FORD WSS-M2D512-A-2016 THERMOPLASTIC ELASTOMER (TPS) STYRENE BLOCK COPOLYMER WITH SILOXANE 45 48 NOMINAL DUROMETER A HARDNESS INTERIOR TO BE USED WITH FORD WSS-M99P1111-A .pdf

《FORD WSS-M2D512-A-2016 THERMOPLASTIC ELASTOMER (TPS) STYRENE BLOCK COPOLYMER WITH SILOXANE 45 48 NOMINAL DUROMETER A HARDNESS INTERIOR TO BE USED WITH FORD WSS-M99P1111-A .pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M2D512-A-2016 THERMOPLASTIC ELASTOMER (TPS) STYRENE BLOCK COPOLYMER WITH SILOXANE 45 48 NOMINAL DUROMETER A HARDNESS INTERIOR TO BE USED WITH FORD WSS-M99P1111-A .pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 1 2016 08 31 N Status No usage or replacement L. Sinclair, NA 2009 05 21 Activated B. Curtiss, NA Copyright 2016, Ford Global Technologies, LLC Page 1 of 3 THERMOPLASTIC ELASTOMER (TPS) WSS-M2D512-A STYRENE BLOCK COPOLYMER WITH SILOXANE,

2、 45/48 NOMINAL DUROMETER A HARDNESS, INTERIOR NOT TO BE USED FOR NEW DESIGN 1. SCOPE The materials defined by this specification are colored and U.V. stabilized thermoplastic elastomers based on styrene block copolymers (TPS) with polydimethyl siloxane (PDMS) to reduce the coefficient of friction fo

3、r interior use of nominal 15 sec Durometer A hardness of 45 or 48, having good long term resistance to heat at temperatures up to 110 C. 2. APPLICATION This specification was released originally for materials used for interior shift boots which are black or color keyed. The materials can be processe

4、d by conventional thermoplastics molding techniques such as injection molding, extrusion and blow-molding. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P111

5、1-A). 3.2 DYNAMIC MECHANICAL ANALYSIS (ASTM D 4065) Ford Motor Company, at its option, may establish shear modulus/damping vs. temperature curves plotted for -50 to +170 C temperature range for material/parts supplied to this specification. The shear modulus and damping curves established for initia

6、l approval shall constitute the reference standard and shall be kept on file at the designated material laboratory. All samples shall produce shear modulus and damping curves that correspond to the reference standard when tested under the same conditions. 3.3 PREPARATION OF TEST SPECIMENS Unless oth

7、erwise specified, all tests shall be conducted on specimens die cut from injection molded plaques 150 x 100 x 2.0 +/- 0.2 mm. The plaques shall be molded according to ISO 294 and film gated along the upper 100 mm edge, and preceded by a 0.8 mm diameter pin gate. No annealing allowed, unless specifie

8、d otherwise. 3.4 FINISHED PART REQUIREMENTS The finished part must conform to the requirements of the appropriate performance specification and/or the relevant System Design Specifications (SDS). ENGINEERING MATERIAL SPECIFICATION WSS-M2D512-A Copyright 2016, Ford Global Technologies, LLC Page 2 of

9、3 3.5 DENSITY 0.85 0.95 g/cm3 (ISO 1183, Method A / ASTM D 792, Method A1) 3.6 HARDNESS, DUROMETER A (ISO 868, after 15 sec.) Hardness, Generic Black 45 +/- 5 Hardness, JA6A Color Matched 48 +/- 5 Note: Hardness and tolerance must be noted on the engineering drawing. 3.7 TENSILE STRENGTH 3 MPa min (

10、ISO 37/ASTM D 412, Die C, 500 mm/min test speed. Measured Parallel to Flow) 3.7.1 Elongation at Break 450% min 3.8 TENSILE MODULUS AT 100% ELONGATION 0.8 MPa min (Test per para 3.7) 3.9 TEAR STRENGTH (ISO 34, Method B, Procedure A / ASTM D 624, Die C) 3.9.1 Parallel to Flow 16 kN/m min 3.9.2 Perpend

11、icular to Flow 16 kN/m min 3.10 COMPRESSION SET (ISO 815, Large Type plied specimen / ASTM D 395, Method B, Type 1 plied specimen) 3.10.1 72 h at 23 +/- 1 C 35% max 3.10.2 24 h at 70 +/- 2 C 55% max 3.11 BRITTLENESS POINT -50 C max (ISO 812, Type B specimen / ASTM D 2137, Method A) 3.12 OZONE RESIST

12、ANCE Rating 0 max (FLTM BP 101-01, Method A at 20% elongation) 3.13 HEAT AGED (ISO 188/ASTM D 573, 150 +/- 50 air changes/h, 1000 h at 110 +/- 2 C) (Note: Unaged property values shall be determined at the time of the aged properties determination.) Hardness Change + 5 pts max Tensile Strength Change

13、 +/- 25% max Elongation Change +/ -25% max ENGINEERING MATERIAL SPECIFICATION WSS-M2D512-A Copyright 2016, Ford Global Technologies, LLC Page 3 of 3 3.14 FOGGING (SAE J1756, 3 h at 100 C heating, 21 C cooling plate, post test conditioning 1 h and 16 h) Fog Number 70 min Formation of clear film, drop

14、lets or crystals is cause for rejection. 3.15 ODOR (SAE J1351 / FLTM BO 131-03) Rating 3 max 3.16 FLAMMABILITY, BURN RATE 100 mm/minute max (ISO 3795 / FMVSS 302) The specimen size required for material approval is 355 x 100 x 2.0 +/- 0.1 mm with a smooth surface. 3.17 WEATHERING RESISTANCE Rating 4 max (FLTM BO 116-01, 225.6 kJ/m2 exposure min ISO 105 A-02 / AATCC Evaluation Procedure 1 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 RECYCLING CODE TPS-SEBS + PDMS