FORD WSS-M3H105-A14-2017 CARPET POLO PATTERN POLYESTER NON WOVEN RANDOM VELOUR NEEDLED POLYETHYLENE MOLDABLE BACKING 305 g m2 (9 oz) TO BE USED WITH FORD WSS-M99P1111-A .pdf
《FORD WSS-M3H105-A14-2017 CARPET POLO PATTERN POLYESTER NON WOVEN RANDOM VELOUR NEEDLED POLYETHYLENE MOLDABLE BACKING 305 g m2 (9 oz) TO BE USED WITH FORD WSS-M99P1111-A .pdf》由会员分享,可在线阅读,更多相关《FORD WSS-M3H105-A14-2017 CARPET POLO PATTERN POLYESTER NON WOVEN RANDOM VELOUR NEEDLED POLYETHYLENE MOLDABLE BACKING 305 g m2 (9 oz) TO BE USED WITH FORD WSS-M99P1111-A .pdf(4页珍藏版)》请在麦多课文档分享上搜索。
1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev 01 2017 11 28 Revised See Summary of Revisions L. Pollard, NA 2010 02 12 Activated L. Sinclair, NA Controlled document at www.MATS Copyright 2017, Ford Global Technologies, Inc. Page 1 of 4 CARPET, POLO PATTERN, POLYESTER, NON WOVEN, RAND
2、OM VELOUR, WSS-M3H105-A14 NEEDLED, POLYETHYLENE MOLDABLE BACKING 305 g/m2 (9 oz) 1. SCOPE The materials defined by this specification are random velour, needled, non-woven carpets of good quality and uniform composition. The carpet face is made with 100% post industrial fiber 2. APPLICATION This spe
3、cification was originally released for material used as trunk covering and seat back material for D385. 3. REQUIREMENTS 3.1 APPROVED SOURCES This specification requires the use of approved sources. Only the sources identified on the Ford Approved Source List (ASL) can be used when this specification
4、 is listed on the drawing, CAD file, or other documents. The list of approved sources is located within Ford at or available externally through a Ford Materials Engineer. 3.2 CONDITIONING AND TEST CONDITIONS All test values are based on material conditioned for not less than 24 h prior to testing i
5、n a controlled environment of 23 +/- 2 C and 50 +/- 5% relative humidity. Testing of the material should occur in the conditioning environment or soon after removal. 3.3 PERFORMANCE CRITERIA 3.3.1 In addition to the requirements listed herein, the end-item carpet assembly (molded or otherwise fabric
6、ated), shall meet all requirements of the WSS-M15P32-D and WSS-M8P16-B performance specifications and any additional SDS requirements. The details for each of the suppliers specific construction shall be documented in the supplement attached and uploaded into the scanned data package. 3.3.2 Recycled
7、 Content This specification must contain at least 60% recycled content as defined by WRS- M99P42-A2 (Textile Materials, Identification of Recycled Content). 3.4 SAMPLE SELECTION All evaluations shall be conducted on test specimens taken from finished roll goods prior to any subsequent operations, su
8、ch as reheating or molding. 3.5 APPEARANCE The color, pattern, and gloss shall match the approved Corporate Design master sample. ENGINEERING MATERIAL SPECIFICATION WSS-M3H105-A14 Copyright 2017, Ford Global Technologies, Inc. Page 2 of 4 3.6 COMPOSITION (ASTM D 629) Fiber 80% Polyester 20% Low Melt
9、 Polyethylene Binder 3.7 METHOD OF DYEING Solution dyed 3.8 CONSTRUCTION 3.6.1 Fiber Size and Description 5 denier/4 denier (ASTM D 1244) (Polyester/Low Melt Polyethylene Binder) 3.9 THICKNESS* 2.5 +/- 0.3 mm (ISO 1765) *Face thickness prior to molding. 3.10 WEIGHT 3.10.1 Face Fiber 214-274 g/m2 (AS
10、TM D5848) (6.3 8.1) oz 4. GENERAL INFORMATION This information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 DRAWING CALL OUT The following shall be called out on
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- FORDWSSM3H105A142017CARPETPOLOPATTERNPOLYESTERNONWOVENRANDOMVELOURNEEDLEDPOLYETHYLENEMOLDABLEBACKING305GM29OZTOBEUSEDWITHFORDWSSM99P1111APDF

链接地址:http://www.mydoc123.com/p-753264.html