FORD WSB-M2G234-C-2007 PRIMER METAL FOR ONE COMPONENT FASTER MOISTURE CURING URETHANE ADHESIVE TO BE USED WITH FORD WSS-M99P1111-A 《单组分快速湿固化氨基甲酸酯胶粘剂用金属底漆 与标准FORD WSS-M99P1111-A一.pdf

《FORD WSB-M2G234-C-2007 PRIMER METAL FOR ONE COMPONENT FASTER MOISTURE CURING URETHANE ADHESIVE TO BE USED WITH FORD WSS-M99P1111-A 《单组分快速湿固化氨基甲酸酯胶粘剂用金属底漆 与标准FORD WSS-M99P1111-A一.pdf》由会员分享，可在线阅读，更多相关《FORD WSB-M2G234-C-2007 PRIMER METAL FOR ONE COMPONENT FASTER MOISTURE CURING URETHANE ADHESIVE TO BE USED WITH FORD WSS-M99P1111-A 《单组分快速湿固化氨基甲酸酯胶粘剂用金属底漆 与标准FORD WSS-M99P1111-A一.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2007 04 19 Revised Inserted 2.1, Table 1 Revised 2., 3.15 Para 3.1, 3.2, 3.3, 3.21, 3.22, 4 deleted 1990 03 21 Released NB00E00179051000 K. King, E. Rezendes, M. Perchard Printed copies are uncontrolled Copyright 2007, Ford Global Technologies

2、, LLC Page 1 of 8 PRIMER, METAL, FOR ONE COMPONENT FASTER WSB-M2G234-C MOISTURE CURING URETHANE ADHESIVE PRIMER, METAL, FOR ONE COMPONENT FASTER WSB-M2G234-C2 MOISTURE CURING URETHANE ADHESIVE - SILANE BASED CLEARCOAT CHEMISTRIES ONLY PRIMER, METAL, FOR ONE COMPONENT FASTER WSB-M2G234-C3 1. SCOPE Th

3、e material defined by these specifications are highly reactive moisture sensitive solvent/resin blend adhesion promoting primers. 2. APPLICATION These specifications were originally released for priming the metal flange of the vehicle openings (windshields, backlites, and side) in preparation for on

4、e component urethane adhesives; i.e. WSB-M2G316-B, and WSS-M2G316-B2/B3/B4/B5. The primer is referred to as Adhesion Primer Painted Metal in the WSB-M2G316-B, and WSS-M2G316-B2/B3/B4/B5 specification. The primer is applied only to painted metal surfaces as approved by the responsible Materials Engin

5、eering Activity. The primer can be manually or robotically brush applied and robotically spray applied. WSB-M2G234-C shall be used in assembly plants with non-silane based clearcoat chemistries. It must not be used with silane based chemistries. WSB-M2G234-C2 shall be used in assembly plants with si

6、lane based clear coat systems only. It must not be used with other paint chemistries. (Reference para 4.8) WSB-M2G234-C3 shall be used in assembly plants where data has shown a compatibility with that plants clearcoat chemistry. (Reference para 4.9). These materials were originally released for some

7、 carbamate paint chemistries (Reference para 4.9). 2.1 MANUFACTURING PROCESS RECOMMENDATION These primers are moisture sensitive and require special handling for manual and automated processes as outlined in Table 1 and Table 2. The process parameters listed in Table 1 and Table 2 cover the critical

8、 elements for these materials and are not all inclusive. Please consult with Materials Engineering for any questions. Approved suppliers are responsible for maintaining the accuracy and relevancy of these process parameters (in their Process Standard). Approved suppliers must submit any changes to t

9、hese process parameters in a timely manner (within 30 days) for review and approval by Materials Engineering. ENGINEERING MATERIAL SPECIFICATION WSB-M2G234-C/C2/C3 Printed copies are uncontrolled Copyright 2007, Ford Global Technologies, LLC Page 2 of 8 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR

10、PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 COLOR Black 3.5 SHEAR ADHESION, min 2.5 MPa 100 % cohesive failure of adhesive on production E-coat and spray primer. Exposure Conditions - Bon

11、ded Test Assemblies: . Normal (fresh materials) test at room temperature, -9 +/- 1 C, and 43 +/- 2 C. . Normal (urethane aged 3 months and primers aged 2 months at 35 +/- 2 C) test at room temperature, -9 +/- 1 C, and 43 +/- 2 C. . Heat Aging 2 weeks (At 88 +/- 2 C) . Water Immersion 240 h (FLTM BI

12、104-01, at 32 +/- 1 C) . Humidity Aging 2 weeks (At 38 +/- 1 C and 98 +/- 2% relative humidity) . Weatherometer 2000 h (SAE J1885) . Florida Exposure 2 years (SAE J1976) . See WSB-M2G316-B/B2, para 4.1, 4.2, 4.3, 4.4. Test Method Exceptions: Lap Shear . Prepare shear assemblies as illustrated in WSB

13、-M2G316-B/B2 Figure 1. . Brush and/or spray apply metal primer on the bottom 6.5 mm of each primed or primed and painted coupon as outlined in WSB-M2G316-B and /B2, Table 1. Condition the applied primer at room temperature for 30 minutes min, 110 h max. . Brush apply glass primer wipe on the bottom

14、6.5 mm of each glass coupon outlined in WSB-M2G316-B/B2 Table 1. Wipe off with a clean cloth 3 to 5 seconds after application. . Within 10 minutes maximum after glass primer wipe off, brush apply glass blackout primer to the glass surface in the same area. Condition primer at room temperature for 5

15、minutes min, 72 h max. ENGINEERING MATERIAL SPECIFICATION WSB-M2G234-C/C2/C3 Printed copies are uncontrolled Copyright 2007, Ford Global Technologies, LLC Page 3 of 8 . Apply a 6.5 mm diameter bead of adhesive along the primed glass coupon surface. Within 5 minutes after adhesive application, positi

16、on the adhesive on the glass coupon in contact with the primed metal surface. Maintain a 5 mm nominal adhesive bondline thickness. . Condition assembly at room temperature for 72 h prior to test or environmental aging. Assemblies tested at -9 C and 43 C shall be maintained at temperature for 2 h min

17、 prior to test. After environmental aging, maintain the assemblies at room temperature for 4 h minimum prior to test. . Determine the adhesion in a tensile machine having a jaw separation rate of 25 mm/ minute. Report strength value and mode of failure. Refer to SAE J1529 for sample fixture and othe

18、r pertinent test information. NOTE: Any new primer must be tested for adhesion properties. Adhesion values and mode of failure shall be reported prior to approval and release for plant application. 3.6 VISCOSITY (FLTM BI 111-01, No. 4 Ford Cup) -C, -C2 -C3 3.6.1 Normal 17 - 30 s 23-50 s 3.6.2 Aged,

19、max 15 s increase 40 s increase (72 h at 50 +/- 1 C over normal over normal Testing should be Conducted, right after the material has been manufactured) -C, -C2 -C3 3.7 SOLIDS, min 30% 35% (ASTM D 2834, except heat at 100 +/- 2 C in a mechanical convection oven for 3 h) 3.8 ODOR The material must no

20、t have a toxic or noxious odor. After curing, the material must be relatively non-odorous. 3.9 ASH CONTENT, BASED ON SOLIDS WEIGHT, max 55% Test Method: Place the crucible containing the solids residue in a cool muffle furnace. Slowly heat to and maintain at 760 +/- 30 C for 1 h. Cool in a desiccato

21、r, weigh, and calculate the ash content. 3.10 WEIGHT PER VOLUME (ASTM D 816) The weight tolerance for any one supplier shall be +/- 0.043 kg/L based on the weight of the original approved production sample (see para 4.3). ENGINEERING MATERIAL SPECIFICATION WSB-M2G234-C/C2/C3 Printed copies are uncon

22、trolled Copyright 2007, Ford Global Technologies, LLC Page 4 of 8 3.11 HIDING POWER The primer when brush and/or spray applied 0.075 mm to 0.130 mm film thickness shall completely blackout a white painted surface. 3.12 BRUSHABILITY/SPRAYABILITY The primer when hand brushed and/or sprayed on white pa

23、inted metal surfaces shall level with no evidence of brush marks, voids, or bare spots to the extent that the painted undersurface is visible. The material under test shall be equal to or better than the current same supplier approved production material for smoothness when applied under identical c

24、onditions. 3.13 DRYING RATE, max WSB-M2G234-C 10 minutes WSB-M2G234-C2 30 minutes WSB-M2G234-C3 10 minutes Test Method: Test apply a hand brushed or sprayed application 0.075 to 0.130 mm film of primer on 25 mm wide to a 75 x 75 mm clean white painted metal panel. To determine the primer drying rate

25、, immediately and at rapid intervals, dab the primer film with a wad of absorbent cotton. Observe if any of the cotton fibers adhere to the primed surface. Record the drying rate, as the time elapsed from the initial primer application until the cotton fibers do not adhere to the primer. Room temper

26、ature condition is required. 3.14 MIGRATION STAINING None (FLTM BU 105-01) Test Method: Expose the painted panel prepared in para 3.13 for a total of 110 h in the Flourescent Sunlamp Cabinet identified in FLTM BU 105-01. 3.15 OPEN TIME The material, upon being applied to the painted metal, shall be

27、dry to the touch prior to urethane ( WSB-M2G316-B) application. The material must have a minimum of 30 minutes dry time prior to urethane ( WSB-M2G316-B) application. Maximum open time shall not exceed 110 h and primer applied surfaces shall be kept free of contamination (e.g. dirt, heavy dust, oils

28、, grease, alcohol, etc.) 3.16 STORAGE STABILITY Shall be stored at ambient room temperature below 35 C, away from all sources of heat such as ovens, direct sunlight etc. The material should not be stored outside. Under these storage conditions, the maximum shelf life of the material in unopened cont

29、ainers shall be six (6) months from date of manufacturer. The supplier must label each container to indicate the expiration date of the material. Material may not be used after the expiration date unless the supplier has given written documentation to Materials Engineering and the affected Manufactu

30、ring Plant that the material conforms to requirements outlined in the material control plan. The supplier shall also indicate in the letter the number of additional days the material will be usable. When stored at temperatures below 23 C, it must be conditioned at 23 +/- 2 C for 48 h prior to use. E

31、NGINEERING MATERIAL SPECIFICATION WSB-M2G234-C/C2/C3 Printed copies are uncontrolled Copyright 2007, Ford Global Technologies, LLC Page 5 of 8 3.17 SENSITIVITY TO ALCOHOL CAUTION: Slight traces of alcohol will inhibit the cure of this adhesive. The use of alcohol or alcohol containing solvents is pr

32、ohibited for cleanup or other uses. 3.18 QUALITY The material shall be a smooth, homogenous mixture free from foreign materials and properties detrimental to normal production operations. 3.19 NON-INTERCHANGEABILITY OF MATERIALS - GLASS BONDING APPLICATIONS ONLY Only approved urethane adhesives and

33、primers from the same production (supplier) source shall be used in conjunction with one another. See related materials for use (para 5.5). 3.20 FUNCTIONAL APPROVAL Materials being evaluated for approval to this specification shall be subjected to a production trial. Functional trial results must be

34、 approved by the affected assembly operation and Design Engineering. Results shall be made available to Materials Engineering prior to material approval and release. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this sp

35、ecification. 5.1 FLASH POINT -7 C (ASTM D 56, Tag closed cup) 5.2 FLAMMABILITY AND/OR TOXICITY This material represents a potential fire and/or health hazard. The Manufacturing Engineering Department shall notify both the Plant Security and the Safety Units of its presence in the Plant to assure tha

36、t proper fire and/or health precautions are provided. The location in which it is used or stored shall be included in the notifications. 5.3 WEIGHT PER VOLUME Materials conforming to this specification and found satisfactory in production, range from 0.90 - 1.20 kg/L. 5.4 MATERIAL HANDLING This prim

37、er is moisture sensitive and dry air or a nitrogen blanket should be utilized in production to preclude contact with atmospheric moisture. This body primer must be agitated prior to use to preclude settling of solids content; agitate a minimum of 30 minutes for brush application and a minimum of 60

38、minutes for spray application. The primer must be agitated by a recirculating system operated at low pressure as required during usage. ENGINEERING MATERIAL SPECIFICATION WSB-M2G234-C/C2/C3 Printed copies are uncontrolled Copyright 2007, Ford Global Technologies, LLC Page 6 of 8 5.5 RELATED MATERIAL

39、S 5.5.1 Glass Primer Wipe - Clear WSB-M5B280-C - Red WSB-M5B280-C2 - Red (non-photochemically reactive) WSB-M5B280-C3 5.5.2 Primer, Glass WSB-M2G314-B 5.5.3 Adhesive, Urethane - WSB-M2G222-B Low Viscosity 5.5.4 Adhesive, Urethane - WSB-M2G316-B High Viscosity WSS-M2G316-B2/B3/B4/B5 5.6 CLEANUP The u

40、ncured material can be satisfactorily removed using Solvent Emulsion Cleaner M5B228-A(F). 5.7 SPRAY EQUIPMENT 5.7.1 When spray applying, the solvent purge solution must not contaminate the primer that is applied to the vehicle. 5.7.2 If in-line heaters are used to raise the temperature of the primer

41、, the temperature must not exceed 30 C. (If 30 C is exceeded, primer could cure in-line causing filter clogging and system failures.) 5.7.3 Selection of airless or air atomized spray equipment must be approved by Vehicle Operations and Advanced Vehicle Technology. 5.8 SILANE BASED PAINT CHEMISTRY Ma

42、terial approved to WSB-M2G234-C2 was originally released for use with DuPont Generation IV Clearcoat. Materials approved to WSB-M2G234-C are compatible with paint systems other than DuPont Generation IV Clearcoat. 5.9 OTHER CLEARCOAT CHEMISTRIES Material(s) approved to WSB-M2G234-C3 was originally r

43、eleased for use with PPG Carbamate chemistry clearcoat. However, materials approved to this specification can potentially be used with other clearcoat technologies. ENGINEERING MATERIAL SPECIFICATION WSB-M2G234-C/C2/C3 Printed copies are uncontrolled Copyright 2007, Ford Global Technologies, LLC Pag

44、e 7 of 8 Table 1 Process Parameters For Manual Application WSB-M2G234-C/C2/C3 Application Agitation Shaker (600 cycles/minute) +/- 30 travel from horizontal. 0.3 or 1.0 L container Primer must be agitated before application: Container must be shaken for 10 minutes prior to initial use. If the sealed

45、 container remains idle for more than 2 hours it must be agitated for 5 minutes prior to filling dispense vessels. Primer must be applied with brush or Felt tipped Polyethylene or Polytetrafluoroethylene squeeze bottles. A continuous 3 to 5 mil (0.08 mm 0.13 mm) wet film without skips or streaks sha

46、ll exist behind the applicator tool. Primer must be applied to the flange a minimum of 30 minutes prior to the application of the urethane adhesive. The time between the application of primer and urethane adhesive must not exceed 110 hours. Open Time In the original container (1L) after opening. Con

47、tainer must be closed after dispensing. Transferred to Squeeze Bottles Must be used within 8 hours. Must be used within 4 hours. Storage Primer must be stored indoors, between 10 C and 35 C to avoid extreme heat or cold. Must not be stored in direct sunlight. ENGINEERING MATERIAL SPECIFICATION WSB-M

48、2G234-C/C2/C3 Printed copies are uncontrolled Copyright 2007, Ford Global Technologies, LLC Page 8 of 8 Table 2 Process Parameters For Automated Application WSB-M2G234-C/C2/C3 Application Agitation 5 Gallon (18.93 L) container Nordson Flow Through- Felt system must be used. Primer must be agitated b

49、efore application: Shaker (1 cycle/second) 60 minutes End-over end tumbler (20 rpm) 3 hours Roller (24 rpm) 7 hours Note: Primer must be installed within 2 hours following agitation. System must circulate the primer to prevent premature settling of the primer. Circulation must be approximately 762 mm /min in order to turn the material over at least 1 time in an hour. A continuous 3 to 5 mil (0.08 mm 0.13 mm) wet film without skips or streaks shall e