EN 1373-2015 en Adhesives - Test method for adhesives for floor and wall coverings - Shear test《胶粘剂 地板和墙壁覆盖物胶粘剂的测试方法 剪切试验》.pdf

《EN 1373-2015 en Adhesives - Test method for adhesives for floor and wall coverings - Shear test《胶粘剂 地板和墙壁覆盖物胶粘剂的测试方法 剪切试验》.pdf》由会员分享，可在线阅读，更多相关《EN 1373-2015 en Adhesives - Test method for adhesives for floor and wall coverings - Shear test《胶粘剂 地板和墙壁覆盖物胶粘剂的测试方法 剪切试验》.pdf（14页珍藏版）》请在麦多课文档分享上搜索。

1、BSI Standards PublicationBS EN 1373:2015Adhesives Test method foradhesives for floor and wallcoverings Shear testBS EN 1373:2015 BRITISH STANDARDNational forewordThis British Standard is the UK implementation of EN 1373:2015. Itsupersedes BS EN 1373:2000 which is withdrawn.The UK participation in it

2、s preparation was entrusted to TechnicalCommittee PRI/52, Adhesives.A list of organizations represented on this committee can beobtained on request to its secretary.This publication does not purport to include all the necessaryprovisions of a contract. Users are responsible for its correctapplicatio

3、n. The British Standards Institution 2015. Published by BSI StandardsLimited 2015ISBN 978 0 580 85707 2ICS 83.180Compliance with a British Standard cannot confer immunity fromlegal obligations.This British Standard was published under the authority of theStandards Policy and Strategy Committee on 30

4、 April 2015.Amendments issued since publicationDate Text affectedBS EN 1373:2015EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 1373 April 2015 ICS 83.180 Supersedes EN 1373:1999English Version Adhesives - Test method for adhesives for floor and wall coverings - Shear test Adhsifs - Mthodes des

5、sais dadhsifs pour revtements de sol et muraux - Essai de cisaillement Klebstoffe - Prfverfahren fr Klebstoffe fr Boden- und Wandbelge - Scherversuch This European Standard was approved by CEN on 16 February 2015. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipul

6、ate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European St

7、andard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the n

8、ational standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania,

9、Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2015 CEN All rights of exploitation in any form and by any

10、means reserved worldwide for CEN national Members. Ref. No. EN 1373:2015 EBS EN 1373:2015EN 1373:2015 (E) 2 Contents Page Foreword 3 1 Scope 4 2 Normative references 4 3 Terms and definitions .4 4 Principle 4 5 Apparatus and materials .5 6 Preparation of the test specimens .6 6.1 Cleaning 6 6.2 Samp

11、ling of adhesive 6 6.3 Conditioning of materials .6 6.3.1 Adhesive and floor and wall coverings .6 6.3.2 Fibre cement substrate .6 6.3.3 Plywood substrates .7 6.4 Application of adhesive 7 6.5 Bonding of the test covering 7 7 Conditioning of the test specimens .8 8 Test procedure .8 9 Evaluation and

12、 expression of results 9 10 Test report 9 BS EN 1373:2015EN 1373:2015 (E) 3 Foreword This document (EN 1373:2015) has been prepared by Technical Committee CEN/TC 193 “Adhesives”, the secretariat of which is held by AENOR. This European Standard shall be given the status of a national standard, eithe

13、r by publication of an identical text or by endorsement, at the latest by October 2015 and conflicting national standards shall be withdrawn at the latest by October 2015. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or

14、 CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 1373:1999. The main changes in respect to EN 1373:1999 are the addition of a plywood substrate and the change of the roller dimensions. SAFETY PRECAUTIONS Persons using this document sho

15、uld be familiar with the normal laboratory practice, if applicable. This document does not purport to address all of the safety problems, if any, associated with its use. It is the responsibility of the user to establish appropriate safety and health practices and to ensure compliance with any regul

16、atory conditions. According to the CEN-CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Mace

17、donia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. BS EN 1373:2015EN 1373:2015 (E) 4 1 Scope This European Standard spec

18、ifies a test method to measure the adhesion of a resilient or textile floor covering or wall covering bonded to a given substrate under shear forces. The term “wall covering” does not include any type of wallpaper. 2 Normative references The following documents, in whole or in part, are normatively

19、referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 923:2005+A1:2008, Adhesives - Terms and definitions EN 1067, Adhes

20、ives - Examination and preparation of samples for testing EN ISO 7500-1, Metallic materials - Verification of static uniaxial testing machines - Part 1: Tension/compression testing machines - Verification and calibration of the force-measuring system (ISO 7500-1) EN ISO 9142, Adhesives - Guide to th

21、e selection of standard laboratory ageing conditions for testing bonded joints (ISO 9142) EN ISO 10365, Adhesives - Designation of main failure patterns (ISO 10365) EN ISO 15605, Adhesives - Sampling (ISO 15605) ISO 554, Standard atmospheres for conditioning and/or testing - Specifications ISO 3205,

22、 Preferred test temperatures 3 Terms and definitions For the purposes of this document, the terms and definitions given in EN 923:2005+A1:2008 and the following apply. 3.1 covering flexible resilient or textile floor covering or wall covering 3.2 adhesive for coverings adhesive which is intended to

23、produce firm and durable bonds between coverings and various substrates 4 Principle The adhesion is determined by measuring the shear strength under specified conditions before and after storing the bonds at 23 C/ 50 C under specified conditions. BS EN 1373:2015EN 1373:2015 (E) 5 5 Apparatus and mat

24、erials 5.1 Notched trowel (for the shape of the notch, see Figure 1) with dimensions a, b and c specified by the adhesive manufacturer. Key a notch depth b notch width c notch distance Figure 1 Shape of notches of notched trowel 5.2 Roller, of width (60 5) mm, diameter (90 5) mm and total mass (3,50

25、 0,05) kg with handle at 90 to the axis (as an example, see Figure 2). Dimensions in millimetres Figure 2 Roller NOTE The length of the handle is not critical and can be used for setting the total mass. BS EN 1373:2015EN 1373:2015 (E) 6 5.3 Heating chamber, ventilated and adjustable to a temperature

26、 between 20 C and 200 C according to EN ISO 9142. 5.4 Tensile testing machine, conforming to EN ISO 7500-1, class 1. 5.5 Primer, if applicable. 5.6 Test covering, five test pieces for each conditioning sequence of dimensions 60 mm 50 mm, the long side, running in the machine direction where this can

27、 be identified, and shall be taken at least 10 mm from the edge. 5.7 Substrate materials: Use either fibre cement or plywood as the substrate. 5.7.1 Fibre cement substrate, one uncoated fibre cement panel, fully compressed and autoclaved, for each test piece. Five fibre cement panels for each condit

28、ioning sequence with a length of approximately 60 mm and a thickness of approximately 8,0 mm. The width is (50 0,5) mm. NOTE 1 Length and thickness are not critical. NOTE 2 Depending on the source of the fibre cement panels the surfaces sometimes differ with respect to gloss, absorbency and strength

29、. In this case, it is important to do some preliminary assessment (i.e. peel tests) of the panels to identify the preferred side for testing. The preferred side will be called the upper side of the substrate in this standard. If failure of the substrate is the main finding of the preliminary assessm

30、ent, a suitable primer may be used for testing. 5.7.2 Plywood substrate, one uncoated plywood panel for each test piece. Five plywood panels for each conditioning sequence with a length of approximately 60 mm and a thickness of approximately 5,0 mm. The width is (50 0,5) mm. NOTE Length and thicknes

31、s are not critical. 6 Preparation of the test specimens 6.1 Cleaning Ensure that all test coverings and substrate materials are clean and free from dust, loose particles or other contamination. 6.2 Sampling of adhesive Take a sample in accordance with EN ISO 15605 of the adhesive to be tested and ex

32、amine and prepare it in accordance with EN 1067. 6.3 Conditioning of materials 6.3.1 Adhesive and floor and wall coverings Condition the materials at a standard atmosphere of (23 2) C and (50 5) % relative humidity in accordance with ISO 554 for at least 24 h prior to use. 6.3.2 Fibre cement substra

33、te Place the test panels (5.7.1) in a heating chamber (5.3) for 6 h at (80 2) C. Ensure that the test panels are spaced in such a way as to enable a free passage of air over them. At the end of this period, remove the test BS EN 1373:2015EN 1373:2015 (E) 7 panels from the heating chamber and store f

34、or 48 h in a standard atmosphere of (23 2) C and (50 5) % relative humidity prior to use. 6.3.3 Plywood substrates Condition the materials at a standard atmosphere of (23 2) C and (50 5) % relative humidity in accordance with ISO 554 for at least 24 h prior to use. 6.4 Application of adhesive Place

35、masking tape across one end of the upper side of each substrate so as to leave 20 mm length to be coated with adhesive. Apply the adhesive under test across the full width of the substrate using a notched trowel (5.1), held at an angle of approximately 60, steadily down the length of the substrate t

36、o provide a uniform adhesive application. Remove the masking tape when the adhesive has been applied. When applying the adhesive, it is essential that the serrated blade is kept clean and free of adhesive build-up. Clean the blade regularly (no more than five substrates to be prepared without cleani

37、ng). In addition, regularly check the notch size and depth, especially where non-hardened steel blades are in use. 6.5 Bonding of the test covering After a time recommended by the adhesive manufacturer (i.e. minimum open time in accordance with EN 923), place the test covering (see 5.6) onto the coa

38、ted panel (5.7) to provide an overlap of 20 mm such that the unbonded length protrudes from the edge of the panel coated with adhesive (see Figure 3). Dimensions in millimetres Figure 3 Shear test specimen Immediately after positioning the test covering, roll the test specimen with a roller (see 5.2

39、) by passing forward and backward once along the test specimen without any additional pressure being applied. As the adhesive has not yet set it should be ensured that the overlapping area remains 20 mm x 50 mm without any shift during the subsequent treatments of the test coverings. Before applying

40、 the roller it is advisable to support the unbonded area of the test covering by an additional panel of the same thickness in order to avoid tilting. To prevent the test covering from slipping caused by the roller an appropriate frame or mould for the substrate sheets in combination with range space

41、rs can be used for the covering. BS EN 1373:2015EN 1373:2015 (E) 8 For coverings which show a tendency to curl after rolling, a dead load of (2,0 0,1) kg mass can be applied for (3,0 0,5) h. The load is spread evenly over the whole surface thus ensuring a contact over the total bonded area of each t

42、est specimen. The procedure applied should be recorded in the test report see 10 i). 7 Conditioning of the test specimens After assembly, expose the test specimens to the conditions as given in Table 1. Table 1 Conditioning Control test Test I Test II a28 days at a standard atmosphere of 23/50 (see

43、ISO 554) 7 days at a standard atmosphere of 23/50 (see ISO 554) 20 days at (50 2) C (see ISO 3205) 41 days at (50 2) C (see ISO 3205) 1 day at a standard atmosphere of 23/50 (see ISO 554) aThis test to be optional for determining the effect of any type of interaction between an adhesive and a coveri

44、ng.8 Test procedure Clamp the ends of the test specimen in appropriate clamps of the tensile testing machine (5.4) using packings to ensure that the axis of the test specimen is aligned with the direction of the clamp movement (see Figure 4). Dimensions in millimetres Key 1 uncoated panel 2 packing

45、3 covering Figure 4 Clamping of shear test specimens Set the tensile testing machine to operate with a crosshead movement of (20 2) mm/min. BS EN 1373:2015EN 1373:2015 (E) 9 9 Evaluation and expression of results Shear strength in newtons per square millimetre N/mm2 is the maximum shear force in new

46、tons N during separation of the bond divided by the area of overlap in square millimetres mm2: max =FAWhere is shear strength; Fmaxis maximum shear force during separation N; A is area of overlap mm2. Record the shear strength for each test specimen, the type of failure in accordance with EN ISO 103

47、65 and calculate the mean value of all five test specimens. Any result which differs by more than 15 % from this value shall be discarded and a second mean value calculated from the remaining results. If more than 2 results are outside the range, discard the highest and the lowest value and calculat

48、e the mean of the remaining three results. 10 Test report The test report shall include at least the following: a) reference to this European Standard, i.e. EN 1373; b) designation of the adhesive together with the batch number; c) designation of test covering, substrate and primer optional used for

49、 substrate preparation; d) notched trowel used; e) open time allowed; f) conditioning sequences used; g) mean shear strength in N/mm2for each conditioning sequence and the type of failure according to EN ISO 10365, e.g. failure in adhesion, in cohesion of adhesive or in adherent; h) any physical changes or abnormalities observed in the bonded test specimen after accelerated ageing conditions; i) any factors that have affected the result; j) date of the test. This page deliberately left blankThis