《FORD WSS-M3H133-A-2010 CARPET BCF NYLON BAVARIA PATTERN PRECOATED 515 g m2 TO BE USED WITH FORD WSS-M99P1111-A 《巴伐利亚（BAVARIA）图案的515 g m、预涂层尼龙BCF地毯 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M3H133-A-2010 CARPET BCF NYLON BAVARIA PATTERN PRECOATED 515 g m2 TO BE USED WITH FORD WSS-M99P1111-A 《巴伐利亚（BAVARIA）图案的515 g m、预涂层尼龙BCF地毯 与标准FORD WSS-M99P1111-A一起使用 》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2010 03 04 N-STATUS No replacement named L. Sinclair, NA 2003 04 11 Activated L.Soreide Printed copies are uncontrolled Page 1 of 3 Copyright 2010, Ford Global Technologies, Inc. CARPET, BCF NYLON, BAVARIA P

2、ATTERN, PRECOATED, 515 g/m WSS-M3H133-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The materials defined by this specification is a bulked continuous filament (BCF) nylon, cut pile carpets, tufted into a synthetic primary foundation. It is then precoated and laminated to a barrier material for improved

3、fit and acoustical properties. 2. APPLICATION These materials were released originally for carpets used for full floor application as part of the Carpet Construction Strategy. 3. REQUIREMENTS In addition to the requirements listed herein, the end-item carpet assembly (molded or otherwise fabricated)

4、 shall meet all requirements of the WSS-M8P16-A performance specification for full floor applications. Must also meet the Sound and Heat SDS. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Mat

5、erials (WSS-M99P1111-A). 3.2 SAMPLE SELECTION All evaluations shall be conducted on test specimens taken from finished roll goods prior to any subsequent operations, such as reheating or molding. 3.3 APPEARANCE (FLTM BI 109-01) The color, pattern, and finish shall match the approved Design Center ma

6、ster sample, or shall be as specified on the engineering drawing. ENGINEERING MATERIAL SPECIFICATION WSS-M3H133-A Page 2 of 3 Copyright 2010, Ford Global Technologies, Inc. 3.4 COMPOSITION (ASTM D 276) Pile Yarn Nylon Primary Foundation Material 100% polyester Pre-coat Polyethylene Back Coat EVA 3.5

7、 METHOD OF DYEING Solution dyed 3.6 CONSTRUCTION 3.6.1 Pile Yarn (ASTM D 1577) 105 - 115 tex t0 (nylon, crimped textured, bulked continuous filament, 1.0 1.5 tex). 3.6.2 Pile Count (ASTM D 5793) Rows 48.0/100 mm min. Stitches 51.0/100 mm min. Rows and stitches per 100 mm shall be based on an average

8、 count on a 254 mm length of carpet. 3.6.3 Foundation Materials Primary (Tufting Foundation) 100% Polyester or 75%/ 25% PET/PA6 *As specified on the Approved Source List. ENGINEERING MATERIAL SPECIFICATION WSS-M3H133-A Page 3 of 3 Copyright 2010, Ford Global Technologies, Inc. 3.6.4 Back coating The

9、 pre-coat shall form a continuous and uniform coating over the back of the carpet so that all pile fibers are covered. The precoat shall be thoroughly melted and shall maintain its ability to lock in the pile fibers in the end-item, molded carpet assembly. The precoat shall thoroughly saturate the b

10、ase of the pile fiber bundles to ensure adequate tuft lock. Penetration of the precoat through to the face shall be controlled to provide the required resistance to abrasion and fiber loss, but precoat shall not be visible on the face of the pile fiber. 3.6.5 Needle Gauge 1.98 mm 3.6.6 Pile Height, max. 6.2 mm (ASTM D 5823) 3.7 WEIGHT, g/m2, min. (ASTM D 5848) Pile Yarn 515 Primary Foundation Material 100 Back Coating 330 3.8 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute