INTERN CEMS GT-8-2009 Heat Resistant Properties Of Paint《油漆的耐热性能》.pdf

《INTERN CEMS GT-8-2009 Heat Resistant Properties Of Paint《油漆的耐热性能》.pdf》由会员分享，可在线阅读，更多相关《INTERN CEMS GT-8-2009 Heat Resistant Properties Of Paint《油漆的耐热性能》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、This document is restricted and may not be sent outside Navistar, Inc. or reproduced without permission from Corporate Technical Standards. Suppliers are required to assume all patent liability. 2009 by Navistar, Inc. AUGUST 2009 Page 1 of 2 NAVISTAR, INC. CEMS (CORPORATE ENGINEERING MATERIAL SPECIF

2、ICATION) NUMBER: CEMS GT-8 TITLE: Heat Resistant Properties Of Paint CURRENT ISSUE DATE: August 2009 WRITTEN/REVIEWED BY: Materials Engineering APPROVED BY: Materials Engineering SUPERSEDES ISSUE OF: August 2001 PRINTED COPIES OF THIS DOCUMENT MUST BE VERIFIED FOR CURRENT REVISION This specification

3、 may involve hazardous materials, equipment, and procedures. This specification does not purport to address all of the safety issues associated with its use. The user is responsible to consult appropriate safety and health practices and to determine the applicability of regulatory limits prior to us

4、e. Change Notice: Replaced “International Truck and Engine Corporation” with “Navistar, Inc.” per corporate directive. 1.0 SCOPE This is a method for evaluating the ability of a dry film of paint to withstand degradation upon prolonged exposure to high temperatures. . 2.0 APPARATUS 2.1 Muffle furnac

5、e capable of maintaining 538 + 6C (1000 + 10F) 2.2 Humidity cabinet per Federal Standard 141a, Method 6201 or QCT humidity cabinet available from the Q-Panel Company, 15610 Industrial Parkway, Cleveland, Ohio 44135. 3.0 MATERIAL 3.1 Aluminized sheet steel panels, 20 gage - 0.8 mm (.033 inches), 100

6、x 200 mm (4 x 8 inches) 3.2 Bonderite CD-10 or Bonderite 958 zinc phosphated steel panels, 100 x 200 mm (4 x 8 inches), available from Advanced Coatings Technologies, 273 Industrial Drive, Hillsdale, Michigan 49242. 4.0 PROCEDURE 4.1 Prepare three aluminized panels and three phosphated steel panels

7、according to Test Method GT-13, Method D. Dry these panels according to the oven drying procedure specified. 4.2 Place all panels in a muffle furnace at 204 + 6C (400 + 10F) and raise temperature to 538 + 6C (1000 + 10F) within 29 to 30 minutes. 4.3 Maintain the furnace temperature at 538 + 6C (1000

8、 + 10F) for 100 hours. 4.4 At the conclusion of the 100 hour period, gradually cool the panels (in not less than 40 minutes) to a temperature below 204 + 6C (400 + 10F) without removing the panels. 4.5 Remove the panels from the furnace and allow them to cool to 21 to 27C (70 to 80F). Turn off the f

9、urnace. 4.6 Examine each of the panels with the unaided eye for evidence of delamination. Evaluate the smoothness and the overall adhesion characteristics of the dry film of each of the panels. Examine the panels for evidence of color change from the original panels. 4.7 On each of the cooled panels

10、 from step (6), perform the humidity test outlined in Test Method GT-7E, commencing with the fourth step. Copyright Navistar International Corporation Provided by IHS under license with INTERNNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-NUMBER: CEMS GT-8 TITLE:

11、Heat Resistant Properties Of Paint CURRENT ISSUE DATE: August 2009 This document is restricted and may not be sent outside Navistar, Inc. or reproduced without permission from Corporate Technical Standards. Suppliers are required to assume all patent liability. 2009 by Navistar, Inc. AUGUST 2009 Pag

12、e 2 of 2 5.0 REPORT Report the following information: 5.1 Dry film appearance after 538C (1000F) exposure: The paint will pass if each of the test panels exhibits a dry film which is uniformly smooth and shows good adhesion, no color change from the original panels and no delamination. All panels wi

13、ll pass. 5.2 Dry film appearance after 538C (1000F) exposure and humidity test: The paint shall pass if each of the test panels exhibits a dry film which shows no evidence of rust or blistering. All panels will pass. Copyright Navistar International Corporation Provided by IHS under license with INTERNNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-