP content of solvents in the adhesive and/or sealer specified by the manufacturer for use with the deck tile system shall not exceed the weight percent (%wt) values listed in Table I. HAP materials are defined by 40

41、CFR 63. TABLE I. Hazardous air pollutant solvent content limits. Hazardous solvent in adhesive or sealer Maximum, %wt Benzene 0.05 Chlorinated solvent(s), total 0.05 Solvents containing fluorine as defined by 40 CFR 82 0.01 Ethyl benzene 0.05 Methyl, ethyl and butyl mono-ethers of ethylene glycol or

42、 the acetates thereof, total (also known as methyl, ethyl and butyl cello solves and methyl, ethyl and butyl cello solve acetates) 0.05 Methyl ethyl ketone (MEK) 0.05 Methyl isobutyl ketone (MIBK) 0.05 Toluene 0.05 Xylene (all forms), total 0.1 3.18 Halogen content. The deck tiles shall be halogen f

43、ree. 4. VERIFICATION 4.1 Classification of inspections. The inspection requirements specified herein are classified as follows: a. Qualification inspection (see 4.2). b. Conformance inspection (see 4.3). 4.1.1 Inspection conditions. Unless otherwise specified (see 6.2), all inspections shall be perf

44、ormed in accordance with the tests specified in 4.2, 4.3, and 4.4. 4.2 Qualification inspection. Qualification inspection shall consist of the inspections and tests specified in Table II. 4.2.1 Changes to product. Any change in basic ingredients or processes which would affect compliance with this s

45、pecification must be reported to both the contracting activity and NAVSEA. The Government reserves the right to require that the product be requalified before shipment is made. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-PRF-32170A 6 TABLE II

46、. Qualification inspection. Inspections Requirements Tests Dimensions and workmanship 3.3 4.4.1 Fire performance 3.4 4.4.2 Indentation 3.5 4.4.3 Flexibility before and after heating 3.6 4.4.4 Wear resistance 3.7 4.4.5 Resistance to heat and light 3.8 4.4.6 Slip resistance 3.9 4.4.7 Impact resistance

47、 3.10 4.4.8 Resistance to cleaning agents 3.11 4.4.9 Serviceability 3.12 4.4.10 Off-gassing 3.13 4.4.11 Toxicity 14 4.4.12 Disposal 15 4.4.13 Volatile organic content (VOC) solvent 3.16 4.4.14 Hazardous air pollutant (HAP) content 3.17 4.4.15 Halogen content 3.18 4.4.16 4.3 Conformance inspection. 4

48、.3.1 Inspection of end item. Inspections shall be in accordance with Table III. TABLE III. Inspection of end item. Inspections Requirements Tests Size 3.3.1 4.4.1.1 Thickness 3.3.2 4.4.1.2 Squareness 3.3.3 4.4.1.3 Weight 3.3.4 4.4.1.4 Workmanship 3.3.5 4.4.1.5 Dimensional stability 3.3.6 4.4.1.6 4.3

49、.1.1 Inspection of end item for defects in appearance. Visual inspections shall be in accordance with Table IV and 4.3.3. TABLE IV. Inspection for visual defects. Inspection Defect Workmanship Cracking Workmanship Scratches Workmanship Pits Workmanship Embedded foreign matter Workmanship Evidence of delamination Workmanship Broken edges Workmanship Voids Workmanship Non-uniform finish 4.3.2 Lot. A lot shall consist of all unit