FORD ESA-M7C6-A-2012 RUST PREVENTIVE WATER EMULSION - WAX TYPE TO BE USED WITH FORD WSS-M99P1111-A 《水乳胶蜡制型防锈剂 与福特WSS-M99P1111-A 一起使用》.pdf

《FORD ESA-M7C6-A-2012 RUST PREVENTIVE WATER EMULSION - WAX TYPE TO BE USED WITH FORD WSS-M99P1111-A 《水乳胶蜡制型防锈剂 与福特WSS-M99P1111-A 一起使用》.pdf》由会员分享，可在线阅读，更多相关《FORD ESA-M7C6-A-2012 RUST PREVENTIVE WATER EMULSION - WAX TYPE TO BE USED WITH FORD WSS-M99P1111-A 《水乳胶蜡制型防锈剂 与福特WSS-M99P1111-A 一起使用》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev 03 2012 04 05 N Status No usage or replacement N. Benipal, NA 2004 03 26 Revised Para 3.0 inserted; paras 3.7 and 4 deleted 1964 07 17 Released AS2-474 Controlled document at www.MATS Copyright 2012, Ford Global Technologies, LLC Page 1 o

2、f 2 RUST PREVENTIVE, WATER EMULSION - WAX TYPE ESA-M7C6-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a rust preventive which is in a water suspension and gives an adherent wax film. 2. APPLICATION This specification was released originally for material used

3、to protect ferrous metal surfaces. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 FORMULATION This material shall consist of waxes, fats, grease

4、s, wetting agents and couplers, which will make a stable, protective coating meeting the requirements of this specification. 3.2 APPLICATION CHARACTERISTICS This material shall be suitable for application by spraying or brushing and shall be readily removed by washing with mineral spirits. The mater

5、ial can be used as received or diluted up to two parts water to one part of rust preventive, dependent upon the coating thickness desired. 3.3 FILM CHARACTERISTICS This material shall form a homogenous stable, non-corrosive protective film, free of sediment or other contaminants. 3.4 COMPOSITION REQ

6、UIREMENTS 3.4.1 Water Content, max 64% 3.4.2 pH, as received 8.0 - 9.5 3.4.3 Melting Point of Residue 72 C - 76 C 3.5 CORROSION REQUIREMENT No rust after (FLTM BJ 107-03) 2,000 h 3.6 FILM FLOW TEST The film shall show no evidence of flow. 3.6.1 Test Method: Brush on polished steel panels the materia

7、l as received and air dry 24 hours; hang vertically in oven at 70 C for 24 hours. Examine for flow. ENGINEERING MATERIAL SPECIFICATION ESA-M7C6-A Copyright 2012, Ford Global Technologies, LLC Page 2 of 2 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. This material is not to be used on parts that are to be subsequently painted. Note: Similar to M7C6-A