FORD ESB-M1C31-B-2008 GREASE HIGH TEMPERATURE WATERPROOF WITH FILLER NLGI #1 TO BE USED WITH FORD WSS-M99P1111-A 《NLGI含填料的防水、耐高温润滑脂》.pdf

《FORD ESB-M1C31-B-2008 GREASE HIGH TEMPERATURE WATERPROOF WITH FILLER NLGI #1 TO BE USED WITH FORD WSS-M99P1111-A 《NLGI含填料的防水、耐高温润滑脂》.pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M1C31-B-2008 GREASE HIGH TEMPERATURE WATERPROOF WITH FILLER NLGI #1 TO BE USED WITH FORD WSS-M99P1111-A 《NLGI含填料的防水、耐高温润滑脂》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 10 09 N-STATUS Replaced by WSS-M13P12-A / WSS-M13P13-A L. Schmalz, FNA 2003 10 20 Revised Updated format 1963 06 25 Released ASI #948 Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, Inc. Page 1 of 2 GREASE, HIGH

2、TEMPERATURE, WATERPROOF WITH ESB-M1C31-B FILLER, NLGI #1 NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a lithium soap, mineral oil, white, waterproof, high temperature grease, with zinc oxide filler. 2. APPLICATION This specification was released originally for

3、 grease used as a lubricant for automotive parts requiring resistance to water and high temperatures. It is not recommended for applications on or near painted interior or exterior automotive finishes. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part pro

4、ducers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 COLOR Amber 3.3 BASE 3.3.1 Lithium Soap 4.0 - 10.0% (ASTM D 128) 3.3.2 Filler, as Zinc Oxide or a combination 8.0% of Zinc Oxide and titanium dioxide, min 3.4 MINERAL OIL Remainder 3.5 DROPPING P

5、OINT, min 175 C (ASTM D 566 or D 2265) 3.6 PENETRATION 310 - 340 (ASTM D 217, worked 60 strokes) ENGINEERING MATERIAL SPECIFICATIONESB-M1C31-B Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, Inc. Page 2 of 2 3.7 OXIDATION STABILITY, PRESSURE DROP, max 69 kPa (ASTM D 942, 10

6、0 h at 100 C) 3.8 WATER SOLUBILITY The material, when applied to metal strips prepared per FLTM BJ 106-01, at a thickness of 1.6 mm, shall withstand 168 h at 38 +/- 1 C in a 98 +/- 2% relative humidity atmosphere without breaking. 3.10 QUALITY Material shall be a smooth homogeneous product free from

7、 abrasive particles, it shall be consistent in color and texture, and free from objectionable odors during normal storage. It shall be suit-able for the intended application. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements o

8、f this specification. 5.1 MINERAL OIL PROPERTY 5.1.1 Viscosity at 40 C, min 76.5 mm2/s (ASTM D 445) 5.2 The following parameters are recommended for the Quality Certification Requirements of para 3.1: 5.2.1 Infrared Analysis, para 3.2 of WSS-M99P1111-A. 5.2.2 Penetration, para 3.6. 5.2.3 Dropping Point, para 3.5.