FORD ESB-M1G158-B-2013 FABRIC VINYL COATED - CARPET BINDING TO BE USED WITH FORD WSS-M99P1111-A .pdf

《FORD ESB-M1G158-B-2013 FABRIC VINYL COATED - CARPET BINDING TO BE USED WITH FORD WSS-M99P1111-A .pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M1G158-B-2013 FABRIC VINYL COATED - CARPET BINDING TO BE USED WITH FORD WSS-M99P1111-A .pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2013 10 31 N Status No usage or replacement named L. Sinclair, NA 2003 01 23 Revised Para 3.0 inserted ; Para 3.1, 3.6, 4 deleted 1979 07 11 Metricated, Renumbered and Retyped CAH1-RD572066-22 1971 08 18 Rel

2、eased AB1-30215 Page 1 of 2 Copyright 2013, Ford Global Technologies, Inc. FABRIC, VINYL COATED - CARPET BINDING ESB-M1G158-B NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a bias cut vinyl coated fabric (ESB-M2F67 quality). 2. APPLICATION This specification was

3、 released originally for material used as sewn edge binding for automotive carpet employed for trim applications on door and quarter panels. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For

4、 Production Materials (WSS-M99P1111-A). 3.2 APPEARANCE The color, pattern, and finish shall match the approved Design Center master sample, or shall be as specified on the engineering drawing. 3.3 CONSTRUCTION The material shall consist of a 1-3/4 in (44 mm) width bias cut (30 to 60 angle from selva

5、ge edge) ESB-M2F6-B and sewn or cemented (ESB-M2G82, or equivalent adhesive) as required. 3.4 MILDEW RESISTANCE Production roll of the binding shall exhibit no evidence of mildew growth after 7 days at 98 +/- 2% relative humidity 38 +/- 1 C. 3.5 ESB-M1G158-B FLAMMABILITY 3.5.1 In order to comply wit

6、h Federal Motor Vehicle Safety Standard No. 302, the materials, portions of components, and composites shall not burn, or transmit a flame across its surface, at a rate of more than 4 in (101 mm) per min. To demonstrate compliance, the sample size and method of testing shall be in accordance with FL

7、TM BN 24-2. ENGINEERING MATERIAL SPECIFICATION ESB-M1G158-B Page 2 of 2 Copyright 2002 Ford Global Technologies, Inc. 3.5.2 Performance - Environmental Aging All materials, portions of components, and composites defined by this specification that have not been treated, modified or reformulated and e

8、xceed a max burn rate of 3.0 in (76 mm) per min as specified by the Flammability Lot Sampling Plan of FLTM BN 24-2, must be evaluated for permanency of the materials flame retardant properties per ESB-M25P3-A according to the accelerated environmental aging requirements applicable to the basic mater

9、ial category of this particular specification. Any material, portions of components, and composites defined by this specification that have been treated, modified or reformulated to conform to Flammability Lot Sampling Plan of FLTM BN 24-2, regardless of max burn rate, must be evaluated for both per

10、manency of materials flame retardant properties and changes in mechanical, chemical and physical properties per ESB-M25P3-A applicable to the basic materials category of this particular specification. 3.5.3 Flammability Test Program Materials, portions of components, and composites governed by this specification must also comply with the requirements of ES-D3AB-11014-AA.