EN 10263-3-2017 en Steel rod bars and wire for cold heading and cold extrusion - Part 3 Technical delivery conditions for case hardening steels.pdf

《EN 10263-3-2017 en Steel rod bars and wire for cold heading and cold extrusion - Part 3 Technical delivery conditions for case hardening steels.pdf》由会员分享，可在线阅读，更多相关《EN 10263-3-2017 en Steel rod bars and wire for cold heading and cold extrusion - Part 3 Technical delivery conditions for case hardening steels.pdf（22页珍藏版）》请在麦多课文档分享上搜索。

1、Steel rod, bars and wire for cold heading and cold extrusionPart 3: Technical delivery conditions for case hardening steelsBS EN 10263-3:2017BSI Standards PublicationWB11885_BSI_StandardCovs_2013_AW.indd 1 15/05/2013 15:06EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 10263-3 November 2017 ICS

2、 77.140.60; 77.140.65 Supersedes EN 10263-3:2001English Version Steel rod, bars and wire for cold heading and cold extrusion - Part 3: Technical delivery conditions for case hardening steels Barres, fil machine et fil en acier pour transformation froid froid et extrusion froid - Partie 3: Conditions

3、 techniques de livraison des aciers de cmentation Walzdraht, Stbe und Draht aus Kaltstauch- und Kaltfliepresssthlen - Teil 3: Technische Lieferbedingungen fr Einsatzsthle This European Standard was approved by CEN on 26 July 2017. CEN members are bound to comply with the CEN/CENELEC Internal Regulat

4、ions which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member.

5、 This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN

6、members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Po

7、rtugal, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2017 CEN All rights of exploitatio

8、n in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 10263-3:2017 ENational forewordThis British Standard is the UK implementation of EN 10263-3:2017. It supersedes BS EN 10263-3:2001, which is withdrawn.The UK participation in its preparation was entrusted to Tech

9、nical Committee ISE/106, Wire Rod and Wire.A list of organizations represented on this committee can be obtained on request to its secretary.This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application. The British Standar

10、ds Institution 2017 Published by BSI Standards Limited 2017ISBN 978 0 580 85296 1ICS 77.140.65; 77.140.60Compliance with a British Standard cannot confer immunity from legal obligations. This British Standard was published under the authority of the Standards Policy and Strategy Committee on 30 Nove

11、mber 2017.Amendments/corrigenda issued since publicationDate Text affectedBRITISH STANDARDBS EN 10263-3:2017EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 10263-3 November 2017 ICS 77.140.60; 77.140.65 Supersedes EN 10263-3:2001English Version Steel rod, bars and wire for cold heading and cold

12、 extrusion - Part 3: Technical delivery conditions for case hardening steels Barres, fil machine et fil en acier pour transformation froid froid et extrusion froid - Partie 3: Conditions techniques de livraison des aciers de cmentation Walzdraht, Stbe und Draht aus Kaltstauch- und Kaltfliepresssthle

13、n - Teil 3: Technische Lieferbedingungen fr Einsatzsthle This European Standard was approved by CEN on 26 July 2017. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without an

14、y alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other langua

15、ge made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark,

16、 Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMI

17、TTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2017 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 10263-3:2017 EBS EN 10263-

18、3:2017EN 10263-3:2017 (E) 2 Contents Page European foreword . 3 1 Scope 4 2 Normative references 4 3 Terms and definitions . 4 4 Classification and Designation . 4 4.1 Classification . 4 4.2 Designation 4 5 Production process . 5 5.1 Steelmaking process 5 5.2 Deoxidation . 5 6 Requirements . 5 6.1 D

19、elivery conditions 5 6.2 Chemical composition . 5 6.2.1 Cast analysis 5 6.2.2 Product analysis 5 6.3 Mechanical properties . 5 6.4 Hardenability 5 6.5 Surface quality 6 6.6 Supplementary or special requirements 6 Table 1 Combination of heat-treatment condition at delivery, product forms and applicab

20、le requirements 7 Table 2 Surface condition at delivery . 8 Table 3 Steel grades and chemical composition. Heat analysis % (by mass). 8 Table 4 Permissible deviations between product analysis and the limiting values specified in Table 3 for the heat analysis 10 Table 5 Mechanical properties of non-a

21、lloyed steel grades 11 Table 6 Mechanical properties of boron-alloyed steel grades . 12 Table 7 Mechanical properties of alloyed steel grades . 13 Table 8 Hardness limits for steel grades with standard hardenability (+H grades - see 6.4.1) . 15 Table 9 Hardness limits for steel grades with restricte

22、d hardenability scatter bands (+HH and +HL grades - see 6.4.2) . 16 BS EN 10263-3:2017EN 10263-3:2017 (E) 3 European foreword This document (EN 10263-3:2017) has been prepared by Technical Committee ECISS/TC 106 “Wire rod and wires”, the secretariat of which is held by AFNOR. This European Standard

23、shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by May 2018, and conflicting national standards shall be withdrawn at the latest by May 2018. Attention is drawn to the possibility that some of the elements of this document

24、 may be the subject of patent rights. CEN shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 10263-3:2001. This European Standard EN 10263 is subdivided as follows: Part 1: General technical delivery conditions Part 2: Technical delivery conditio

25、ns for steels not intended for heat treatment after cold working Part 3: Technical delivery conditions for case hardening steels Part 4: Technical delivery conditions for steels for quenching and tempering Part 5: Technical delivery conditions for stainless steels According to the CEN-CENELEC Intern

26、al Regulations, the national standards organisations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ire

27、land, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. BS EN 10263-3:2017EN 10263-3:2017 (E) 4 1 Scope 1.1 This part of EN 10263 is applicable to round rod, round bars a

28、nd wire with a diameter up to and including 100 mm, of non-alloy and alloy steel, intended for cold heading and cold extrusion and case hardening. 1.2 EN 10263-1:2017 is indispensable for this part of EN 10263. 2 Normative references The following documents, in whole or in part, are normatively refe

29、renced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 10020, Definition and classification of grades of steel EN 10263-1:201

30、7, Steel rod, bars and wire for cold heading and cold extrusion Part 1: General technical delivery conditions 3 Terms and definitions For the purposes of this document, the terms and definitions given in EN 10263-1:2017 and the following apply. 3.1 case-hardening steels structural steels with a rela

31、tively low carbon content, which are carburized or carbonitrided on their surface and subsequently hardened Note 1 to entry: These steels, after hardening, have a high degree of hardness in the surface zone and good resistance to wear, while the core material is characterized principally by extreme

32、toughness. Note 2 to entry: Further possibilities for heat treatment of case-hardening steels are, for example, nitrocarburizing and nitriding. 4 Classification and Designation 4.1 Classification All steels covered by this part of EN 10263 are special steels according to EN 10020. Steel grades from

33、C10E2C to C20E2C as quoted in Table 3 are non-alloy steels and all others are alloy steels according to EN 10020. 4.2 Designation See EN 10263-1:2017. BS EN 10263-3:2017EN 10263-3:2017 (E) 5 5 Production process 5.1 Steelmaking process See EN 10263-1:2017. 5.2 Deoxidation All steels quoted in Table

34、3 shall be deoxidised. 6 Requirements 6.1 Delivery conditions The delivery conditions in which the products covered by this part of EN 10263 are normally supplied, the product forms and the applicable requirements are given in Tables 1 and 2. 6.2 Chemical composition 6.2.1 Cast analysis The chemical

35、 composition shall be in accordance with the values specified in Table 3 for the cast analysis. 6.2.2 Product analysis In cases where a product analysis is requested, the admissible deviations from the values specified for the cast analysis are indicated in Table 4. 6.3 Mechanical properties The mec

36、hanical properties of the products, to be determined by the tensile test or hardness test, shall be in accordance with Tables 5, 6 and 7 but by consideration of the prescriptions given in Table 1 and of the delivery conditions given in Table 2. 6.4 Hardenability 6.4.1 In the case of products ordered

37、 with standard requirements regarding hardenability, that is, when the steel names or numbers as quoted in Table 3 are supplemented by the symbols “+H”, the hardness values obtained in the end quench test (Jominy test) (see Table 1 of EN 10263-1:2017) shall be in compliance with the values given in

38、Table 8. 6.4.2 In the case of products ordered with restricted requirements regarding the scatter bands of the hardness values obtained by the Jominy test, that is when the steel name or number as quoted in Table 3 is supplemented by the symbol “+HH” or “+HL”, the above hardness values shall be in c

39、ompliance with the values given in Table 9. NOTE 1 The symbol “+HH” denotes that the upper limit of the scatter band coincides with the upper limit for the corresponding steel “+H”. NOTE 2 The symbol “+HL” denotes that the lower limit of the scatter band coincides with the lower limit for the corres

40、ponding steel “+H”. NOTE 3 See EN 10263-1:2017, 7.7.4 and 10.2 6.4.3 The austenizing temperatures for the Jominy test are given in Tables 8 and 9. BS EN 10263-3:2017EN 10263-3:2017 (E) 6 6.5 Surface quality For any particular surface requirement to be agreed at the time of ordering see EN 10263-1:20

41、17, 7.10. 6.6 Supplementary or special requirements Other requirements that can be agreed at the time of enquiry and order are described in Annex A of EN 10263-1:2017. BS EN 10263-3:2017EN10263-3:2017(E)7Table1Combinationofheat-treatmentconditionatdelivery,productformsand applicablerequirementsHeat-

42、treatmentconditionatdeliverySymbolProductsformApplicable requirementsincaseswhere the steelconcernedhasbeenorderedwith referencetothesteelnamesindicated inrodbarwireTables3,5 or 6 or7Tables3,5 or 6 or 7,8 or9Table3,5,6,7,8or9untreatedNoneor+UXXXChemicalcompositionasspecifiedin Tables3and4Mechanical

43、propertiesasspecifiedinTable5or6or7Chemicalcompositionasspecifiedin Tables3and4Mechanical propertiesasspecifiedinTable5or6or7ValuesforhardenabilityaccordingtoTables8 or9Supplementaryor special requirementsas specifiedinAnnexAofEN10263-1:2017aspheroidized+ACXXXTreatedtoferrite-pearlite structure andh

44、ardnessrange+FPXOthersOtherdeliveryconditionsmaybe agreedatthe timeof orderingKeyX=applicable=notapplicableaIfagreedat thetimeoftheenquiryand order.BS EN 10263-3:2017EN10263-3:2017(E)8Table2SurfaceconditionatdeliverySurfaceconditionatdeliverySymbolbarrodwireUnlessotherwise agreedasrollednoneor+ARxxP

45、articularsurfaceconditions suppliedbyagreementcolddrawn+Cxxskinpassed+LCxxpeeled+PExxxTable3Steelgradesand chemicalcomposition.Heatanalysis%(bymass)SteelgradesCSimax. aMnPmax.SCrMoNiBCumaxSteelnameSteelnumberC10E2CC15E2CC17E2CC20E2C1.11221.11321.11471.11520.08to0,120,13to0,170,15to0,190,18to0,220,30

46、0,300,300,300,30to0,600,30to0,600,60to0,900,30to0,600,0250,0250,0250,0250,025max.0,025max.0,025max.0,025max.0,250,250,250,2515B218B21.55011.55030,13to0,160,16to0,200,300,300,60to0,800,60to0,800,0250,0250,025max.0,025max.0,0008 to0,0050,0008 to0,0050,250,2518MnB422MnB41.55211.55220,16to0,200,20to0,24

47、0,300,300,90to1,200,90to1,200,0250,0250,025max.0,025max.0,0008 to0,0050,0008 to0,0050,250,2517Cr317CrS31.70161.70140,14to0,200,14to0,200,300,300,60to0,900,60to0,900,0250,0250,025max.0,020to0,0400,70to1,000,70to1,000,250,25BS EN 10263-3:2017EN10263-3:2017(E)8Table2SurfaceconditionatdeliverySurfacecon

48、ditionatdeliverySymbolbarrodwireUnlessotherwise agreedasrollednoneor+ARxxParticularsurfaceconditions suppliedbyagreementcolddrawn+Cxxskinpassed+LCxxpeeled+PExxxTable3Steelgradesand chemicalcomposition.Heatanalysis%(bymass)SteelgradesCSimax. aMnPmax.SCrMoNiBCumaxSteelnameSteelnumberC10E2CC15E2CC17E2C

49、C20E2C1.11221.11321.11471.11520.08to0,120,13to0,170,15to0,190,18to0,220,300,300,300,300,30to0,600,30to0,600,60to0,900,30to0,600,0250,0250,0250,0250,025max.0,025max.0,025max.0,025max.0,250,250,250,2515B218B21.55011.55030,13to0,160,16to0,200,300,300,60to0,800,60to0,800,0250,0250,025max.0,025max.0,0008 to0,0050,0008 to0,0050,250,2518MnB422MnB41.55211.55220,16to0,200,20to0,240,300,300,90to1,200,90to1,200,0250,0250,025max.0,025max.0,0008 to0,0050,0008 to0,0050,250,2517Cr317CrS31.70161.70140,14to0,200,14to0,200,30