FORD ESB-M99J291-A-2005 TAPE URETHANE PRESSURE SENSITIVE CHIP RESISTANT EXTERIOR - 0 36 MM (14 MIL) NOMINAL THICKNESS TO BE USED WITH FORD WSS-M99P1111-A 《标称厚度0 36 MM(14 MIL)的汽车外.pdf
《FORD ESB-M99J291-A-2005 TAPE URETHANE PRESSURE SENSITIVE CHIP RESISTANT EXTERIOR - 0 36 MM (14 MIL) NOMINAL THICKNESS TO BE USED WITH FORD WSS-M99P1111-A 《标称厚度0 36 MM(14 MIL)的汽车外.pdf》由会员分享,可在线阅读,更多相关《FORD ESB-M99J291-A-2005 TAPE URETHANE PRESSURE SENSITIVE CHIP RESISTANT EXTERIOR - 0 36 MM (14 MIL) NOMINAL THICKNESS TO BE USED WITH FORD WSS-M99P1111-A 《标称厚度0 36 MM(14 MIL)的汽车外.pdf(5页珍藏版)》请在麦多课文档分享上搜索。
1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2005 08 11 Revised Inserted 3.0; deleted 3.1, 3.6 and 4 1985 01 10 Released ESB-M99J291-A2/A2/A4 C9P1-RD527931 1977 05 12 Released AG1-6000-224 Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 1 of 5 TAPE, URE
2、THANE, PRESSURE SENSITIVE, CHIP ESB-M99J291-A RESISTANT, EXTERIOR - 0.36 MM (14 MIL) NOMINAL THICKNESS TAPE, URETHANE, PRESSURE SENSITIVE, CHIP ESB-M99J291-A2 RESISTANT, EXTERIOR - 0.20 MM (8 MIL) NOMINAL THICKNESS TAPE, URETHANE, PRESSURE SENSITIVE, CHIP ESB-M99J291-A3 RESISTANT, NON-VISIBLE APPLIC
3、ATIONS - 0.36 MM (14 MIL) NOMINAL THICKNESS TAPE, URETHANE, PRESSURE SENSITIVE, CHIP ESB-M99J291-A4 RESISTANT, NON-VISIBLE APPLICATIONS - 0.20 MM (8 MIL) NOMINAL THICKNESS 1. SCOPE The materials defined by these specifications are clear, paper backed, urethane films with a water clear pressure sensi
4、tive adhesive. ESB-M99J291-A3 & A4 are not suitable for use on visible exterior areas. 2. APPLICATION ESB-M99J291-A & A2 were released originally for material used for application to lower body sides to provide protection from stone abrasion. ESB-M99J291-A3 & A4 were released originally for material
5、 used to provide a galvanic barrier between steel and aluminum bumper components. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 PHYSICAL PROPER
6、TIES A, A2, A4 A3 3.2.1 Tensile Strength, MPa min 55 48 (ASTM D 882, Method A, 25 x 150 mm sample, 25 mm distance between bench marks, jaw spaced at start 100 mm, pulling speed 300 mm/min) 3.2.1.1 Elongation, min 400% 400% ENGINEERING MATERIAL SPECIFICATIONESB-M99J291-A/A4Printed copies are uncontro
7、lled Copyright 2005, Ford Global Technologies, LLC Page 2 of 5 A, A3, A2 A4 3.2.2 Tear Strength, kg min 1.8 0.9 1.1 (ASTM D 1938) 3.2.3 Adhesion (ASTM D 1000 Method A. Determine the adhesion to ESB-M50J quality enamel. The tape shall be 25 mm wide for this test.) 3.2.3.1 As Received, min 438 N/m 3.2
8、.3.2 Aged, min 657 N/m Test Method: Expose duplicate samples to each of the following conditions: . 72 h at 70 C. . 400 h weatherometer, per FLTM BO 101-01. . 168 h at 38 C and 95 - 100% relative humidity. . 10 cycles consisting of 4 h at 70 C, 4 h at 38 C and 95 - 100% relative humidity, and 16 h a
9、t -30 C. Samples shall be conditioned for 48 h at 23 +/- 2 C prior to exposure. Tests shall be completed within 1 h after removal from the conditioning environment. The cycle test samples shall be allowed to recover to 23 +/- 2 C prior to test. 3.3 FILM PROPERTIES 3.3.1 Appearance The film and adhes
10、ive shall be water clear and colorless. 3.3.2 Gloss (ESB-M99J291-A & A2) 75 +/- 10 (FLTM BI 110-01, using a 20 Gardner Glossmeter) A, A3 A2, A4 3.3.3 Thickness (ASTM D 1000) 3.3.3.1 Film, mm 0.27-0.34 0.13-0.18 3.3.3.2 Film & Adhesive, mm 0.32-0.39 0.18-0.23 ENGINEERING MATERIAL SPECIFICATIONESB-M99
11、J291-A/A4Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 3 of 5 3.4 RESISTANCE PROPERTIES 3.4.1 Sample Preparation Resistance properties test shall be conducted using appropriate sized steel panels freshly painted with white (ZWFA-5418) ESB-M50J100 quality high glo
12、ss enamel per FLTM BI 103-02, Method C. The test panels shall be solvent wiped with M-14J147 Petroleum Naphtha prior to applying the film per the following procedure: . Peel off the backing paper from the film in a smooth, continuous motion. Do not pull the film from the paper. . Liberally apply wet
13、ting solution 5 mL of liquid dish washing detergent per 4 L of water or a 1:3 or 1:4 ratio if isopropyl alcohol/water to panel. . Apply some wetting solution to adhesive side of film. . Position the film on the panel. . Using a plastic squeegee, smooth out the film using firm overlapping strokes, wo
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制: