FORD FLTM EU BN 001-02-2001 YARN PULL-OUT STRENGTH OF WOVEN FABRICS《机织织物的纱线抽出强度》.pdf

《FORD FLTM EU BN 001-02-2001 YARN PULL-OUT STRENGTH OF WOVEN FABRICS《机织织物的纱线抽出强度》.pdf》由会员分享，可在线阅读，更多相关《FORD FLTM EU BN 001-02-2001 YARN PULL-OUT STRENGTH OF WOVEN FABRICS《机织织物的纱线抽出强度》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、FORD LABORATORY TEST METHOD EU BN 001-02 Date Action YARN PULL-OUT STRENGTH OF WOVEN FABRICS Revisions Application 2001 0822 Revised Editorial - no technical change A. Cockman 1994 02 28 This method is used to determine the pull-out strength of one or more adjacent yarns from woven fabric constructi

2、ons. This gives an indication of the effectiveness of resin backcoatings or foam lamination in locking the yarns of the fabric construction. Apparatus Required Tensile Testing Machine Constant rate of extension machine with autographic load recording device. Test speed to be 125 mm/minute. Specimen

3、clamps to be a minimum of 50 mm wide. Sharp Bladed Knife or Scalpel Conditioning and Test Conditions All test values indicated herein are based on material conditioned in a controlled atmosphere of 23 +/- 2 “C and 50 +/- 5 % relative humidity for not less than 24 h prior to testing and tested under

4、the same conditions unless otherwise specified. Procedure Method A This method is for testing the pull-out strength of single warp or weft yarns. 1. Three test specimens, each 300 x 50 mm in size are cut from different areas of the sample for each fabric direction. The longer dimension of the specim

5、en must be parallel to the warp or weft yarns of the fabric. 2. Unravel the shorter yarns from one end of each test specimen for a length of 40 mm (see Figure 1). Copynght02001, Ford Global Technologies, Inc FORD LABORATORY TEST METHOD EU BN 001-02 3. Select the warp (or weft) yarn along the centre

6、of the specimen for testing the pull-out strength. Cut through this yarn 200 mm from the edge of the unravelled yarns. 4. Clamp the unravelled end of the test yarn in the upper jaws of the tensile test machine. Clamp the other end of the fabric in the lower jaws (see Figure 1). Initial jaw separatio

7、n to be 220 mm. 5. Start the tensile tester and pull out the yarn at 125 mm/minute. Evaluation Report the initial peak load in Newtons required to pull out the test yarn. Method B This method is for testing the pull-out strength of two or more adjacent yarns which follow the same path through the fa

8、bric weave pattern. 1. & 2. Same as Method A. 3. Select a group of 2 or more warp (or weft) yarns which follow the same path through the centre of the test specimen. Cut through each of these test yarns at 200 mm from the edge by the unravelled yarns (see Figure 1). 4. Clamp the unravelled ends of t

9、he selected test yarns in the upper jaws of the tensile test machine and the other end of the fabric in the lower jaws (see Figure 1). Initial jaw separation to be 220 mm. 5. Start the tensile tester and pull out the group of yarns at 125 mm/minute. Evaluation Report the initial peak load in Newtons

10、 required to pull out the test yarns and the number of yarns in the group. Chemicals, materials, parts, and equipment referenced in this document must be used and handled properly. Each party is responsible for determining proper use and handling in its facilities. Page 2 of 3 Copynght02001, Ford Gl

11、obal Technologies, Inc FORD LABORATORY TEST METHOD EU BN 001-02 Test Speed 125 mmlminute /c / YARN PULL-OUT STRENGTH OF WOVEN FABRICS Unravel warp or weft yarns to approximately 40 mm 200 mm Initial jaw separation 220 mm Yarn or Yarns cut 10 mm from jaw to cut line Specimen Size 300 mm x 50 mm Figure 1 Page 3 of 3 Copynght02001, Ford Global Technologies, Inc