《FORD WSS-M3H105-B5-2013 CARPET POLYESTER NON WOVEN FLAT FELT NEEDLED ONE LAYER SYSTEM 300 G M2 (8 8 oz) NOMINAL TO BE USED WITH FORD WSS-M99P1111-A .pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M3H105-B5-2013 CARPET POLYESTER NON WOVEN FLAT FELT NEEDLED ONE LAYER SYSTEM 300 G M2 (8 8 oz) NOMINAL TO BE USED WITH FORD WSS-M99P1111-A .pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev 00 2013 05 01 Released L. Sinclair, NA Controlled document at www.MATS Copyright 2013, Ford Global Technologies, Inc. Page 1 of 4 CARPET, POLYESTER, NON WOVEN, FLAT FELT, WSS-M3H105-B5 NEEDLED, ONE LAYER SYSTEM 300 G/M2 (8.8 oz) NOMINAL C

2、ARPET, POLYESTER, NON WOVEN, FLAT FELT, WSS-M3H105-B6 NEEDLED, ONE LAYER SYSTEM 850 G/M2 (25 oz) NOMINAL 1. SCOPE The materials defined by these specifications are flat felt, needled, nonwoven carpets of good quality and uniform composition. The carpet face is made with 100% virgin face fiber and ha

3、s no separate backing system since the backing is integrated into the face material. This material has a heathered gray coloration and is not a solid color, color match. 2. APPLICATION The B5 specification was released originally for B car trunk load floor application. The B6 specification was relea

4、sed originally for B car side trim and deck lids. 3. REQUIREMENTS In addition to the requirements listed herein, the end-item floor carpet shall be tested to WSS-M15P32-D and any additional SDS requirements. The details for each of the suppliers specific construction shall be documented in the suppl

5、ement attached and uploaded into the FMD (Ford Materials Database) or scanned data package. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1.1 Vehicle Interior En

6、vironment Quality Materials/Component Performance Requirements Materials used in interior applications must meet the requirements outlined in WSS-M99P2222-D1/ latest. Test data to be provided by the Tier 1 at the appropriate program milestone. 3.2 SAMPLE SELECTION All evaluations shall be conducted

7、on test specimens taken from finished roll goods prior to any subsequent operations, such as reheating or molding. 3.3 APPEARANCE (FLTM BI 109-01) ENGINEERING MATERIAL SPECIFICATION WSS-M3H105-B5/B6 Copyright 2013, Ford Global Technologies, Inc. Page 2 of 4 The color, pattern, and finish shall match

8、 the approved Design Center master sample, or shall be as specified on the engineering drawing. 3.4 COMPOSITION 3.4.1 Face Fiber Virgin Polyester (white / (ASTM D276) black blend) 3.4.2 Binder Fiber coPolyester / (ASTM D276) Polyester Bicomponent (Bico) Note: The composition is a 60% /40% blend betw

9、een the face fibers and binder fibers. 3.5 METHOD OF DYEING Solution 3.6 CONSTRUCTION 3.6.1 Face Fiber 9 and 11 Denier (ASTM D 1244) 3.6.2 Binder Fiber 4 Denier (ASTM D1244) 3.7 THICKNESS* 3.7.1 Thickness (WSS-M3H105-B5) 2.0 +/- 0.2 mm (ISO 1765) 3.7.2 Thickness (WSS-M3H105-B6) 3.0 +/- 0.3 mm (ISO 1

10、765) *Face thickness after molding. 3.8 WEIGHT 3.8.1 Total Weight(B5 suffix) (270-330) g/m2 (ASTM D5848) (7.9 9.7) oz 3.8.2 Total Weight (B6 suffix) (765 935)g/m2 (ASTM D5848) (22.6 27.9) oz 4. GENERAL INFORMATION This information given below is provided for clarification and assistance in meeting t

11、he requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 DRAWING CALL OUT The following shall be called out on the Engineering drawing to correctly designate the approved material. ENGINEERING MATERIAL SPECIFICATION WSS-M3H105-B5/B6 Copyright

12、2013, Ford Global Technologies, Inc. Page 3 of 4 WSS-M3H105-B5 Supplier Name and Product Code (As it appears on the Approved Source Listing) WSS-M15P32-D Or WSS-M3H105-B6 Supplier Name and Product Code (As it appears on the Approved Source Listing) WSS-M15P32-D 5. SUMMARY OF REVISIONS ENGINEERING MA

13、TERIAL SPECIFICATION WSS-M3H105-B5/B6 Copyright 2013, Ford Global Technologies, Inc. Page 4 of 4 Non Woven Carpet Construction Supplement Supplier _Supplier Contact Name_ Number _ Product/ Style Name _ Material Specification _ Performance Specification _ Supplier Product Code _ Manufacturing Locatio

14、n _ Supplier Lab Number _ Supplier Lab Date _ Composition Type Supplier Face Fiber ASTM D276 _ _ Minimum Recycled Content _ % PIR _ % PCR Pre-Coat ASTM D276 _ _ Mass Backing ASTM D276 _ _ Back Coating ASTM D276 _ _ Construction Solution or piece dyed (circle one) Denier (s) _ Face Fiber Thickness IS

15、O 1765 _+/- _ mm Pre Coating Thickness ISO 1765 _+/- _ mm Mass Backing Thickness ISO 1765 _+/- _ mm Back Coating Thickness ISO 1765 _+/- _ mm Mass per Unit Area Weight Face Fiber ASTM D5848 _+/- _ g/m2 Pre Coating ASTM D5848 _+/- _ g/m2 Mass Backing ASTM D5848 _+/- _ g/m2 Back Coating ASTM D5848 _+/- _ g/m2 Materials Engineering Signature _Date _ Comments _ Rolled Goods _ Molded Product _