FORD WSS-M7H61-A-2003 WEBBING POLYPROPYLENE PULL STRAP 20 5 mm WIDE TO BE USED WITH FORD WSS-M99P1111-A 《20 5 mm宽拉带用聚丙烯（PP）织物带 与标准FORD WSS-M99P1111-A一起使用 》.pdf

《FORD WSS-M7H61-A-2003 WEBBING POLYPROPYLENE PULL STRAP 20 5 mm WIDE TO BE USED WITH FORD WSS-M99P1111-A 《20 5 mm宽拉带用聚丙烯（PP）织物带 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M7H61-A-2003 WEBBING POLYPROPYLENE PULL STRAP 20 5 mm WIDE TO BE USED WITH FORD WSS-M99P1111-A 《20 5 mm宽拉带用聚丙烯（PP）织物带 与标准FORD WSS-M99P1111-A一起使用 》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2003 07 11 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 1 of 2 WEBBING, POLYPROPYLENE, PULL STRAP, 20.5 mm WIDE WSS-M7H61-A 1. SCOPE The material defined by this specification is a

2、 polypropylene pull strap woven with continuous filament yarn and finished selvages. Proper dyes and dyeing procedures shall be employed to provide acceptable colors, appearance, and physical properties. Color stripping for redyeing of webbing rejected for color is not allowed. The webbing shall be

3、of good quality and uniform construction. 2. APPLICATION This specification was released originally for material used as a rear seat back assist strap on P131 Crew Cab 2004 Model Year. 3. REQUIREMENTS In addition to the requirements listed herein, this material must meet the requirements of the WSS-

4、M15P40-A, webbing materials. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 APPEARANCE (FLTM BI 109-01) The color, pattern, and finish shall match the approved

5、Design Center master sample, or shall be as specified on the engineering drawing. 3.3 THICKNESS, range 1.6 +/- 0.2 mm (SAE J882) 3.4 WIDTH Measured at less than 22 N load 3.4.1 Minimum 20 mm 3.4.2 Maximum 22 mm 3.5 COMPOSITION (ASTM D 629) Polypropylene 99.6% Polyester 0.4% ENGINEERING MATERIAL SPEC

6、IFICATIONWSS-M7H61-APrinted copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 2 of 2 3.6 YARN CONSTRUCTION (ASTM D 1244) Warp 74.4 tex f144 t0 semi-dull polypropylene Fill 74.4 tex f144 t0 semi-dull polypropylene Catchcord 1/16.7 tex semi-dull round polyester Ends per width

7、 134 Picks per 25mm 24 +/- 2 Dye Method solution dye 3.7 WEIGHT, min 14.80 +/- 1.5 g/m 3.8 BREAKING STRENGTH, min (ASTM D 5034) Full Width 2840 N 3.9 RESISTANCE TO FADE, min (SAE J1885, AATCC Evaluation Procedure 1) 112.8 kJ/m2Rating 4 3.9.1 Retained Breaking Strength after 112.8kJ/m2exposure 40% No

8、 individual yarn or combination of yarns shall fade, stain or exhibit any color tone change, nor shall the yarns change in hue or brightness in excess of the above ratings. 3.10 RESISTANCE TO CROCKING, min (FLTM BN 107-02, Evaluation Procedure 3) Dry and Wet Rating 4.0 3.11 FOGGING (SAE J1756, 3h at 100 C heating, 21 C cooling) Fog Number, min 70 The formation of clear film, droplets or crystals is cause for rejection. 3.12 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute