FORD WSS-M1H831-A-2008 FABRIC LINKS PATTERN WOVEN TO BE USED WITH FORD WSS-M99P1111-A 《沙丘图案的机织织物 与标准FORD WSS-M99P1111-A一起使用 》.pdf

《FORD WSS-M1H831-A-2008 FABRIC LINKS PATTERN WOVEN TO BE USED WITH FORD WSS-M99P1111-A 《沙丘图案的机织织物 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M1H831-A-2008 FABRIC LINKS PATTERN WOVEN TO BE USED WITH FORD WSS-M99P1111-A 《沙丘图案的机织织物 与标准FORD WSS-M99P1111-A一起使用 》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2008 12 17 N-STATUS No Replacement B. Haggart, FNA 2003 04 28 Revised Rev para 3.5 M. Dumitrescu 2000 04 04 Activated M. Dumitrescu Printed copies are uncontrolled Page 1 of 2 Copyright 2008, Ford Global Tec

2、hnologies, Inc. FABRIC, LINKS PATTERN, WOVEN WSS-M1H831-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a Dobby Rapier pattern flat woven body cloth of good quality and uniform composition. 2. APPLICATION This specification was released originally for material

3、used as an interior trim fabric for 2002 F-SERIES Insert the fabric used is backcoated and laminated. 3. REQUIREMENTS In addition, to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. The fabric must be backcoated. 3.0 STANDARD REQUIREMENTS FOR

4、PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 FABRIC CONSTRUCTION 3.4.1 Fabric Count, +/- 5% tolerance (ASTM D 3775) Warp 190 ends/10 cm Fill 190 picks/10 cm 3.4.2 Fabric Weight, range, g/m

5、2(FLTM BN 106-01) Laminated * Face with Backcoat 425 - 495 326 - 395 * At 3 mm thickness ENGINEERING MATERIAL SPECIFICATION WSS-M1H831-A Page 2 of 2 Copyright 2008, Ford Global Technologies, Inc. 3.5 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 100% Polyester Backcoating

6、 PVC Latex 3.6 YARN CONSTRUCTION (ASTM D 1244) Warp (A) 80.6 tex, f192, (natural, texturized) (B) 80.6 tex, f136, (texturized) Fill (C) 80.6 tex, f192, (natural, texturized) (D) 80.6 tex, f136, (texturized) 3.7 METHOD OF DYEING A, C Piece dyed B, D, Solution dyed 3.8 FINISHING OPERATIONS Dye, Dry, B

7、ackcoat, laminate 3.9 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute Note: Not required on face fabric when used as a fully bonded composite. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 Purchase departments will ensure that both materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only.