《FORD WSS-M1C147-C-2012 GREASE LITHIUM SOAP MINERAL OIL SOLID LUBRICANTS AXLE TO BE USED WITH FORD WSS-M99P1111-A 《锂皂矿物油固体润滑剂车轴润滑脂 与福特WSS-M99P1111-A 一起使用》.pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M1C147-C-2012 GREASE LITHIUM SOAP MINERAL OIL SOLID LUBRICANTS AXLE TO BE USED WITH FORD WSS-M99P1111-A 《锂皂矿物油固体润滑剂车轴润滑脂 与福特WSS-M99P1111-A 一起使用》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 0 2012 02 15 Released A. Wedepohl/C. Ved, NA Controlled document at www.MATS Copyright 2012, Ford Global Technologies, LLC Page 1 of 2 GREASE, LITHIUM SOAP, MINERAL OIL, SOLID LUBRICANTS, AXLE WSS-M1C147-C 1. SCOPE The material defined b

2、y this specification is grease consisting of mineral oil, lithium soap thickener, extreme pressure additives, and solid lubricants. NLGI grade 2. 2. APPLICATION This specification was released originally to lubricate ring and pinion gears for the NVH check prior to assembly into axle. Recommended op

3、erating range is -30C to 130C. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 COLOR Black (Visual) 3.3 WORKED PENETRATION, tenths of a millimete

4、r 265 295 (ASTM D217, DIN ISO 2137, 60 stroke) 3.4 DROPPING POINT 175 C min (ASTM D556, ASTM D2265, DIN ISO 2176) 4. GENERAL INFORMATION This information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engi

5、neering Material Specifications. Grease approved to this specification should have the following typical properties. 4.1 BASE OIL VISCOSITY at 40C 114 mm2/s (ASTM D445, DIN 51562, ISO 3104) 4.2 PENETRATION (ASTM D217, DIN ISO 2137) 4.2.1 Worked Penetration, 60 strokes 265 295 4.2.2 Prolonged Worked

6、Penetration, 100,000 strokes 272 ENGINEERING MATERIAL SPECIFICATION WSS-M1C147-C Copyright 2012 Ford Global Technologies, LLC Page 2 of 2 4.3 LOAD CARRYING PROPERTIES 4.3.1 4-Ball EP Weld Point 3600 N (ASTM D2596, DIN 51350 T4) 4.3.2 Ball Wear Test, Wear Scar dia. 0.8 mm (ASTM D 2266, DIN 51350 T5 8

7、00N) 4.3.3 Almen-Weiland OK load 15,500 N (DIN 51350 T5) 4.3.4 Friction Force with OK load 3,150 N (DIN 51350 T5) 4.4 OXIDATION STABILITY (ASTM D942 or DIN 51808, 100hr at 99C) 10 kPa 4.5 CORROSION PROTECTION 0 (DIN 51802, SKF-Emcor) 4.6 WATER WASHOUT 3 - 4% (ASTM D1264, DIN 51807 T02, 1 hr at 79C)

8、4.7 OIL SEPARATION DURING STORAGE 0% (ASTM D1742, DIN 51817 or FTMS 791 C 321.3) 4.8 OIL SEPARATION 3.8% (DIN 51817, 7 days at 40C) 4.9 LOW TEMPERATURE TORQUE (ASTM D1478 or IP 186) -20 C start 151 Nm -20 C running after 20 minutes 59 Nm 4.10 INTERFACE COMPATIBILITY 4.10.1 Chemical Attack to Painted

9、 Surfaces (FLTM BJ 126-01). Note: Not tested for initial application of this grease. Grease must be tested for chemical attack to painted surfaces for applications that come in contact with paint surfaces, ex. E-coat and powder coat. 4.10.2 Resistance to Stress Cracking (FLTM BO 127-03) Note: Not te

10、sted for initial application of this grease. Grease must be tested for resistance to stress cracking when used for additional applications that come in contact with polymers such as PC, ABS, PC+ABS, ASA or acrylic 4.10.3 Elastomer Compatibility, (ASTM D 4289, 70 h, 100 C, DIN 53505, DIN 53504) Note: Not tested for initial application of this grease. Grease must be tested for elastomer compatibility when used for additional applications that come in contact with elastomers. Application specific elastomer should be used for testing instead of a reference elastomer.