FORD FLTM BU 156-01-2010 CARBON FILTER PAPER ADHESION TEST《炭过滤器滤纸粘合试验》.pdf

《FORD FLTM BU 156-01-2010 CARBON FILTER PAPER ADHESION TEST《炭过滤器滤纸粘合试验》.pdf》由会员分享，可在线阅读，更多相关《FORD FLTM BU 156-01-2010 CARBON FILTER PAPER ADHESION TEST《炭过滤器滤纸粘合试验》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 FORD LABORATORY TEST METHODFLTM BU 156-01 Date Action Revisions 2010 12 02 Activated G. Kowalski, NA Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, Inc. Page 1 of 3 CARBON FILTER PAPER ADHESION TEST Application This procedure is used to test adhesion of carbon filter pape

2、r affixed to the interior cover of the air cleaner component of the air induction system (AIS) when contaminated with engine oil. Apparatus Required Laboratory Air Flow Through Oven Maintained at 110 +/- 2 C (230oF) Resin Substrate Smooth un-grained plaques of production representative material. Rol

3、ler A roller weighing 2.3 kg (5 lbs) for bonding an adhesive backed carbon paper to a resin plaque. Oil Current Motorcraft service engine oil Oil distribution Tool Hand held rubber scraper attached to a glass rod (rubber policeman) Tensile Testing Machine Machine capable of maintaining a constant ja

4、w separation rate of 305 mm/minute (12 in/minute). 90oPeel Test Setup The test setup for peel adhesion is illustrated in figure 1. 90oPeel Test Fixture The test fixture for peel adhesion is illustrated in figure 2. Conditioning and Test Conditions All test values indicated herein are based on materi

5、al conditioned in a controlled atmosphere of 23 +/- 2 C (73oF) and 50 +/- 5% relative humidity for not less than 24 h prior to testing and tested under the same conditions unless otherwise specified. FORD LABORATORY TEST METHODFLTM BU 156-01 Printed copies are uncontrolled Copyright 2010, Ford Globa

6、l Technologies, Inc. Page 2 of 3 Procedure 1. Adhere the first 102mm of a 178mm X 12.7mm (4“ of a 7“ X 0.5“) carbon filter material pre-bonded with transfer tape onto the appropriate resin substrate. A 2.3 kg (5 lbs) roller should be used to obtain uniform pressure when applying the carbon filter ma

7、terial to the resin plaque. 10 specimens are needed (See Figure 1) for testing. Inspect for streaks, blisters, or wrinkles. 2. Cure bonded test specimens for 24 hours at 23oC (73oF) before starting test. Set 5 specimens aside for initial adhesion testing to be performed in step 8 of this procedure.

8、3. Apply drop wise 0.25 ml of SAE 10W30 oil heated to 110oC (230oF) over the bonded filter strips. 4. With the use of a rubber policeman distribute the oil evenly over the bonded area. 5. Place samples horizontally in an oven for 2 hours at 110oC (230oF). 6. Remove specimens from oven and allow samp

9、les to equilibrate at room temperature for one hour. 7. Examine carbon paper and adhesive backing for visual evidence of peeling, loss of adhesion, wrinkling, loss of printing or legibility, or any other effect which would detract from its proper function. 8. Perform peel strength within one hour of

10、 cooling to ambient temperature per ASTM D1000 adhesion test modified using a 90opeel fixture (or variable angle peel fixture set to 90o), test speed 305mm/min (12 in/min). The fixture must permit forward motion of the substrate to maintain the 90o. See Figure 1. Figure 1: 90 Peel test set-up Resin

11、Plaque Tape Carbon Filter MatlFix onto Peel Test Fixture 305mm/min (12in/min) FORD LABORATORY TEST METHODFLTM BU 156-01 Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, Inc. Page 3 of 3 Figure 2: Variable Angle Peel Test Fixture (must be set to 90o, Instron #2820-029 Variable Angle Peel Fixture shown)