FORD ESB-M4D100-A2-2010 POLYCARBONATE (PC) OPTICAL GRADE - COATED TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD ESF-M4D100-A1)《光学级聚碳酸酯(PC)涂层 与福特WSS-M99P1111-A 一起使用 在福特ESF-.pdf

《FORD ESB-M4D100-A2-2010 POLYCARBONATE (PC) OPTICAL GRADE - COATED TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD ESF-M4D100-A1)《光学级聚碳酸酯(PC)涂层 与福特WSS-M99P1111-A 一起使用 在福特ESF-.pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M4D100-A2-2010 POLYCARBONATE (PC) OPTICAL GRADE - COATED TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD ESF-M4D100-A1)《光学级聚碳酸酯(PC)涂层 与福特WSS-M99P1111-A 一起使用 在福特ESF-.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2010 09 10 N-STATUS Replaced by WSS-M4D1051-A1, WSS-M4D1052-A2, WSS-M4D1053-A1, WSS-M4D1053-A2 L. Soreide, NA 2005 01 07 Revised Inserted 3.0; Deleted 3.1, 3.2.2, 3.6, 3.7 & 4 1975 12 12 Released AF1-6000-53 Printed copies are uncontrolled Cop

2、yright 2010, Ford Global Technologies, LLC Page 1 of 4 POLYCARBONATE (PC), GENERAL PURPOSE GRADE ESF-M4D100-A1 POLYCARBONATE (PC), OPTICAL GRADE - COATED ESB-M4D100-A2 POLYCARBONATE (PC), OPTICAL GRADE - UNCOATED ESB-M4D100-A3 NOT TO BE USED FOR NEW DESIGN 1. SCOPE The materials defined by these spe

3、cifications are polycarbonate resins characterized by high strength and high heat resistance. These materials are naturally transparent. Three types are defined. 2. APPLICATION ESF-M4D100-A1: This specification was released originally for material used in applications requiring optical clarity, such

4、 as instrument cluster light filters and lenses. This material may be color pigmented when optical transparency is not required, and may be specified for applications requiring high strength and high impact resistance. This general purpose resin is not used for exterior signal lenses. ESB-M4D100-A2:

5、 This specification was released originally for material used in exterior signal lamp lenses incorporating reflex reflectance where any surface change due to weathering is unacceptable (SAE J 576c). These applications, when using material defined by this specification, must have an approved coating

6、(para 3.4.5) applied to the first surface. ESB-M4D100-A3: This specification was released originally for material used in uncoated exterior signal lamp lenses not incorporating reflex reflectance. Note: Materials defined by ESF-M4D100-A1 or ESB-M4D100-A2 designation correspond to former ESF-M4D100-A

7、, Type I or Type II designation as follows: ESF-M4D100-A1 replaces ESF-M4D100-A, Type I ESB-M4D100-A2 replaces ESF-M4D100-A, Type II Existing drawings specifying ESF-M4D100-A, Type I or Type II, do not require revision to reflect this new classification. ESF-M4D100-A specification shown without type

8、 designation is understood to be ESF-M4D100-A1. ESF-M4D100-A1 also replaces ESB-M4D100-A1. Drawings showing the ESB-M4D100-A1 do not require revision to reflect the ESF designation. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform

9、to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 MOLDED TEST SPECIMEN The following requirements are intended for initial source qualifications, and Initial Sample Inspection Report. These will be rechecked at intervals specified by Quality Assurance. ENGINEERING

10、MATERIAL SPECIFICATIONESF-M4D100-A1 ESB-M4D100-A2/A3Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 2 of 4 3.2.1 Preparation of Test Specimens All test specimens shall be injection molded in accordance with ASTM D 1897. The values of this specification are based on

11、 natural color, injection molded specimens unless otherwise specified. ESF-M4D100-A1 ESB-M4D100-A2 ESB-M4D100-A3 3.2.3 Specific Gravity 1.19 - 1.26 1.22 max (ASTM D 792) 3.2.4 Tensile Strength, MPa, min (ASTM D 638, Type 1 specimen, 50 mm/minute test speed) Natural 59 56 Pigmented 57 55 Elongation,

12、% min 60 100 3.2.5 Flexural Modulus, GPa, min 2 2.1 (ASTM D 790, Method I, Procedure A) 3.2.6 Flexural Strength, MPa, min 76 83 (ASTM D 790 Method I, Procedure A) 3.2.7 Impact Strength, Izod, J/m, min (ASTM D 256, 63.5 x 12.7 x 3.2 mm specimen) 3.2.7.1 Notched Natural 640 640 Pigmented 534 534 3.2.7

13、.2 Unnotched 3200 2400 3.2.8 Heat Deflection Temperature, C, min (ASTM D 648, 127 x 12.7 x 6.4 mm specimen) At 1.82 MPa 124 121 At 0.45 MPa - 135 ENGINEERING MATERIAL SPECIFICATIONESF-M4D100-A1 ESB-M4D100-A2/A3Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 3 of 4

14、3.3 OPTICAL PROPERTIES (ESB-M4D100-A2 and A3) 3.3.1 Haze, max 2.0% (ASTM D 1003) 3.3.2 Luminous Transmission, min 87.0% (ASTM D 791, 3.2 mm molded disc) 3.3.3 Color As specified on the engineering drawing. Color shall match master sample approved for production on file in the Quality Control or Prod

15、uct Engineering Laboratory. 3.3.4 Resistance to Fade No change in color (FLTM BN 001-01) after exposure to 500 SFH. 3.4 MOLDED PART 3.4.1 Color Natural or as specified on engineering drawing. 3.4.2 Appearance Shall be uniform in density, texture and finish, free of visible porosity, warpage, heat sc

16、orch, checks, cracks, chipped edges and uneven surfaces. Shall also be free of other contamination. 3.4.3 Heat Resistance Finished parts must pass the following test. Test Method: Condition the parts for 3 h in a mechanical convection oven maintained at 107 +/- 3 C (or as otherwise specified on engi

17、neering drawing). After removal, parts shall exhibit no more than 0.5% shrinkage. There shall be no local shrinkage where the part has been gated which will interfere with assembly to mating parts of affects its appearance. The part shall not warp to an extent that would affect its use in ultimate a

18、ssembly. 3.4.4 Optics - Including Outdoor Exposure, for Exterior Lens Applications 3.4.4.1 ESB-M4D100-A2 Parts must be molded from a material which conforms to the requirements of SAE J 576c and any further special requirements indicated on the engineering drawing. In addition, proof of ETL approval

19、 and State of California Highway Patrol approval must be furnished to PEO on samples weathered for 3 years in both Florida and Arizona. ENGINEERING MATERIAL SPECIFICATIONESF-M4D100-A1 ESB-M4D100-A2/A3Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 4 of 4 3.4.4.2 ES

20、B-M4D100-A3 Material approved to this specification must satisfy all requirements of 3.4.4.1 with the noted exception of surface haze. After outdoor exposure, surface haze shall not exceed 30%. 3.4.5 Clear Coating (ESB-M4D100-A2 only) The polycarbonate, clear coat system shall conform to all require

21、ments of ESB-M2P80. Only those clear coatings approved by the responsible PEO and referenced in the general information section of ESB-M2P80 shall be utilized. 3.5 FLAMMABILITY Burn Rate, max 100 mm/min (FLTM BN 024-02, without the lot Self-extinguishing (SE) sampling plan) In addition, the test spe

22、cimen shall not exhibit any flashing or sudden flaming on either surface in excess of the above maximum value. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of these specifications. 5.1 DIELECTRIC STRENGTH 13.8 kV/mm (ASTM

23、 D 149, short time) 5.2 WATER ABSORPTION, by weight 0.5% (ASTM D 570) 5.3 MOLD SHRINKAGE 0.005 - 0.007 (ASTM D 955) 5.4 COEFFICIENT OF LINEAR THERMAL EXPANSION 6.75-5/C (ASTM D 696) 5.5 REFRACTIVE INDEX (ASTM D 542) ESB-M4D100-A2 and A3 only 1.58 5.6 HARDNESS, ROCKWELL M 65 - 80 (ASTM D 785) 5.7 CHEMICAL SENSITIVITY These materials are soluble in chlorinated hydrocarbons and aromatic solvents. 5.8 FLEXURAL MODULUS ESF-M4D100-A1 only 2 GPa (ASTM D 790, Method I, Procedure A)