NAVY MIL-C-81814 C (1)-2003 CLOTH TWILL ARAMID HIGH TEMPERATURE RESISTANT《耐高温的芳族聚酰胺斜纹布织的帆》.pdf

《NAVY MIL-C-81814 C (1)-2003 CLOTH TWILL ARAMID HIGH TEMPERATURE RESISTANT《耐高温的芳族聚酰胺斜纹布织的帆》.pdf》由会员分享，可在线阅读，更多相关《NAVY MIL-C-81814 C (1)-2003 CLOTH TWILL ARAMID HIGH TEMPERATURE RESISTANT《耐高温的芳族聚酰胺斜纹布织的帆》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 MILITARY SPECIFICATION CLOTH, TWILL, ARAMID, HIGH TEMPERATURE RESISTANT This amendment forms a part of MIL-C-81814C, dated 17 August 1990, and is approved for use by all Departments and Agencies of the Department of Defense. PAGE 2 Paragraph 2.2, add the following test methods that have replaced me

2、thods from FED-STD-191: “AATCC16 Colorfastness to Light” “AATCC20A Fiber Analysis: Quantitative” “AATCC61 Colorfastness to Laundering, Home and Commercial: Accelerated” “AATCC158 Dimensional Changes on Drycleaning in Perchloroethylene: Machine Method”. “ASTM-D737 Test Method for Air Permeability of

3、Textile Fabrics” “ASTM-D1422 Test Method for Twist in Single Spun Yarns by the Untwist-Retwist Method” “ASTM-D1683 Test Method for Failure in Sewn Seams of Woven Fabrics “ASTM-D2261 Test Method for Tearing Strength of Fabrics by the Tongue (Single Rip) Procedure” “ASTM-D3775 Test Method for Fabric C

4、ount of Woven Fabric” “ASTM-D3776 Test Method for Mass Per Unit Area (Weight) of Fabric” “ASTM-D5035 Test Method for Breaking Force and Elongation of Textile Fabrics (Strip Method)” “ (Applications for copies should be addressed to the American Society for Testing and Materials, 100 Barr harbor Driv

5、e, West Conshohocken, PA 19428-2959.)” AMSC N/A 1 of 3 FSC 8305 DISTRIBUTION STATEMENT A. Approved for public release; distribution is unlimited.INCH-POUND MIL-C-81814C AMENDMENT 1 29 August 2003 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-C-

6、8184C AMENDMENT 1 2 PAGE 3 Table I, Characteristics column: Shrinkage after 10 launderings, delete “launderings” and substitute “drycleanings”. Table I, Requirements column: Shrinkage after 10 launderings, delete “2.0” for warp and substitute “4.0”. PAGE 8 Table II, test method column: Delete FED-ST

7、D-191 test methods and substitute commercial test methods as follows: Test method Commercial Standard “5660” “AATCC-16 Opt A” “5610” “AATCC-61 Test 4A” “5041” “ASTM-D-3776 Opt C” “5050” “ASTM-D-3775” “4052” “ASTM-D-1422” “5104” “ASTM-D-5035” “5134” “ASTM-D-2261” “5450” “ASTM-D-737” “2611” “AATCC-20A

8、” “5110” “ASTM-D1683” “5556 3/ ” “AATCC 158” PAGE 9 Table II, Characteristics column: Dimensional Stability, delete “launderings” and substitute “drycleanings”. Table II, test method column: Delete “5556 3/ ” and substitute commercial test method “AATCC 158” Table II, Delete footnote 3/. Provided by

9、 IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-C-8184C AMENDMENT 1 3 Custodians: Preparing Activity: Navy AS Navy AS Air Force 11 DLA CT (Project 8305-0816) Review activities: Navy NU Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-