FORD FLTM BI 115-01-2001 COLOR MATCH AND INTERCOAT ADHESION FOR REPAIR ENAMELS (Replaces FLTM BI 015-01 FLTM EU-BI 015-01)《修复用瓷漆的配色和中间涂层的粘附性 替代FLTM BI 015-01 FLTM EU-BI 015-01［替代 F.pdf

《FORD FLTM BI 115-01-2001 COLOR MATCH AND INTERCOAT ADHESION FOR REPAIR ENAMELS (Replaces FLTM BI 015-01 FLTM EU-BI 015-01)《修复用瓷漆的配色和中间涂层的粘附性 替代FLTM BI 015-01 FLTM EU-BI 015-01［替代 F.pdf》由会员分享，可在线阅读，更多相关《FORD FLTM BI 115-01-2001 COLOR MATCH AND INTERCOAT ADHESION FOR REPAIR ENAMELS (Replaces FLTM BI 015-01 FLTM EU-BI 015-01)《修复用瓷漆的配色和中间涂层的粘附性 替代FLTM BI 015-01 FLTM EU-BI 015-01［替代 F.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 FORD LABORATORY TEST METHOD BI 115-01 Date Action Revisions 2001 03 19 Revised Editorial no technical change A. Cockman 1990 12 04 Printed copies are uncontrolled Page 1 of 2 Copyright 2001, Ford Global Technologies, Inc. COLOR MATCH AND INTERCOAT ADHESION FOR REPAIR ENAMELS Application This proced

2、ure is used to determine the acceptability of production enamels for repair color matching and intercoat adhesion of repair coat to original coat. Apparatus and Materials Required Mechanical Convection Oven Capable of maintaining a constant temperature of 180 +/- 2 C. Test Panels Steel body skin pan

3、els: Per ASTM D 609 or 150 x 300 mm having a surface finish of 1.35 - 0.45 microns Ra. Masking Tape and Paper Color Matching Device - according to FLTM BI 109-01. Reference Ford Laboratory Test Methods BI 103-02 Preparation of Panels for Paint Tests BI 106-02 Intercoat Adhesion Test BI 109-01 Color

4、Matching with Artificial Light Conditioning and Test Conditions All test values indicated herein are based on material conditioned in a controlled atmosphere of 23 +/- 2 C and 50 +/- 5 % relative humidity for not less than 24 h prior to testing and tested under the same conditions unless otherwise s

5、pecified. FORD LABORATORY TEST METHOD BI 115-01 Page 2 of 2 Copyright 2001, Ford Global Technologies, Inc. Procedure 1. Prepare a panel as described in FLTM BI 103-02, Method “C“. 2. Allow panel to cool to 23 +/- 2 C and rebake for ten minutes at 140 +/-2 C metal temperature or as specified in the E

6、ngineering Materials specification. Care must be taken to avoid touching the panel test surface with hands. 3. Allow panel to cool to 23 +/- 2 C and mask upper half of the panel and respray the unmasked area with the original material under identical conditions to a dry film thickness of 40 +/- 10 m

7、icrons. Remove masking paper and tape, flash-off test panel for 3 minutes and bake according to the Engineering Materials Specification. Evaluation 1. After cooling to room temperature, compare repaired area with the unrepaired area of the panel for color match with each other, according to FLTM BI

8、109-01. 2. Age repaired panel for 16 h at 45 +/- 2 C, or 72 h at 23 +/- 2 C and check intercoat adhesion according to FLTM BI 106-02. Chemicals, materials, parts, and equipment referenced in this document must be used and handled properly. Each party is responsible for determining proper use and handling in its facilities.