FORD ESB-M3G41-A-2005 TAPE THERMOPLASTIC - BONDING TO BE USED WITH FORD WSS-M99P1111-A 《热塑性胶带 与标准FORD WSS-M99P1111-A一起使用 》.pdf

《FORD ESB-M3G41-A-2005 TAPE THERMOPLASTIC - BONDING TO BE USED WITH FORD WSS-M99P1111-A 《热塑性胶带 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M3G41-A-2005 TAPE THERMOPLASTIC - BONDING TO BE USED WITH FORD WSS-M99P1111-A 《热塑性胶带 与标准FORD WSS-M99P1111-A一起使用 》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2005 09 19 Revised Inserted 3.0; Deleted 3.1, 3.10, 4 1978 11 14 Metricated, Renumbered & Retyped CAH1-RD572066-175 1963 09 10 Released AS1-1082 Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 1 of 2 TAPE, TH

2、ERMOPLASTIC BONDING ESB-M3G41-A 1 SCOPE The material defined by this specification is a flexible, dry film adhesive tape composed of synthetic elastomers and various thermoplastic and thermosetting resins. 2. APPLICATION This specification was released originally for material used for bonding produc

3、t name plates on scuff plates as well as exterior decorative finishes to chrome plated die castings. The bonds are made by heat and pressure activation. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requ

4、irements For Production Materials (WSS-M99P1111-A). 3.2 COLOR Dark Brown (cured and uncured) 3.3 THICKNESS, min 0.0016 in (41 m) (ASTM D 1000) 3.4 SOLIDS, min 97% (ASTM D 1084, except heat at 102 +/- 3 C for 3 h) 3.5 TENSILE STRENGTH, (uncured) 1.35 lb/in (236 N/m) (ASTM D 1000, pulled at 12 in (305

5、 mm) min) Elongation, min 200% 3.6 WEIGHT 0.010 +/- 0.002 lb/ft2(50 +/- 10 g/m2) 3.7 TENSILE SHEAR ADHESION, min 3.7.1 Normal Adhesion 550 psi (3.8 MPa) 3.7.2 Aged Adhesion 7 days water immersion at 23 +/- 2 C 450 psi (3.1 MPa) 7 days at 93 +/- 3 C 600 psi (4.1 MPa) 7 days immersion 5% salt solution

6、 150 psi (1.0 MPa) 7 days at 38 C and 95-100% R.H. 450 psi (3.1 MPa) ENGINEERING MATERIAL SPECIFICATIONESB-M3G41-APrinted copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 2 of 2 Test Method: Clean an area approximately 1 in (25 mm) wide along the edge of the long dimension

7、of (2) 4-1/2 x 12 in (174 x 305 mm) pieces of 0.030 in (0.76 mm) AA-5052-H32 aluminum using first toluol (M-14J 242) and then acetone (M-1021). The area may be considered free of oils and greases when there is no haze remaining on the metal. Apply the bonding tape to the cleaned area of one panel. L

8、ay the cleaned bond area of the second panel over the first, making a bond area 1/2 wide x 12 in long (13 x 305 mm). Apply a pressure of 150 psi (1.0 MPa) to the bond line using a laboratory press or other suitable means and bring the bond line temperature to 191 C. Maintain at that temperature for

9、10 minutes. Remove the pressure and allow the panel to cool 4 to 24 h at 23 +/- 2 C. Cut the panel into 1 in (25 mm) wide strips using a band saw. This will provide specimens 8-1/2 in (216 mm) long with a 1/2 in (13 mm) overlap bond. Pull the specimens at a rate of 0.1 in (25 mm)/min and double the

10、load reading to compute and record the load in psi (or MPa). An average of 3 samples shall be used to obtain the results. Subject three 1 in (25 mm) specimens to each of the above aging tests. 3.8 90 PEEL ADHESION, min 3.8.1 Normal 5 lb/in (880 N/m) 3.8.2 Aged Peel Adhesion 7 days at 38 C and 95-100

11、% R.H. 5 lb/in (880 N/m) 7 days immersion 5% salt solution 5 lb/in (880 N/m) Test Method: Clean 1 x 7 x 0.010 in (25 x 178 x 0.25 mm)/min strips of AA3003-H14 aluminum using first toluol (M-14J242) and then acetone (M-1021). The strip may be considered free of oils and greases when there is no haze

12、remaining on the metal. Panels of AA-5052-H32, 0.030 in (0.76 mm) aluminum 2 x 9 in (50 x 230 mm) are prepared in the same manner. Apply the bonding tape (1 x 6 in (25 x 150 mm) strips) to the 2 x 9 in (50 x 230 mm) aluminum panel and carefully lay the 1 x 7 in (25 x 178 mm) aluminum strip over it.

13、Apply a pressure of 150 psi (1.0 MPa) to the bond line using a laboratory press or other suitable means and bring the bond line temperature to 197 C. Maintain at that temperature for 10 minutes. The above procedure will provide a bond area 1 x 6 in (25 x 150 mm). Peel the samples at a rate of 12 in

14、(305 mm) per minute. The load reading recorded is expressed as pounds per inch (or kg per mm) of width. No point shall fall beneath the minimum adhesion values indicated above. An average of 3 samples shall be used to obtain the results. Subject 3 specimens to each of the above aging tests. 3.9 FLAM

15、MABILITY, max 4 in (101 mm)/min (FLTM BN 024-02, without the lot sampling plan) In addition, the test specimen shall not exhibit any flashing or sudden flaming on either surface in excess of the above max value. 5. GENERAL INFORMATION The information given below is provided for clarification and ass

16、istance in meeting the requirements of this specification. 5.1 SOLVENT RESISTANCE The cured film shall not soften, swell or dissolve when immersed for 5 minutes in aliphatic hydrocarbons (light petroleum naphtha, M-14J147 or M-14J148) or aromatic solvents such as toluol or xylol, M-14J242 or M-14M245.