FORD WSS-M5H46-A1-2016 FABRIC WINSTON NON WOVEN LATEX IMPREGNATED TO BE USED WITH FORD WSS-M99P1111-A .pdf

《FORD WSS-M5H46-A1-2016 FABRIC WINSTON NON WOVEN LATEX IMPREGNATED TO BE USED WITH FORD WSS-M99P1111-A .pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M5H46-A1-2016 FABRIC WINSTON NON WOVEN LATEX IMPREGNATED TO BE USED WITH FORD WSS-M99P1111-A .pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev 00 2016 05 24 Released C. Zhang AP Controlled document at www.MATS Copyright 2016, Ford Global Technologies, LLC Page 1 of 3 FABRIC, WINSTON, NON WOVEN, LATEX IMPREGNATED WSS-M5H46-A1 1. SCOPE The material defined by this specification is

2、 for Winston pattern, a needled non-woven polyester fabric impregnated with synthetic latex. 2. APPLICATION This specification was released originally for material used as cover material for headliners. Any other applications must be evaluated and approved by the responsible Materials Engineering ac

3、tivity. 3. REQUIREMENTS 3.1 APPROVED SOURCES This specification requires the use of approved sources. Only the sources identified on the Ford Approved Source List (ASL) can be used when this specification is listed on the drawing, CAD file, or other documents. The list of approved sources is located

4、 within Ford at or available externally through a Ford Materials Engineer. 3.2 FABRIC PERFORMANCE 3.2.1 Materials manufactured to this Specification shall also meet the requirements contained in WSS-M8P27-A1/latest. 3.2.2 Materials manufactured to this Specification may also meet the following appl

5、icable specifications: Headlining Formed Performance: WSS-M15P27- G/latest IP and Soft Interior Assembly Performance: WSS-M8P27-A1/latest. Sun visor Assembly Performance: WSS-M98P3-B/latest. 10% Transmittance Fixed Tinted Glass Sunshade: WSS-M5H33-B 0% Transmittance Moonroof/Sunroof : WSS-M5H34-B 3.

6、3 APPEARANCE The color, pattern, and finish shall match the approved Corporate Design master sample 3.4 VEHICLE INTERIOR ENVIRONMENTAL PERFORMANCE Materials used in interior applications must meet the requirements outlined in WSS-M99P2222- D1/latest. 3.5 CONDITIONING AND TEST CONDITIONS All test val

7、ues are based on material conditioned for not less than 24 h prior to testing in a controlled environment of 23 +/- 2 C and 50 +/- 5% relative humidity. Testing of the material should occur in the conditioning environment or soon after removal. ENGINEERING MATERIAL SPECIFICATION WSS-M5H46-A1 Copyrig

8、ht 2016, Ford Global Technologies, LLC Page 2 of 3 3.6 FABRIC CONSTRUCTION 3.6.1 Fabric Weight (FLTM BN 106-01) Fiber 218-258 g/m2 Impregnated Latex 5-10 g/m2 Total 223-268 g/m2 3.7 COMPOSITION (ASTM D629) 3.7.1 Fabric 100% polyester 3.7.2 Thickness 1.9 2.4 mm (SAE J882) 3.8 YARN CONSTRUCTION (ASTM

9、D1244) Fiber Description and Construction 3.3-4.5dtex Polyester 3.9 METHOD OF DYEING Solution Dyed 3.10 STRENGTH PROPERTIES 3.10.1 Breaking Strength 250N min (ASTM D5034 Grab Method, 300 mm/min speed Average of 5 samples in each direction) 3.10.2 Ultraviolet Deterioration Retained Breaking Strength

10、(FLTM BO 116-01, ASTM D5034 Grab Method, 300 mm/min speed Average of 5 samples in each direction) Headliner application 225.6 kJ/m2 250N min 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for

11、 questions concerning Engineering Material Specifications. 4.1 Purchase departments will ensure that the material defined in this specification and shipped to any one assembly plant will be produced by one supplier only. In the event of a Global Program or Regional duplication, each regional locatio

12、n of the supplier for this specification must provide a Construction package and be approved to meet this specification. 4.2 If yarn is locally sourced it must meet the above fabric construction, composition and yarn construction. 4.3 APPROVAL OF MATERIALS Suppliers desiring approval of their materi

13、als shall first obtain an expression of interest from Purchasing, Design or Product Development, and Materials Engineering. The supplier shall submit a completed copy of their laboratory test reports, signed by a qualified and authorized ENGINEERING MATERIAL SPECIFICATION WSS-M5H46-A1 Copyright 2016

14、, Ford Global Technologies, LLC Page 3 of 3 representative of the test facility, demonstrating full compliance with all the requirements of the Material Specification. Tested material samples must be available for review upon request and kept for a minimum of one year. Upon request, the supplier wil

15、l review the associated quality control documents (Process Failure Mode and Effects Analysis, Control Plans, Certification testing) with Ford. 4.4 SUPPLIERS ONGOING RESPONSIBILITY All materials must be equivalent in all characteristics to the material upon which approval was originally granted. Prio

16、r to making any changes to the material originally approved, whether or not such changes affect the materials ability to meet the specification requirements, the supplier shall notify the affected Supplier Technical Assistance (STA), Purchasing, and Materials Engineering activities of the proposed c

17、hanges (with reasons) by submission of a completed Suppliers Request for Engineering Approval, SREA. For parts and components using Ford Engineering Material Specifications, all samples tested to the specifications for Design Verification (DV), Production Verification (PV) and Production Part Approv

18、al Process (PPAP) sign off must be kept until Job 1. 4.5 RESTRICTED SUBSTANCE MANAGEMENT STANDARD Substance restrictions imposed by regulations or Company direction applies to the materials addressed by this document. The restrictions are identified in the Restricted Substance Management Standard WSS-M99P9999-A/latest which is updated yearly. It is the suppliers responsibility to comply with this standard on a continuing basis. 5. SUMMARY OF REVISIONS