FORD WSS-M1H1199-A-2009 FABRIC DOT-COM PATTERN FLAT WOVEN 25% MINIMUM PIR CONTENT TO BE USED WITH FORD WSS-M99P1111-A 《DOT-COM图案的工业使用后材料比例不低于25%的平织织物 与标准FORD WSS-M99P1111-A一起使用 .pdf

《FORD WSS-M1H1199-A-2009 FABRIC DOT-COM PATTERN FLAT WOVEN 25% MINIMUM PIR CONTENT TO BE USED WITH FORD WSS-M99P1111-A 《DOT-COM图案的工业使用后材料比例不低于25%的平织织物 与标准FORD WSS-M99P1111-A一起使用 .pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M1H1199-A-2009 FABRIC DOT-COM PATTERN FLAT WOVEN 25% MINIMUM PIR CONTENT TO BE USED WITH FORD WSS-M99P1111-A 《DOT-COM图案的工业使用后材料比例不低于25%的平织织物 与标准FORD WSS-M99P1111-A一起使用 .pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions Rev. 0 2009 01 07 Activated M. Dumitrescu, FNA Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 1 of 2 FABRIC, DOT-COM PATTERN, FLAT WOVEN WSS-M1H1199-A 25% MINIMUM PIR CONTENT 1. SCOPE The material defined by

2、 this specification is a Dot-Com pattern, Dobby, flat woven bodycloth of good quality and uniform composition. The fabric has min 25% PIR (Post Industrial Recycled yarn) content and it is backcoated. 2. APPLICATION This specification was released originally for material used as a seat fabric, bolste

3、r application for 2011 P473 F-250/350/450 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of: WSS-M8P18-A1/A4. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirem

4、ents for Production Materials (WSS-M99P1111-A) 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3775) Warp 330 ends/10 cm Fill 165 picks/10 cm 3.2.2 Fabric Weight, +/- 5% tolerance (FLTM BN 106-01) Face Fabric w/backcoat 340 g/m2 Backcoat 35 g/m23.3 COMPOSITION (ASTM D 629) Toler

5、ance as specified in WSS-M8P18-A1/A4. Fabric 100% Polyester Backcoating Acrylic ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1199-A Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 65 tex f192 (air texture polyester) x 1 F

6、ill 85 tex f192 (air texture 100% PIR polyester yarn) x 1 83 tex f192 (air texture polyester) x 1 3.5 METHOD OF DYEING Solution dye/yarn-package dye 3.6 FINISHING OPERATIONS Warping, weaving, backcoated, heat set 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase department will ensure that the material defined in this specification and shipped to any one assembly plant will be produced by one supplier only.