FORD FLTM BV 002-1-2001 ABRASION RESISTANCE TEST FOR SOUND DEADENERS AND UNDERCOATING.pdf

《FORD FLTM BV 002-1-2001 ABRASION RESISTANCE TEST FOR SOUND DEADENERS AND UNDERCOATING.pdf》由会员分享，可在线阅读，更多相关《FORD FLTM BV 002-1-2001 ABRASION RESISTANCE TEST FOR SOUND DEADENERS AND UNDERCOATING.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、FORD LABORATORY TEST METHOD BV 002-01 Date 2001 10 31 2000 08 11 1992 08 11 ABRASION RESISTANCE TEST FOR SOUND DEADENERS AND UNDERCOATING Action Revisions Revised Editorial - no technical change A. Cockman Revised Editorial - no technical change A. Cockman Application This procedure is used to deter

2、mine the abrasion resistance of sound deadeners and undercoating materials which are used on the underside of automobile bodies. A primed steel panel coated with the test material is subjected to a bombardment of wet steel shot to simulate actual road conditions wherein stones, pebbles, etc. are thr

3、own against the coated underbody during driving. Apparatus Required Drying Oven Convection type - capable of maintaining temperature of 100 +/- 2 F to 400 +/- 5 OF Source: Young Bros. Electric Type L3 or equivalent. Balance Laboratory Beam or equivalent - accurate to .I g. Spray Booth Binks or equiv

4、alent. Spray Equipment for Deadener Pyles Industry Pump - Model 2600-485 20 - 1 Ratio Pump 052 Tip or equivalent Spray Equipment for Primer Binks #62 -Air Cap 66 SH - Tip 66 SS Air Pressure 50 - 80 psi Abrasion Tester or Gravelometer The Gravelometer (see attached sketch) consists of an elongated bo

5、x with a hopper on one end and a slot for inserting an abrasion test panel in the other end. Steel shot mixed with water is poured into the hopper where a stream of air propels the shot onto the test panel inserted in the opposite end. Steel Shot 50 Ibs of SAE 780 shot with the following additional

6、requirements: Copyright O 2001, Ford Global Technologies, Inc FORD LABORATORY TEST METHOD BV 002-01 Size 100 % to pass through a No. 8 sieve (.O937 in.) 100 % to be retained on a No. 10 sieve (.O787 in.) ASTM E 11 Shape To be as near 100 % round as possible. No voids, heads, cracks or tails permitte

7、d. Hard ness 90 % to be Rc 42 - 48. 2 quarts of water containing 10 g of potassium dichromate is used to prevent rusting of the shot in storage. Steel Test Panels The panels used in this test shall be 5 x 12 x ,036 - ,042 inch flat C.R.L.C. steel with a 1/4 inch hole in the center of one end for han

8、ging the panel when spraying with deadener. Conditioning and Test Conditions All test values indicated herein are based on material conditioned in a controlled atmosphere of 23 +/- 2 OC and 50 +/- 5 % relative humidity for not less than 24 h prior to testing and tested under the same conditions unle

9、ss otherwise specified. Procedure 1. Prepare three test panels with deadener or undercoating, following Steps 1 through 10 where applicable under FLTM BV 001-01. Use Method “A, “B“, or “C“ etc. as designated by the Engineering specification. Where masking is called for in Step No. 4, the top and bot

10、tom 3 inches of the panel are masked before applying the deadener. 2. Condition all panels for 24 h at 100 +/- 2 OF and 98 +/- 2 % relative humidity. Note: If a humidity cabinet is not available, the panels may be supported over a few inches of water in a sealed container placed in an oven at 1 O0 +

11、/- 2 OF for 24 h. 3. Cool each panel to 23 +/- 2 OC and insert in the Gravelometer as shown in the sketch. 4. Main line air supply should be at 80 psi prior to and during the test. Open the line valve and adjust so that air flow through the Flowmeter indicates a volume of 80 CU ft min is obtained. N

12、ote the open line pressure at the indicating gage. This pressure should indicate 9 - 12 psi, however, it is not critical if all hoses and fittings are standard. Page 2 of 4 Copynght02001, Ford Global Technologies, Inc FORD LABORATORY TEST METHOD BV 002-01 5. Abrade each panel with the full 50 Ibs of

13、 shot, collecting the spent shot in a pail directly below the test panel, and repeat the cycle four additional times. 6. Invert each test panel and repeat five cycles of abrasion with the wet shot. 7. Rinse the test panels in clean tap water to remove all loose particles of test material, dry for on

14、e hour at 21 5 +/- 5 OF, cool and weigh. 8. Calculate the percent retention as follows: x 100 = % retention B-A Where A = Weight of uncoated panel B = Weight of coated panel before abrasion C = Weight of coated panel after abrasion 9. Report the minimum retention of the three panels tested. Chemical

15、s, materials, parts, and equipment referenced in this document must be used and handled properly. Each party is responsible for determining proper use and handling in its facilities. Page 3 of 4 Copynght02001, Ford Global Technologies, Inc FORD LABORATORY TEST METHOD BV 002-01 ABRASION RESISTANCE TEST FOR SOUND DEADENERS Gravelometer HOPPER PLUG PANEL INSERT 3/8“TD PIPE 6-1/4“ LONG PRESSURE GAUGE PRESSURE REGULATOR FLOW METER 10 518 HIGH PAIL Page 4 of 4 Copynght02001, Ford Global Technologies, Inc