FORD ESB-M1C163-C-2012 GREASE CALCIUM 12 HYDROXY STEARATE LOW TEMPERATURE NLGI 2 TO BE USED WITH FORD WSS-M99P1111-A 《低温硬脂酸钙12羟基润滑脂 美国润滑脂协会2 与福特WSS-M99P1111-A 一起使用》.pdf

《FORD ESB-M1C163-C-2012 GREASE CALCIUM 12 HYDROXY STEARATE LOW TEMPERATURE NLGI 2 TO BE USED WITH FORD WSS-M99P1111-A 《低温硬脂酸钙12羟基润滑脂 美国润滑脂协会2 与福特WSS-M99P1111-A 一起使用》.pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M1C163-C-2012 GREASE CALCIUM 12 HYDROXY STEARATE LOW TEMPERATURE NLGI 2 TO BE USED WITH FORD WSS-M99P1111-A 《低温硬脂酸钙12羟基润滑脂 美国润滑脂协会2 与福特WSS-M99P1111-A 一起使用》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2012 02 17 N Status No replacement named A. Wedepohl, NA 2004 03 16 Revised Para 3.0 inserted; para 3.1, 3.2, 3.3, 3.15 & 4 deleted 1991 09 04 NB00I10043054119 Released R.D. Moore DRB LM Controlled document at www.MATS Copyright 2012, Ford Gl

2、obal Technologies, LLC Page 1 of 2 GREASE, CALCIUM 12 HYDROXY STEARATE, LOW ESB-M1C163-C TEMPERATURE, NLGI 2 NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a low temperature lubricant containing a calcium 12 hydroxy stearate thickener with lubricating oils and n

3、ecessary rust and oxidation inhibitors. The lubricant operating temperatures range from - 46 C to 137 C. 2. APPLICATION This specification was released originally for grease used to lubricate body parts requiring a low temperature lubricant, such as window regulators and related hardware application

4、s. NOTICE: This grease shall be formulated so that it will not stain or soften painted exterior or interior automotive finishes, when evaluated according to FLTM BJ 126-01. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTD FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Co

5、mpanys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 COLOR Amber 3.5 SURFACE EXAMINATION No separation 3.6 CALCIUM 12 HYDROXY STEARATE CONTENT 8.0 - 13.0% (ASTM D 128) 3.7 MINERAL OIL Remainder 3.8 DROPPING POINT, min 138 C (ASTM D 566) 3.9 PENETRATION 265 - 295 (ASTM D 217, w

6、orked 60 strokes) 3.10 OXIDATION STABILITY, pressure drop, max 41 kPa (ASTM D 942, 100 h) 3.11 WATER WASHOUT, max 22.5 (ASTM D 1264, 80 C) 3.12 CORROSION 1 a (ASTM D 4048, 24 h at 50 C) ENGINEERING MATERIAL SPECIFICATION ESB-M1C163-C Copyright 2012, Ford Global Technologies, LLC Page 2 of 2 3.13 LUB

7、RICANT PAINT STAINING No stain or (FLTM BJ 126-01) softening 3.14 CONSISTENCY Material shall be a smooth homogeneous product free from abrasive particles, it shall be consistent in color and texture, and free from objectionable odors during normal storage. It shall be suitable for the intended appli

8、cation. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 MINERAL OIL PROPERTIES 5.1.1 Viscosity at 40 C 13.0 - 17.0 mm2/s (ASTM D 445) 5.1.2 Viscosity at 100 C 1.8 - 4.2 mm2/s (ASTM D 445) 5.1.3 Vis

9、cosity Index, min 15 (ASTM D 2270) 5.1.4 Pour Point, max - 45 C (ASTM D 97) 5.1.5 Flash Point, min 150 C (ASTM D 93) 5.1.6 Fire Point, min 170 C (ASTM D 93) 5.2 The following parameters are recommended for the Quality Certification Requirements: 5.2.1 Infrared Analysis 5.2.2 Penetration, para 3.9 5.2.3 Dropping Point, para 3.8