FORD WSS-M4D1051-A2-2014 POLYCARBONATE (PC) GENERAL PURPOSE INTERIOR TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSS-M4D1051-A1).pdf

《FORD WSS-M4D1051-A2-2014 POLYCARBONATE (PC) GENERAL PURPOSE INTERIOR TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSS-M4D1051-A1).pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M4D1051-A2-2014 POLYCARBONATE (PC) GENERAL PURPOSE INTERIOR TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSS-M4D1051-A1).pdf（7页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 3 2014 12 16 Editorial See Summary of Revisions L. Soreide, NA 2014 07 21 Revised See Summary of Revisions R. Harris, NA 2012 06 22 Activated G. Eaton, NA Controlled document at www.MATS Copyright 2014, Ford Global Technologies, LLC Page

2、 1 of 7 POLYCARBONATE (PC), GENERAL PURPOSE, EXTERIOR WSS-M4D1051-A1 POLYCARBONATE (PC), GENERAL PURPOSE, INTERIOR WSS-M4D1051-A2 1. SCOPE The material defined by this specification is a thermoplastic injection molded compound based on polycarbonate. This is a non UV-stable material. 2. APPLICATION

3、WSS-M4D1051-A1: This specification was released originally for materials used for headlamp lenses and rear lamp housings and protected by UV resistant coatings. WSS-M4D1051-A2: This specification was released originally for materials used for general purpose applications not requiring optical clarit

4、y, such as instrument cluster light filters. This material may be color pigmented when optical transparency is not required. 2.1 LIMITATIONS This material does not contain UV stabilizers, long term exposure to direct sunlight will cause chalking and loss of gloss. 3. REQUIREMENTS 3.1 STANDARD REQUIR

5、EMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.1.1 Many 4D resin specifications prior to 2011, identified certain requirements with the symbol (s), which indicated that the mean and

6、 +/- 3 sigma values were to be reported. The specification minimum, maximum or range was established using 3 sigma data. For 2011 and beyond, refer to Table 1 for number of samples required for each test. 3.1.2 The use of regrind is permitted, for economic / environmental reasons, with compliance as

7、 indicated in Ford Engineering CAD and Drafting Standard E-4. 3.1.3 WSS-M4D1051-A2: Materials used in interior applications must meet the requirements outlined in WSS-M99P2222-C1/Latest, Performance, Vehicle Interior Environment Quality Material/Component Requirements. Data must be included in mater

8、ial submission. 3.1.4 Performance Criteria: WSS-M4D1051-A1: Parts using this specification shall meet the appropriate performance specifications, WSS-M98P13-C/Latest (MIC Exterior) or WSK-M98P10-A/Latest (Exterior Lamp Assembly). WSS-M4D1051-A2: Parts using this specification shall meet the appropri

9、ate performance specification, WSS-M15P4-F/Latest. ENGINEERING MATERIAL SPECIFICATION WSS-M4D1051-A1 WSS-M4D1051-A2 Copyright 2014, Ford Global Technologies, LLC Page 2 of 7 3.2 SAMPLE PREPARATION Unless otherwise specified all tests shall be carried out on injection molded, one-end gated test speci

10、mens. The test specimens A and D shall be molded using molding conditions defined in ISO 7391-2. See Tables 1 and 2 for the number of samples required. Specimens shall be as follows: Specimen A 150 minimum x 10 x 4.0 +/- 0.2 mm (ISO 527-2, specimen type 1A) Specimen B 355 x 100 x 1.0 +/- 0.1 mm (ISO

11、 3795) Specimen C 145 x 60 x 3.2 +/- 0.2 mm Specimen D Center of Specimen A. 80 x 10 x 4.0 +/- 0.2 mm Specimen E 100 mm diameter x 3.2 mm thick Specimen F 80 mm diameter x 3.2 mm Specimen G 90 mm x 200 mm Specimen H 50 +/- 1 mm diameter x 3.2 +/- 0.2 mm Specimen I 100 mm x 150 mm, min 3.3 APPEARANCE

12、 3.3.1 Weathering Resistance (WSS-M4D1051-A2 only) Rating 4 min (FLTM BO 116-01, 601.6 kJ/m2 exposure Specimen C from smooth polished mold, ISO 105-A02 / AATCC Evaluation Procedure 1) After exposure the material shall show no fading or color change in excess of the specified AATCC rating. In additio

13、n, there shall be no cracking, crazing or other deterioration. Use regional choice for initial approval and report the color house used. See Table 2 for additional color durability submission requirements. 3.4 MATERIAL PROPERTIES 3.4.1 Density 1.17 1.23 g/cm3 (ISO 1183, Method A) 3.4.2 Tensile Stren

14、gth at Yield 59 MPa min (ISO 527-1 Flow Cross Flow 7.1 7.7 E-5 mm/mm/C E-5 mm/mm/C 3.5.3 Molding Shrinkage After 48 h at 23 +/- 2 C (For specific method and sample size, contact Materials Engineering) Flow Cross Flow 0.78 0.78 % % 3.5.4.1 Impact Strength, Notched Izod; At 23 +/- 2 C 10 kJ/m2 3.5.4.2

15、 Impact Strength, Notched Izod; At -40 +/- 2 C 6 kJ/m2 3.5.5 Poissons Ratio 0.38 N/A 4.2 MATERIAL IDENTIFICATION FOR RECYCLING PURPOSES (ISO 1043/ 11469) PC ENGINEERING MATERIAL SPECIFICATION WSS-M4D1051-A1 WSS-M4D1051-A2 Copyright 2014, Ford Global Technologies, LLC Page 6 of 7 Table 1: Minimum Sam

16、ple Size Initial Approval New Manufacturing Location for Previously Approved Material Para. Test Minimum Lots Specimens per Lot Total Test Specimens Lots Specimens per lot Total Test Specimens 3.1 WSS-M99P1111-A 3.1.4 WSS-M99P2222-C1/Latest Total Carbon, Hazardous Substances, Formaldehyde, Acraldehy

17、de, Acetaldehyde (See below for Odor and Fogging) 1 1 1 per test 3.3.1 Weathering 1 1 1 3.4.1 Density 1 3 3 3.4.2 Tensile Strength at Yield* 3 5 15 1 5 5 3.4.3 Elongation at Yield* 3 5 15 1 5 5 3.4.4 Tensile Modulus 1 10 10 3.4.5 Flexural Modulus 3 10 30 1 10 10 3.4.6 Impact Strength Izod, Notched (

18、per condition)* 3 10 30 1 10 10 3.4.7 Heat Deflection Temperature* 3 2 6 1 2 2 3.4.8 Vicat Softening Temperature 3 2 6 1 2 2 3.4.9 Heat Aging Performance 3.4.9.1 Tensile Strength at Yield, Change 1 5 5 3.4.9.2 Impact Strength, Notched Charpy Change 1 10 10 3.4.10 Fogging Photometric 1 3 3 3.4.11 Odo

19、r 1 9 9 3.4.12 Flammability 1 5 5 3.5.1 Melt Flow Rate 1 1 1 3.5.2 Coefficient of Linear Thermal Expansion (per condition) 1 3 3 3.5.3 Mold Shrinkage 1 5 5 3.5.4 Post Shrinkage 1 5 5 3.5.5 Impact Strength, Izod, Notched (per condition) 1 10 10 3.4.6 Poissons Ratio 1 2 2 3.4.7 Curves - IR - TGA - DSC

20、 - CLTE - Engineering Stress/Strain at 23 C 1 1 1 per test * For these requirements the 3 sigma value from the raw data is used to meet the requirements. ENGINEERING MATERIAL SPECIFICATION WSS-M4D1051-A1 WSS-M4D1051-A2 Copyright 2014, Ford Global Technologies, LLC Page 7 of 7 Table 2: Minimum Color

21、Property Testing 5. SUMMARY OF REVISIONS 2014 12 15 Editorial Corrected prefix in section 3.1.4 2014 07 21 Changed melt flow from 14.5-21.9 low flow 11 and high flow of 18. Removed gravimetric fogging. 2014 01 21 Editorial added PC to titles. Para. Test Lots Specimens per Lot Total Test Specimens Co

22、lor Test Direction 3.3.1 Weathering Resistance 1 1 1 Every color 3.4.2 Tensile Strength at Yield 1 5 5 As directed by Materials Engineering 3.4.5 Flexural Modulus 1 10 10 As directed by Materials Engineering 3.4.6.1 Impact Strength, Notched Charpy at 23 +/- 2 C 1 10 10 As directed by Materials Engineering 3.4.11 Fogging Photometric 1 3 3 As directed by Materials Engineering 3.4.12 Odor 1 9 9 As directed by Materials Engineering 3.4.13 Flammability 1 5 5 Every color