EN ISO 11126-9-2004 en Preparation of steel substrates before application of paints and related products - Specifications for non-metallic blast-cleaning abrasives - Part 9 Staurol.pdf

《EN ISO 11126-9-2004 en Preparation of steel substrates before application of paints and related products - Specifications for non-metallic blast-cleaning abrasives - Part 9 Staurol.pdf》由会员分享，可在线阅读，更多相关《EN ISO 11126-9-2004 en Preparation of steel substrates before application of paints and related products - Specifications for non-metallic blast-cleaning abrasives - Part 9 Staurol.pdf（12页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD BS EN ISO 11126-9:2004 BS 7079-F9: 2004 Incorporating Amendment No. 1 to BS 7079-F9:1999 (renumbers the BS as BS EN ISO 11126-9:2004) Preparation of steel substrates before application of paints and related products Specification for non-metallic blast-cleaning abrasives Part 9: Sta

2、urolite The European Standard EN ISO 11126-9:2004 has the status of a British Standard ICS 25.220.10 BS EN ISO 11126-9:2004 This British Standard, having been prepared under the direction of the Sector Committee for Materials and Chemicals, was published under the authority of the Standards Committe

3、e and comes into effect on 15 August 1999 BSI 25 April 2005 ISBN 0 580 32928 3 National foreword This British Standard is the official English language version of EN ISO 11126-9:2004. It is identical with ISO 11126-9:1999. The UK participation in its preparation was entrusted to Technical Committee

4、STI/21, Surface preparation of steel, which has the responsibility to: aid enquirers to understand the text; present to the responsible international/European committee any enquiries on the interpretation, or proposals for change, and keep the UK interests informed; monitor related international and

5、 European developments and promulgate them in the UK. A list of organizations represented on this committee can be obtained on request to its secretary. Cross-references The British Standards which implement international or European publications referred to in this document may be found in the BSI

6、Catalogue under the section entitled “International Standards Correspondence Index”, or by using the “Search” facility of the BSI Electronic Catalogue or of British Standards Online. This publication does not purport to include all the necessary provisions of a contract. Users are responsible for it

7、s correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a front cover, an inside front cover, the EN ISO title page, the EN ISO foreword page, the ISO title page, page ii, pages 1 to 4, an inside ba

8、ck cover and a back cover. The BSI copyright notice displayed throughout this document indicates when the document was last issued. Amendments issued since publication Amd. No. Date Comments 15512 25 April 2005 Implementation of the European Standard.EUROPEANSTANDARD NORMEEUROPENNE EUROPISCHENORM EN

9、ISO111269 December2004 ICS25.220.10 Englishversion Preparationofsteelsubstratesbeforeapplicationofpaintsand relatedproductsSpecificationsfornonmetallicblastcleaning abrasivesPart9:Staurolite(ISO111269:1999) Prparationdessubjectilesdacieravantapplicationde peinturesetdeproduitsassimilsSpcificationspo

10、ur abrasifsnonmtalliquesdestinslaprparationpar projectionPartie9:Staurolite(ISO111269:1999) VorbereitungvonStahloberflchenvordemAuftragenvon BeschichtungsstoffenAnforderungenannichtmetallische StrahlmittelTeil9:Staurolith(ISO111269:1999) ThisEuropeanStandardwasapprovedbyCENon21December2004. CENmembe

11、rsareboundtocomplywiththeCEN/CENELECInternalRegulationswhichstipulatetheconditionsforgivingthisEurope an Standardthestatusofanationalstandardwithoutanyalteration.Uptodatelistsandbibliographicalreferencesconcernings uchnational standardsmaybeobtainedonapplicationtotheCentralSecretariatortoanyCENmembe

12、r. ThisEuropeanStandardexistsinthreeofficialversions(English,French,German).Aversioninanyotherlanguagemadebytra nslation undertheresponsibilityofaCENmemberintoitsownlanguageandnotifiedtotheCentralSecretariathasthesamestatusast heofficial versions. CENmembersarethenationalstandardsbodiesofAustria,Bel

13、gium,Cyprus,CzechRepublic,Denmark,Estonia,Finland,France, Germany,Greece,Hungary,Iceland,Ireland,Italy,Latvia,Lithuania,Luxembourg,Malta,Netherlands,Norway,Poland,Portugal, Slovakia, Slovenia,Spain,Sweden,SwitzerlandandUnitedKingdom. EUROPEANCOMMITTEEFORSTANDARDIZATION COMITEUROPENDENORMALISATION EU

14、ROPISCHESKOMITEEFRNORMUNG ManagementCentre:ruedeStassart,36B1050Brussels 2004CEN Allrightsofexploitationinanyformandbyanymeansreserved worldwideforCENnationalMembers. Ref.No.ENISO111269:2004:E Foreword The text of ISO 11126-9:1999 has been prepared by Technical Committee ISO/TC 35 “Paints and varnis

15、hes” of the International Organization for Standardization (ISO) and has been taken over as EN ISO 11126-9:2004 by Technical Committee CEN/TC 139 “Paints and varnishes“, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by public

16、ation of an identical text or by endorsement, at the latest by June 2005, and conflicting national standards shall be withdrawn at the latest by June 2005. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this E

17、uropean Standard: Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. Endorsemen

18、t notice The text of ISO 11126-9:1999 has been approved by CEN as EN ISO 11126-9:2004 without any modifications. ENISO111269:2004ENISO111269:2004EN ISO 11126-9:2004 ii BSI 25 April 2005 Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards

19、bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizat

20、ions, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rules given in th

21、e ISO/IEC Directives, Part 3. Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. International Standard ISO 11126-9 was prep

22、ared by Technical Committee ISO/TC 35, Paints and varnishes, Subcommittee SC 12, Preparation of steel substrates before application of paints and related products. ISO 11126 consists of the following parts, under the general title Preparation of steel substrates before application of paints and rela

23、ted products Specifications for non-metallic blast-cleaning abrasives: Part 1: General introduction and classification; Part 3: Copper refinery slag; Part 4: Coal furnace slag; Part 5: Nickel refinery slag; Part 6: Iron furnace slag; Part 7: Fused aluminium oxide; Part 8: Olivine sand; Part 9: Staur

24、olite; Part 10: Almandite garnet. At the time of publication of this part of ISO 11126, part 10 was in the course of preparation. Part 2 has been deleted.EN ISO 11126-9:2004 BSI 25 April 2005 1 WARNING Equipment, materials and abrasives used for surface preparation can be hazardous if used carelessl

25、y. Many national regulations exist for those materials and abrasives that are considered to be hazardous during or after use (waste management), such as free silica or carcinogenic or toxic substances. These regulations are therefore to be observed. It is important to ensure that adequate instructio

26、ns are given and that all required precautions are exercised. 1 Scope This part of ISO 11126 specifies requirements for staurolite abrasives, as supplied for blast-cleaning processes. It specifies ranges of particle sizes and values for apparent density, Mohs hardness, moisture content, conductivity

27、 of aqueous extract and water-soluble chlorides. The requirements specified in this part of ISO 11126 apply to abrasives supplied in the “new” condition only. They do not apply to abrasives either during or after use. Test methods for non-metallic blast-cleaning abrasives are given in the various pa

28、rts of ISO 11127. NOTE 1 Information on commonly referenced national standards for non-metallic abrasives is given in Annex A. NOTE 2 Although this part of ISO 11126 has been developed specifically to meet requirements for preparation of steelwork, the properties specified will generally be appropri

29、ate for use when preparing other material surfaces, or components, using blast-cleaning techniques. These techniques are described in ISO 8504-2:1992. Preparation of steel substrates before application of paints and related products Surface preparation methods Part 2: Abrasive blast-cleaning. 2 Norm

30、ative references The following normative documents contain provisions which, through reference in this text, constitute provisions of this part of ISO 11126. For dated references, subsequent amendments to, or revisions of, any of these publications do not apply. However, parties to agreements based

31、on this part of ISO 11126 are encouraged to investigate the possibility of applying the most recent editions of the normative documents indicated below. For undated references, the latest edition of the normative document referred to applies. Members of ISO and IEC maintain registers of currently va

32、lid International Standards. ISO 11127-1:1993, Preparation of steel substrates before application of paints and related products Test methods for non-metallic blast-cleaning abrasives Part 1: Sampling ISO 11127-2:1993, Preparation of steel substrates before application of paints and related products

33、 Test methods for non-metallic blast-cleaning abrasives Part 2: Determination of particle size distribution ISO 11127-3:1993, Preparation of steel substrates before application of paints and related products Test methods for non-metallic blast-cleaning abrasives Part 3: Determination of apparent den

34、sity ISO 11127-4:1993, Preparation of steel substrates before application of paints and related products Test methods for non-metallic blast-cleaning abrasives Part 4: Assessment of hardness by a glass slide test ISO 11127-5:1993, Preparation of steel substrates before application of paints and rela

35、ted products Test methods for non-metallic blast-cleaning abrasives Part 5: Determination of moisture ISO 11127-6:1993, Preparation of steel substrates before application of paints and related products Test methods for non-metallic blast-cleaning abrasives Part 6: Determination of water-soluble cont

36、aminants by conductivity measurement ISO 11127-7:1993, Preparation of steel substrates before application of paints and related products Test methods for non-metallic blast-cleaning abrasives Part 7: Determination of water-soluble chlorides 3 Term and definition For the purposes of this part of ISO

37、11126, the following term and definition apply. 3.1 staurolite a material manufactured from the naturally occurring mineral staurolite which is washed, dried, sieved, magnetically separated, and prepared for use as a blast-cleaning abrasive NOTE Staurolite is an iron/aluminium silicate with the appr

38、oximate chemical formula FeAl 5 SiO 12 OH.EN ISO 11126-9:2004 2 BSI 25 April 2005 4 Designation of abrasives Staurolite sand abrasives shall be identified by “Abrasive ISO 11126” and the abbreviation N/ST indicating non-metallic staurolite abrasive. This shall be followed, without spaces, by an obli

39、que stroke, and then the symbol S to indicate the required particle shape of the abrasive, when purchased, as shot. The designation shall be completed by numbers denoting the particle size range, in millimetres, required (see Table 1). NOTE Although staurolite is designated as a shot material, the g

40、rit comparator is used when assessing the profile produced. This is due to it having an irregular grain shape. EXAMPLE Abrasive ISO 11126 N/ST/S 0,20,6 denotes an abrasive of the non-metallic staurolite type, complying with the requirements of this part of ISO 11126, of initial particle shape shot a

41、nd particle size range 0,2 to 0,6 mm. It is essential that this full product designation is quoted on all orders. 5 Sampling Sampling procedures shall be as specified in ISO 11127-1. 6 Requirements 6.1 General requirements Staurolite abrasives shall be free from corrosive constituents and adhesion-i

42、mpairing contaminants. Foreign, harmful impurities shall not be permitted. Silica in staurolite abrasives shall be present as bonded silicate. 6.2 Particular requirements Particular requirements for staurolite abrasives shall be as specified in Table 2. 7 Identification and marking All materials sha

43、ll be clearly marked or identified using the appropriate designation as specified in Clause 4, either directly or by the accompanying delivery note. 8 Information to be supplied by the manufacturer or supplier The manufacturer or supplier shall supply, if requested, a test report detailing results f

44、or any relevant property as determined by the appropriate method specified in Table 2. Table 1 Particle size distribution Particle size range a 0,1 to 0,3 0,1 to 0,4 0,2 to 0,6 mm Oversize Sieve size mm 0,3 0,4 0,6 Residue, % (m/m)m a x . 1 01 01 0 Nominal size Sieve size mm 0,1 0,1 0,2 Residue, % (

45、m/m)m i n . 8 58 58 5 Undersize Sieve size mm 0,1 0,1 0,2 Through-flow, % (m/m)m a x .555 a By agreement between the interested parties, abrasives of different particle size ranges may be mixed together. Details of proportions of nominal size, oversize and undersize shall be specified. The maximum p

46、article size shall not exceed 3,15 mm and the proportion of particles less than 0,1 mm shall not exceed 5 % (m/m).EN ISO 11126-9:2004 BSI 25 April 2005 3 Table 2 Particular requirements for staurolite abrasives Property Requirement Test method Particle size range and distribution See Table 1 ISO 111

47、27-2 Apparent density kg/m 3 (3,6 to 3,7) 10 3 ISO 11127-3 kg/dm 3 3,6 to 3,7 Mohs hardness a min. 6 ISO 11127-4 Moisture % (m/m) max. 0,2 ISO 11127-5 Conductivity of aqueous extract mS/m max. 25 ISO 11127-6 Water-soluble chlorides % (m/m) max. 0,002 5 ISO 11127-7 a Another method of assessing hardn

48、ess may be used, together with an appropriate minimum requirement, by agreement between the interested parties.EN ISO 11126-9:2004 4 BSI 25 April 2005 Bibliography Commonly referenced national standards for non-metallic abrasives are as follows: 1 DIN 8200:1982, Strahlverfahrenstechnik; Begriffe, Einordnung der Strahlverfahren (Blasting; terms, classification of blasting techniques). 2 DIN 8201-5:1985, Feste Strahlmittel, natrlich, mineralisch; Qu