FORD WSD-M1H563-F1-2008 FABRIC COLOMBO PATTERN KNITTED 3 mm PU - TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSD-M1H563-A)《科伦坡(COLOMBO)图案的3 mm PU针织织物 与标准FORD WSS-M99P1111.pdf

《FORD WSD-M1H563-F1-2008 FABRIC COLOMBO PATTERN KNITTED 3 mm PU - TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSD-M1H563-A)《科伦坡(COLOMBO)图案的3 mm PU针织织物 与标准FORD WSS-M99P1111.pdf》由会员分享，可在线阅读，更多相关《FORD WSD-M1H563-F1-2008 FABRIC COLOMBO PATTERN KNITTED 3 mm PU - TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSD-M1H563-A)《科伦坡(COLOMBO)图案的3 mm PU针织织物 与标准FORD WSS-M99P1111.pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 11 06 N-STATUS No Replacement L. Schmalz, FNA / M. Montgomery, FOE 2007 08 10 Revised WSD-M1H563-B1 inactivated and removed, no replacement named; Revised 2, 3.141, 3.14.3 & 3.14.4 S. Kornylo 1992 04 16 Released C10206048 Printed copies a

2、re uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 1 of 6 FABRIC, COLOMBO PATTERN, KNITTED, UNLAMINATED WSD-M1H563-A FABRIC, COLOMBO PATTERN, KNITTED, 6 mm WSD-M1H563-B2 FABRIC, COLOMBO PATTERN, KNITTED, 15 mm WSD-M1H563-B5 FABRIC, COLOMBO PATTERN, KNITTED, 3 mm WSD-M1H563-C1 FABRIC,

3、 COLOMBO PATTERN, KNITTED, 6 mm WSD-M1H563-C2 FABRIC, COLOMBO PATTERN, KNITTED, 15 mm WSD-M1H563-C5 FABRIC, COLOMBO PATTERN, KNITTED, 6 mm WSD-M1H563-D2 FABRIC, COLOMBO PATTERN, KNITTED, 3 mm PU WSD-M1H563-F1 FABRIC, COLOMBO PATTERN, KNITTED, 6 mm PU WSD-M1H563-F2 FABRIC, COLOMBO PATTERN. KNITTED, H

4、FW WSD-M1H563-G FABRIC, COLOMBO PATTERN, KNITTED, HFW WSD-M1H563-H FABRIC, COLOMBO PATTERN, KNITTED, HFW WSD-M1H563-J FABRIC, COLOMBO PATTERN, KNITTED, HFW WSD-M1H563-K NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by these specifications is a 6 bar 44 gauge DBR knitted, simulated velo

5、ur, polyester bodycloth. 2. APPLICATION These specifications were released originally for material used as an interior trim polyester fabric for the CDW27 program. The face fabric is flame laminated to polyester or polyether urethane foam and a knitted fabric or polyurethane film backing for seating

6、 applications. The face fabric is flame laminated to polyether foam alone for inner door and quarter trim panel applications. The face fabric is supplied unlaminated for seat piping applications. It can be backed with HFW weldable backcoating. COLOMBO PATTERN WSD-M1H563-A Unlaminated WSD-M1H563-B2 6

7、.0 mm, flame laminated to polyether foam and knitted fabric WSD-M1H563-B5 15.0 mm, flame laminated to polyether foam and knitted fabric ENGINEERING MATERIAL SPECIFICATIONWSD-M1H563-A/B2/B5/C1/ C2/C5/D2/F1/F2/G/H/I/J/K Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page

8、 2 of 6 WSD-M1H563-C1 3.0 mm, flame laminated to polyester foam and knitted fabric (EAO use only) WSD-M1H563-C2 6.0 mm, flame laminated to polyester foam and knitted fabric (EAO use only) WSD-M1H563-C5 15.0 mm, flame laminated to polyester foam and knitted fabric (EAO use only) WSD-M1H563-D2 6.0 mm,

9、 flame laminated to polyether foam WSD-M1H563-F1 3.0 mm flame laminated to polyester foam and polyurethane film (EAO use only) WSD-M1H563-F2 6.0 mm flame laminated to polyester foam and polyurethane film (EAO use only) WSD-M1H563-G HF weldable vinyl film adhesive bonded or an engineering approved al

10、ternative WSD-M1H563-H HF weldable acrylic backcoating applied by the doctor-knife spreading technique, or an engineering approved alternative WSD-M1H563-J HF weldable vinyl backcoating applied by the doctor-knife spreading technique, or an engineering approved alternative WSD-M1H563-K HF weldable P

11、U backcoating applied by the doctor-knife spreading technique, or an engineering approved alternative 3. REQUIREMENTS In addition to the requirements listed herein, the fabric or laminate shall meet all requirements of WSS-M8P18-A1/A4. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material supp

12、liers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 FABRIC CONSTRUCTION 3.4.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Wales 90 wales/10 cm Courses 110 courses/10 cm 3.4.2 Fabric Weight, range 280 - 320 g/m2(FLTM BN 106-01) 3

13、.4.3 Pile Height, min 1.7 mm (Microscope technique) 3.5 COMPOSITION (ASTM D 629) Fabric 100% polyester ENGINEERING MATERIAL SPECIFICATIONWSD-M1H563-A/B2/B5/C1/ C2/C5/D2/F1/F2/G/H/I/J/K Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 3 of 6 3.6 YARN CONSTRUCTION (AS

14、TM D 1244) No. 1 Bar 100 dtex f20, (polyester, spun dyed grey, texturized) No. 2 Bar 100 dtex f40, (polyester, semi-dull) No. 3 Bar 270 dtex f64-72, (polyester, bright) No. 4 Bar 270 dtex f64-72, (polyester, bright) No. 5 Bar 100 dtex f40, (polyester, semi-dull) No. 6 Bar 100 dtex f20, (polyester, s

15、pun dyed grey, texturized) 3.7 METHOD OF DYEING Yarn dyed and space dyed or as approved by Materials Engineering 3.8 FINISHING OPERATIONS As approved by Materials Engineering 3.9 REQUIREMENTS FOR POLYETHER FOAM As specified in WSD-M2D243-A2 3.10 REQUIREMENTS FOR POLYESTER FOAM As specified in SK-M4D

16、9502-A 3.11 REQUIREMENTS FOR THE BACKING As specified in WSD-M9H111-B FABRIC (B1, B2, B5) 3.12 REQUIREMENTS FOR THE BACKING As specified in WSD-M9H136-A FABRIC (C1, C2, C5) 3.13 REQUIREMENTS FOR THE As specified in ESD-M99H134-A POLYURETHANE BACKING FILM 3.14 REQUIREMENTS FOR THE FLAME LAMINATED MAT

17、ERIAL 3.14.1 Thickness, range (ASTM D 1777, circular presser foot area 645 mm2, 2.8 g force, 43 Pa pressure) WSD-M1H563-B2 6.5 +/- 1.0 mm WSD-M1H563-B5 15.0 +/- 1.0 mm WSD-M1H563-C1 3.0 +/- 1.0 mm WSD-M1H563-C2 6.0 +/- 1.0 mm WSD-M1H563-C5 15.0 +/- 1.0 mm WSD-M1H563-D2 7.0 +/- 1.0 mm WSD-M1H563-F1 4

18、.0 +/- 1.0 mm WSD-M1H563-F2 6.75 +/- 1.0 mm 3.14.2 Compressed Thickness (1 kg Force, circular presser foot area 645 mm2, 5 s dwell) WSD-M1H563-D2 2.8 +/- 0.3 mm WSD-M1H563-F1 1.8 +/- 0.3 mm WSD-M1H562-F2 2.8 +/- 0.3 mm ENGINEERING MATERIAL SPECIFICATIONWSD-M1H563-A/B2/B5/C1/ C2/C5/D2/F1/F2/G/H/I/J/K

19、 Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 4 of 6 3.14.3 Weight, min (FLTM BN 106-01) WSD-M1H563-B2 560 +/- 50 g/m2WSD-M1H563-B5 900 +/- 50 g/m2WSD-M1H563-C1 440 +/- 50 g/m2WSD-M1H563-C2 540 +/- 50 g/m2WSD-M1H563-C5 780 +/- 50 g/m2WSD-M1H563-D2 550 +/- 50 g/m

20、2WSD-M1H563-F1 440 +/- 50 g/m2WSD-M1H563-F2 540 +/- 50 g/m23.14.4 Stretch and Set, %, range (SAE J855) Stretch (WSD-M1H563-B2, B5, C1, C2, C5) . Wales 0 - 15 . Courses 5 - 25 Stretch (WSD-M1H563-F1, F2) . Wales 3 - 19 . Course 8 - 24 Set (WSD-M1H563-B2, B5, C1, C2, C5, F1, F2) . Wales 0 -5 . Courses

21、 0 - 5 3.14.5 Modulus, max (WSD-M1H563-F1, F2, D2) Strain, 6 % . Wales 100 N . = Courses 85 N 3.15 REQUIREMENTS FOR THE BACKCOATED MATERIAL (WSD-M1H563-G) 3.15.1 Weight, min (FLTM BN 106-01) PVC film 100 g/m2Face fabric weight as specified in para 3.4.2 Or an engineering approved alternative. ENGINE

22、ERING MATERIAL SPECIFICATIONWSD-M1H563-A/B2/B5/C1/ C2/C5/D2/F1/F2/G/H/I/J/K Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 5 of 6 3.16 REQUIREMENTS FOR THE BACKCOATED MATERIAL (WSD-M1H563-H) 3.16.1 Weight, min (FLTM BN 106-01) Acrylic Backcoating 35 g/m2Face fabri

23、c weight as specified in para 3.4.2 Or an engineering approved alternative. 3.17 REQUIREMENTS FOR THE BACKCOATED MATERIAL (WSD-M1H563-J) 3.17.1 Weight, min (FLTM BN 106-01) PVC Backcoating 40 g/m2Face fabric weight as specified in para 3.4.2 Or an engineering approved alternative. 3.18 REQUIREMENTS

24、FOR THE BACKCOATED MATERIAL (WSD-M1H563-K) 3.18.1 Weight, min (FLTM BN 106-01) Polyurethane Backcoating 40 g/m2Face fabric weight as specified in para 3.4.2 Or an engineering approved alternative. 3.19 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute Note: Not required on face fabric wh

25、en used as a fully bonded composite ENGINEERING MATERIAL SPECIFICATIONWSD-M1H563-A/B2/B5/C1/ C2/C5/D2/F1/F2/G/H/I/J/K Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 6 of 6 3.20 REQUIREMENTS FOR THE FULLY BONDED DOOR PANELS The fully bonded finished component must

26、satisfy the requirements of engineering component specification S-77FBB-23942-AA or equivalent if specified on the engineering drawing. In addition to these requirements, fabric general performance should not be reduced by the bonding process. Ford Motor Company at its discretion may perform test on

27、 the finished components to verify this. Minimum bond strengths will be specified which may vary according to the method of bonding employed. 3.20.1 Peel Adhesion Strength, min (FLTM BN 151-05) Fabric Press Formed To Adhesive Coated Board As Received 20 N/50 mm width After Ageing 20 N/50 mm width (4

28、 h at 100 +/- 2 C, 20 h at 40 +/- 2 C and 98 +/- 2 % relative humidity) 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of these specifications. 4.1 Purchase Departments will ensure that both materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only.