《FORD WSB-M3G221-A-2006 TAPE ADHESIVE PRESSURE SENSITIVE TWO SIDED ACRYLIC MEDIUM TACK INTERIOR TO BE USED WITH FORD WSS-M99P1111-A 《车内用中等粘性丙烯酸系树脂双面涂布压敏粘合胶带 与标准FORD WSS-M99P1111-.pdf》由会员分享，可在线阅读，更多相关《FORD WSB-M3G221-A-2006 TAPE ADHESIVE PRESSURE SENSITIVE TWO SIDED ACRYLIC MEDIUM TACK INTERIOR TO BE USED WITH FORD WSS-M99P1111-A 《车内用中等粘性丙烯酸系树脂双面涂布压敏粘合胶带 与标准FORD WSS-M99P1111-.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 02 15 Revised Inserted 3.0; Deleted 3.1, 3.2, 3.3, 3.12, 3.13, 3.14, 4 1994 11 17 Released NBOOI10043054396 AWB KPM Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 3 TAPE, ADHESIVE, PRESSURE SENSITI

2、VE, TWO SIDED, WSB-M3G221-A ACRYLIC, MEDIUM TACK, INTERIOR 1. SCOPE The material defined by this specification is a two sided acrylic based pressure sensitive adhesive film with a medium to firm tack. One side is protected by a release liner. 2. APPLICATION This specification was released originally

3、 for material to bond flexible (PVC) foam to interior trim substrates. Prior to approval for other applications, the performance of the tape must be verified on the intended substrates to the requirements of the specifications and requirements defined in any associated component or assembly specific

4、ations. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 GREEN STRENGTH The tape shall develop sufficient adhesion to permit normal handling immed

5、iately after application. 3.5 MATERIAL PROPERTIES 3.5.1 Color Clear 3.5.2 Tape Dimension As specified on engineering drawing 3.5.3 Tape Thickness (ASTM D 1000) Adhesive 0.13 +/- 0.03 mm Release Liner, nominal 0.10 mm 3.6 LINER REMOVAL, max 25 N/m (ASTM D 1000, Method A) 3.7 PREPARATION OF TEST SPECI

6、MENS Steel panels, painted with current production enamel according to respective paint specification if not otherwise specified. ENGINEERING MATERIAL SPECIFICATIONWSB-M3G221-APrinted copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 3 Apply the tape per the following p

7、rocedure. Clean test panels with a 50/50 blend (volume) of isopropyl alcohol and water and allow to air dry. Peel the liner from the film in a smooth continuous motion. Do not peel the film from the liner. Position the tape on the test substrate. Using the roller described in ASTM D 1000 with no add

8、itional pressure, pass the roller over the full length of the tape once in each direction. Test samples with applied tape shall be conditioned for 48 h at 23 +/- 2 C and 50% relative humidity prior to exposure. Tests shall be completed within 4 h after removal from the conditioning environment unles

9、s otherwise specified. 3.8 ADHESION PROPERTIES (ASTM D 1000) To minimize elongation during testing, apply aluminum foil or polyester film of about 50 micrometer thickness to the reverse side of the tape. 3.8.1 Peel Adhesion (ASTM D 1000) 1 h at 23 +/- 2 C 400 N/m 3.8.2 Heat Resistance 500 N/m (7 d a

10、t 100 +/- 2 C) 3.8.3 Humidity Resistance 500 N/m (7 d at 38 +/- 2 C, 95 - 100% relative humidity) 3.8.4 Environmental Cycle Resistance 500 N/m 5 cycles, each cycle consisting of the following: 4 h at 90 +/- 2 C 4 h at 38 +/- 2 C and 95 - 100% relative humidity 16 h at -30 +/- 2 C 3.8.5 Heat Resistan

11、ce 500 N/m (30 minutes at 120 +/- 2 C) 3.9 FOGGING (FLTM BO 116-03, 3 h at 100 C heating, 21 C cooling plate) Fog Number, min 60 Formation of a clear film, droplets or crystals is cause for rejection. Perform the test with the tape bonded to aluminum foil with the release liner removed. ENGINEERING

12、MATERIAL SPECIFICATIONWSB-M3G221-APrinted copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 3 of 3 3.10 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute Perform the test with the tape bonded to aluminum foil with the release liner removed. 3.11 ODOR, max Rating

13、2 (FLTM BO 131-01/SAE J1351) Perform the test with the tape bonded to aluminum foil with the release liner removed. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 STORAGE STABILITY 12 months (From

14、 date of receipt at Ford Motor Company) 5.2 STORAGE TEMPERATURE (Range) 10 - 28 C 5.3 STORAGE HUMIDITY (Range) 20 - 80% RH 5.4 For information on currently approved fluids used in para 3.6 of this specification contact: Materials Laboratory 13/100 Fluids Materials Section Research & Engineering Center Coolants/Greases Ford Motor Company Ltd. Engine Engineering Laindon, Basildon P.O. Box 2053 Essex SS15 6EE, England 21500 Oakwood Blvd. Dearborn, MI 48121 U.S.A. Materials Engineering Product Engineering Office Ford Motor Co. of Australia Ltd. Princes Highway, Norlane Victoria 3214, Australia