1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2004 10 28 Revised Added A2, revised title on A1 and para 2.0 C. Bezant 2004 05 27 Activated C. Bezant Printed copies are uncontrolled Copyright 2004, Ford Global Technologies, LLC Page 1 of 1 POLYESTER WOOD STOPPER/FILLER WSS-M11G36-A POLYEST

2、ER WOOD STOPPER/FILLER HARDENER WSS-M11G36-A2 1. SCOPE The materials defined by these specifications are polyester stoppers/fillers and the associated polyester hardener. They are suitable for filling cracks in wood veneer surfaces prior to finishing with a polyester lacquer. 2. APPLICATION These sp

3、ecifications WSS-M11G36-A/A2 were released for materials used for wooden decorative automotive components. 3. REQUIREMENTS Material specification requirements are to be used for initial qualification of materials. When in the fully assembled form the veneer assembly must perform to the Material spec

4、ification requirements of WSS-M15P34-B1 or as specified on the engineering drawing. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 MATERIAL PROPERTIES 3.2.1 Col

5、or Assembly to be as per Master samples 3.2.2 Drying/Curing, at 20 - 23 C Recoating 4 - 5 Hours Min 3.2.3 Shelf life When stored between 20 - 23 C WSS-M11G36-A 3 Months WSS-M11G36-A2 6 Months 3.2.4 Pot life When stored at 20 C WSS-M11G36-A 6 - 8 Min 3.2.5 Handling 20 - 23 C 3.2.6 Mixing ratio 100 parts by weight putty to 3 parts by weight hardener paste 3.3 PERFORMANCE PROPERTIES The material shall be of uniform quality, free from foreign materials and properties detrimental to normal production use.