FORD SK-M3G9523-B1-2006 ADHESIVE TAPE POLYURETHANE CLEAR PAINTABLE STONE CHIP RESISTANT TO BE USED WITH FORD WSS-M99P111-A 《耐石击可印刷透明聚氨酯胶带 与标准FORD WSSS-M99P111-A一起使用》.pdf
《FORD SK-M3G9523-B1-2006 ADHESIVE TAPE POLYURETHANE CLEAR PAINTABLE STONE CHIP RESISTANT TO BE USED WITH FORD WSS-M99P111-A 《耐石击可印刷透明聚氨酯胶带 与标准FORD WSSS-M99P111-A一起使用》.pdf》由会员分享,可在线阅读,更多相关《FORD SK-M3G9523-B1-2006 ADHESIVE TAPE POLYURETHANE CLEAR PAINTABLE STONE CHIP RESISTANT TO BE USED WITH FORD WSS-M99P111-A 《耐石击可印刷透明聚氨酯胶带 与标准FORD WSSS-M99P111-A一起使用》.pdf(4页珍藏版)》请在麦多课文档分享上搜索。
1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 07 27 Revised Inserted 3.0; Deleted 3.1, 3.2, 3.3, 3.15, 3.17, 3.8, 4 1999 01 29 Revised Deleted B2; Revised & Updated K. Bruley1982 07 12 Released SM/EQ9044TP Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC
2、Page 1 of 4 ADHESIVE TAPE, POLYURETHANE, CLEAR, PAINTABLE, SK-M3G9523-B1 STONE CHIP RESISTANT 1. SCOPE The material defined by this specification is a heat resistant colorless clear polyurethane tape single coated by a self adhesive and covered by release paper. 2. APPLICATION This material was orig
3、inally released as a stone chip protection on wheel arch flare. Application is possible prior to paint application as well as after paint curing oven. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requir
4、ements For Production Materials (WSS-M99P1111-A). 3.4 DIMENSIONS 3.4.1 Width As specified on (Sliding gauge) Engineering drawing 3.4.2 Thickness 0.29 - 0.39 mm (ASTM D 1000) Or as specified on Engineering drawing. 3.5 COLOR Colorless clear or as specified on Engineering drawing 3.6 MASS per m20.30 -
5、 0.50 kg 3.7 TENSILE STRENGTH, min 150 N/25 mm (ASTM D 882, Method A, separation rate 300 mm/minute, clamp distance 50 mm) 3.7.1 Elongation at Break, min 350% 3.8 180 PEEL ADHESION (ASTM D 1000, on polished stainless steel) 3.8.1 Original, min 35 N/25 mm (24 h at room temperature) ENGINEERING MATERI
6、AL SPECIFICATIONSK-M3G9523-B1 Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 4 3.8.2 After Ageing No loss of adhesion (14 days at 70 +/- 2 C, 1 h at room temperature) 3.8.3 After Humidity Ageing No loss of adhesion (72 h at 38 +/- 2 C and 98 +/- 2.5 relative
7、humidity) 3.9 SHEAR ADHESION, min 40 N/2.5 cm2Test Method: 2.5 cm2of a 25 mm wide tape shall be bonded to a polished stainless steel panel. The mating surfaces must be pressed firmly together to force out trapped air and ensure a good bond. Determine shear strength at a rate of 25 mm/minute. Free ta
8、pe length maximum 5 mm. 3.10 SOFTENING POINT, min 95 C (ASTM D 816, except specimens per clause 3.6) Test Method: Maintain oven temperature at 50 C for 15 minutes and then increase 2.5 C/5 minute until bond failure. 3.11 PAINTABILITY If required on Engineering drawing The surface shall be dry to tou
9、ch after cooling to room temperature. It shall be free from cracks or bubbles and shall show a uniform closed paint film without staining or discoloration. Test Method: 1) Prepare test panels of 300 x 100 mm according to FLTM BI 120-01 A and C. 2) Bond 250 x 25 mm pieces of tape on the test panels.
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- FORDSKM3G9523B12006ADHESIVETAPEPOLYURETHANECLEARPAINTABLESTONECHIPRESISTANTTOBEUSEDWITHFORDWSSM99P111A

链接地址:http://www.mydoc123.com/p-748135.html