FORD WRS-M3H105-B3-2014 CARPET POLYESTER NON WOVEN FLAT FELT NEEDLED NON BACK COATED 185 G M2 (5 5 oz) NOMINAL FACE TO BE USED WITH FORD WSS-M99P1111-A .pdf

《FORD WRS-M3H105-B3-2014 CARPET POLYESTER NON WOVEN FLAT FELT NEEDLED NON BACK COATED 185 G M2 (5 5 oz) NOMINAL FACE TO BE USED WITH FORD WSS-M99P1111-A .pdf》由会员分享，可在线阅读，更多相关《FORD WRS-M3H105-B3-2014 CARPET POLYESTER NON WOVEN FLAT FELT NEEDLED NON BACK COATED 185 G M2 (5 5 oz) NOMINAL FACE TO BE USED WITH FORD WSS-M99P1111-A .pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev 00 2014 03 27 Released L. Sinclair, NA Controlled document at www.MATS Copyright 2014, Ford Global Technologies, Inc. Page 1 of 4 CARPET, POLYESTER, NON WOVEN, FLAT FELT, WRS-M3H105-B3 NEEDLED, NON BACK COATED 185 G/M2 (5.5 oz) NOMINAL FA

2、CE 1. SCOPE The materials defined by these specifications are flat felt, needled, nonwoven carpets of good quality and uniform composition. The carpet face is made with 80% minimum recycled (PIR/PCR) face fiber with a bi component backing of various stiffness which is not back coated. This material

3、has a heathered gray coloration and is not a solid color, color match. 2. APPLICATION The specification was released originally for trunk deck sides and deck lid applications. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the

4、 Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1.1 In addition to the requirements listed herein, the end-item floor carpet shall be tested to WSS-M15P32-D and any additional SDS requirements. The details for each of the suppliers specific construction shall be document

5、ed in the supplement attached and added to the scanned data package. 3.1.2 Vehicle Interior Environment Quality Materials/Component Performance Requirements Materials used in interior applications must meet the requirements outlined in WSS-M99P2222-D1/ latest. Test data to be provided by the Tier 1

6、at the appropriate program milestone. 3.2 SAMPLE SELECTION All evaluations shall be conducted on test specimens taken from finished roll goods prior to any subsequent operations, such as reheating or molding. 3.3 APPEARANCE (FLTM BI 109-01) The color, pattern, and finish shall match the approved Des

7、ign Center master sample, or shall be as specified on the engineering drawing. ENGINEERING MATERIAL SPECIFICATION WRS-M3H105-B3 Copyright 2014, Ford Global Technologies, Inc. Page 2 of 4 3.4 COMPOSITION 3.4.1 Face Fiber Recycled Polyester (ASTM D276) (white / black blend) 3.4.2 Backing Fiber coPolye

8、ster / (ASTM D276) Polyester Bicomponent (Bico) Note: The backing blend used for stiffness will be noted on the approved source listing. 3.5 METHOD OF DYEING Solution 3.6 CONSTRUCTION 3.6.1 Face Fiber 6 Denier (ASTM D 1244) 3.6.2 Backing Fiber 4-6 Denier (ASTM D1244) 3.7 THICKNESS* 3.7.1 Face Thickn

9、ess 1.0 +/- 0.5 mm (ISO 1765) *Face thickness prior to molding. Face thickness may change based on geometry and molding compression. 3.8 WEIGHT 3.8.1 Face Weight * 185 g/m2 (5.5 oz) nominal (ASTM D5848) * Weight tolerances approved for each suppliers construction can be found in the scanned data pac

10、kage. Maximum tolernace is +/- 10% from the nominal. 3.8.2 Backing Weight* report g/m2 (ASTM D5848) * Backing weight can be found on the approved supplier listing for the specification. 4. GENERAL INFORMATION This information given below is provided for clarification and assistance in meeting the re

11、quirements of this specification. Contact for questions concerning Engineering Material Specifications. ENGINEERING MATERIAL SPECIFICATION WRS-M3H105-B3 Copyright 2014, Ford Global Technologies, Inc. Page 3 of 4 4.1 DRAWING CALL OUT The following shall be called out on the Engineering drawing to co

12、rrectly designate the approved material. WRS-M3H105-B3 Supplier Name and Product Code (As it appears on the Approved Source Listing) WSS-M15P32-D 5. SUMMARY OF REVISIONS ENGINEERING MATERIAL SPECIFICATION WRS-M3H105-B3 Copyright 2014, Ford Global Technologies, Inc. Page 4 of 4 Non Woven Carpet Const

13、ruction Supplement Supplier _Supplier Contact Name_ Number _ Product/ Style Name _ Material Specification _ Performance Specification _ Supplier Product Code _ Manufacturing Location _ Supplier Lab Number _ Supplier Lab Date _ Composition Type Supplier Face Fiber ASTM D276 _ _ Minimum Recycled Conte

14、nt _ % PIR _ % PCR Pre-Coat ASTM D276 _ _ Mass Backing ASTM D276 _ _ Back Coating ASTM D276 _ _ Construction Solution or piece dyed (circle one) Denier (s) _ Face Fiber Thickness ISO 1765 _+/- _ mm Pre Coating Thickness ISO 1765 _+/- _ mm Mass Backing Thickness ISO 1765 _+/- _ mm Back Coating Thickness ISO 1765 _+/- _ mm Mass per Unit Area Weight Face Fiber ASTM D5848 _+/- _ g/m2 Pre Coating ASTM D5848 _+/- _ g/m2 Mass Backing ASTM D5848 _+/- _ g/m2 Back Coating ASTM D5848 _+/- _ g/m2 Materials Engineering Signature _Date _ Comments _ Rolled Goods _ Molded Product _