FORD WRS-M1H1072-A2-2012 FABRIC ZARAH JACQUARD WOVEN 39% PIR PCR UNLAMINATED TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSS-M1H1072-A1).pdf

《FORD WRS-M1H1072-A2-2012 FABRIC ZARAH JACQUARD WOVEN 39% PIR PCR UNLAMINATED TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSS-M1H1072-A1).pdf》由会员分享，可在线阅读，更多相关《FORD WRS-M1H1072-A2-2012 FABRIC ZARAH JACQUARD WOVEN 39% PIR PCR UNLAMINATED TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSS-M1H1072-A1).pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 0 2012 08 27 Released M. Montgomery, FOE Controlled document at www.MATS Copyright 2012, Ford Global Technologies, LLC Page 1 of 2 FABRIC, ZARAH, JACQUARD WOVEN, WSS-M1H1072-A1 UNLAMINATED FABRIC, ZARAH, JACQUARD WOVEN, WRS-M1H1072-A2 39

2、% PIR/PCR UNLAMINATED 1. SCOPE The material defined by this specification is a woven dobby polyester face fabric. Material conforming to WRS-M1H1072-A2 contains 39% PIR/PCR (Post industrial/post consumer) recycled yarn. 2. APPLICATION WSS-M1H1072-A1 & WRS-M1H1072-A2 have been introduced as an interi

3、or trim fabric for use in the B299 MCA 2013.5 Model Year, as a seat insert supplied as a tri-laminate. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A)

4、. Materials with recycled content as defined by WRS-M99P42-A2 (Textile Materials, Identification of Recycled Content ) should be used whenever technically feasible. 3.1.1 WSS-M1H1072-A1. This specification is based on virgin materials 3.1.2. WRS-M1H1072-A2 This specification must contain 39% recycle

5、d content as defined by WRS-M99P42-A2. The remaining portion of the material can come from virgin sources. 3.1.3 In addition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 10 % toleranc

6、e (ASTM D3775) Warp 272 / 10 cm Weft 175 / 10 cm 3.2.2 Fabric Weight, +/- 10 % tolerance (FLTM BN 106-01) 300 g/m2 3.3 COMPOSITION (ASTM D629) Fabric 100% polyester ENGINEERING MATERIAL SPECIFICATION WSS-M1H1072-A1 WRS-M1H1072-A2 Copyright 2012, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CON

7、STRUCTION (ASTM D1244) Warp 620 dtex f102 airjet texturized Weft A1 A2 620 dtex f 102 620 dtex f 102 (polyester airjet texturized) (polyester airjet texturized) 100 % recycled yarn) 3.5 METHOD OF DYEING package dye or as approved by Materials Engineering 3.6 FINISHING OPERATIONS - Antistatic - Washi

8、ng -Thermo fixation. or as approved by Materials Engineering. 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 Purchase departm

9、ents will ensure that the material defined in this specification and shipped to any one assembly plant will be produced by one supplier only. 4.2 If yarn is locally sourced it must meet the above fabric construction, composition and Yarn construction. The fabric must also meet the requirements of WSS-M8P18-A1/A2/A3/A4. 4.3 Global strategy for this fabric is to use Tri-Laminate / foam & scrim construction in all regions.