FORD ESP-M3D136-A2-2016 PHENOLIC COMPRESSION MOLDING COMPOUND TO BE USED WITH FORD WSS-M99P1111-A .pdf

《FORD ESP-M3D136-A2-2016 PHENOLIC COMPRESSION MOLDING COMPOUND TO BE USED WITH FORD WSS-M99P1111-A .pdf》由会员分享，可在线阅读，更多相关《FORD ESP-M3D136-A2-2016 PHENOLIC COMPRESSION MOLDING COMPOUND TO BE USED WITH FORD WSS-M99P1111-A .pdf（1页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev 03 2016 04 20 N Status No replacement named L. Sinclair, NA 2006 08 16 Revised Inserted 3.0; Deleted 3.2, 3.3 Removed Inactive ESP-M3D136-A1 1980 04 15 Released 733721-P2 Copyright 2016, Ford Global Technologies, LLC Page 1 of 1 PHENOLIC

2、COMPRESSION MOLDING COMPOUND ESP-M3D136-A2 NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a mineral filled, heat resistant, phenolic material, impact modified with organic fibers. 2. APPLICATION This specification was released originally for material used as thr

3、ust washers in automatic transmissions. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 COMPRESSION MOLDED TEST SPECIMENS (As molded without post

4、bake.) 3.1.1 Impact Strength, Izod, notched, min 11 J/m (ASTM D 256) 3.1.2 Specific Gravity 1.55 1.59 (ASTM D 792) 3.1.3 Flexural Strength, min 55 MPa (ASTM D 790) 3.1.4 Tensile Strength, min 35 MPa (ASTM D 638) 3.1.5 Compressive Strength, min 155 MPa (ASTM D 695) 3.1.6 Water Absorption, max 0.2% (ASTM D 570) 3.1.7 Hardness, Rockwell “E“, min 80 (ASTM D 785) 3.1.8 Deflection Temperature, min 190 C (ASTM D 648, 1820 kPa) 3.1.9 Ash, min 28% (FLTM BO 006-02)