《FORD ESB-M1C161-B-2008 GREASE SYNTHETIC - HIGH TEMPERATURE TO BE USED WITH FORD WSS-M99P1111-A 《耐高温合成润滑 与标准FORD WSS-M99P1111-A一起使用 ［使用 FORD WSS-M13P12-A FORD WSS-M13P12-A FORD .pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M1C161-B-2008 GREASE SYNTHETIC - HIGH TEMPERATURE TO BE USED WITH FORD WSS-M99P1111-A 《耐高温合成润滑 与标准FORD WSS-M99P1111-A一起使用 ［使用 FORD WSS-M13P12-A FORD WSS-M13P12-A FORD .pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 10 10 N-STATUS Replaced by WSS-M13P12-A L. Schmalz, FNA 2004 03 16 Revised Para 3.0 inserted; para 3.1, 3.10, 3.11, 3.12 & 4 deleted 1971 06 11 AA1-6000-207 Released Printed copies are uncontrolled Copyright 2008, Ford Global Technologies

2、, LLC Page 1 of 2 GREASE, SYNTHETIC - HIGH TEMPERATURE ESB-M1C161-B NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a high temperature synthetic lubricant containing highly complex ashless organic thickeners with carefully selected lubricating oils and necessary

3、rust and oxidation inhibitors. The lubricant operating temperatures range from - 25 to 175 C. 2. APPLICATION This specification was released originally for grease used, after being reduced with a solvent (M14J167), to lubricate door latches installed prior to vehicle paint. Recommended solvent reduc

4、tion is 3.6 kg lubricant to 3.8 L of solvent to obtain a coating thickness of 0.25 - 0.30 mm after solvent flash off. NOTICE: This grease shall be formulated so that it will not stain or soften painted exterior or interior automotive finishes, when evaluated according to FLTM BJ 126-01. 3. REQUIREME

5、NTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 COLOR Light brown 3.3 SURFACE EXAMINATION Slight bleed 3.4 THICKENER Inorganic compound or equivalent to meet

6、 specification requirements 3.4.1 Thickener, by Weight 6.0 - 9.0% (ASTM D 128) 3.5 MINERAL OIL Remainder 3.6 DROPPING POINT, min 210 C (ASTM D 566) 3.7 PENETRATION 323 - 350 (ASTM D 217, worked 60 strokes) ENGINEERING MATERIAL SPECIFICATIONESB-M1C161-B Printed copies are uncontrolled Copyright 2008,

7、 Ford Global Technologies, LLC Page 2 of 2 3.8 CORROSION 1 (ASTM D 4048, 24 h at 50 C) 3.9 LUBRICANT PAINT STAINING No stain or (FLTM BJ 126-01) softening 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification

8、. 5.1 MINERAL OIL PROPERTIES 5.1.1 Viscosity at 40 C 81 - 99.7 mm2/s (ASTM D 445) 5.1.2 Viscosity at 100 C 9.3 - 11.7 (ASTM D 445) mm2/s 5.1.3 Viscosity Index, min 90 (ASTM D 2270) 5.1.4 Pour Point, max -23 C (ASTM D 97) 5.1.5 Flash Point, min 220 C (ASTM D 93) 5.1.6 Fire Point, min 246 C (ASTM D 93) 5.2 The following parameters are recommended for the Quality Certification Requirements: 5.2.1 Infrared Analysis 5.2.2 Penetration, para 3.7. 5.2.3 Dropping Point, para 3.6.